Analysis of Intermetallic Phases Formed on Surface Vapor Oxidized H13 Hot Work Steels in Molten Aluminum

In this paper, the author dipped surface vapor oxidized H13 steel specimens into 700℃ molten aluminum liquid for a certain period of time. Analyze the intermetallic phases formed on the H13 samples surface with optical microscope and X-ray diffraction method. The observation of immersion test sample's cross-section shows that Fe3O4 film will protect die substrate from molten aluminum erosion. The identification of the intermetallic phases reveals that they consist of 2parts, which is named as the composite layer and the compact layer. Further investigations are made in order to know the phase constituents of the 2 layers, they are Al8Fe2Si (outer composite layer), (AlCuMg) and Al5Fe2 (compact layer),respectively. The experimental results show that on the same specimen, a convex surface with bigger radius of curvature is more likely to be molten and the melting loss speed is also faster than a flat and smooth surface. The thickness of compact layer on a smooth surface is much bigger than that of the convex surface. Therefore, the author supposes the compact layer is favorable in stabilizing the die surface material from further melting loss, as their formation on the die surface, the melting loss speed will decrease.     

有限元方法在离心机转鼓强度分析中的应用

在回顾以往转鼓强度分析的基础上 ,指出了目前转鼓有限元应力分析所存在的问题 ,给出了提高计算精度和保证模拟有效性的注意事项 ,并探讨了转鼓强度评定准则     

碳铵化肥发青问题解决小结

探讨了该厂化肥生产中碳铵发青的原因,通过硫化氢含量的测定,分析了系统内外影响因素,提出了解决措施,达到了不停车稳定产品质量的目的。     

海特隆酸不饱和聚酯树脂的性能及应用

叙述了海特隆酸不饱和聚酯树脂的特点和性能，并介绍其在湿氯气和其它氧化性介质中的应用。     

离子膜使用过程中起泡的原因及危害

分析并列举了离子交换膜在使用过程中鼓泡的原因，阳极液质量浓度；pH值；阴极液质量浓度；电流密度；开停车及盐水质量等因素都可以造成膜鼓泡，形成针孔。提出了相应的预防措施。     

Influence of Hydrostatic Pressure and Humidity on Superplastic Ductility of Two β-Spodumene Glass-Ceramics

The extent of superplastic deformation in two lithium aluminosilicate glass-ceramics was found to be limited either by intergranular cavitation or by the initiation and growth of surface cracks. Tensile tests were performed under a superimposed hydrostatic pressure to distinguish between the two failure mechanisms. Two materials, one with a high flow stress and the other with a low flow stress, were studied. Cavitation was substantially suppressed by hydrostatic pressure in both materials. The strain-to-fracture, however, was enhanced only in the material with the lower flow stress. (In at least one instance the tensile ductility became almost infinite.) In the material with the higher flow stress, failure was caused by the initiation and propagation of cracks from the surface. The crack-propagation mode of failure was found to be sensitive to humidity, raising the possibility of stress-corrosion cracking at high temperatures in glass-ceramic materials.     

冲击波和爆轰波的共异性

炸药爆炸是实现一些纳米新材料的重要能量来源之一。文章对炸药爆炸所涉及到的一些最基本的概念、模型及其基本关系及冲击波和爆轰波曲线的特征等做了一般性评述，旨在对纳米金刚石合成技术有所指导。     

Guerbet十四醇的合成与表征

以正庚醇为原料 ,通过Guerbet反应合成Guerbet十四醇 (2 戊基壬醇 ,C14 GA)。用IR、NMR和元素分析测定了C14 GA的结构 ,并研究了反应温度和用料比对其产率的影响。实验结果如下 :(1)在较优化的反应条件下 (正庚醇的总加入量为 1mol,在实验过程中 ,先加入 1/ 3mol庚醇和 1/ 4mol的KOH ,在 16 0℃下反应 2h ,然后再加入剩下的 2 / 3mol庚醇和 4g 5 %Pd -C催化剂 ,在 15 5℃下反应 6h)合成产物 ,其产率可达到 5 4 2 0 % ;(2 )所合成的产物与试图要得到的Guerbet十四醇 (2 戊基壬醇 ,C14 GA)含有相同的基团 (2×—CH3、10×—CH2 —、1×CH、1×—CH2 —O—和 1×—OH) ,而且 ,所合成的产物中 ,w (C) =79 0 6 % ,w (H ) =13 6 2 % ,与从Guerbet十四醇分子式计算的理论值w(C) =78 5 0 % ,w (H) =14 0 1%基本一致。可见所合成的产物正是Guerbet十四醇 (C14 GA)     

角蛋白基药物载体的发展及应用探讨

从毛发中提取角蛋白，开发具有独特功能的角蛋白基药物载体材料，提高药物的活性和生物利用率，既能够增加毛发的利用价值，又能够实现节能减排，符合可持续发展战略要求。对毛发中提取角蛋白进行二硫键重建、自由基聚合、多糖改性和烷基化等改性处理，赋予角蛋白基药物载体优异地功能特性，进一步拓宽其作为角蛋白基药物载体的应用范围。角蛋白基药物载体可被加工成纳米粒子、纤维支架、水凝胶等各种形式用于药物的递送。作为一种高硫含量且具有良好细胞相容性的结构蛋白，角蛋白基药物载体在组织工程、再生医学等领域扮演着重要的角色。     

竹红菌甲素衍生物13－SO_3Na－DDHA电化学及光诱导还原的研究

本工作研究了化合物１３－ＳＯ＿３Ｎａ－ＤＤＨＡ在不同ｐＨ的缓冲溶液中的电化学氧化还原行为．实验证明：化合物中羰基的还原电位与ｐＨ之间存在线性关系，其直线的斜率为６０ｍＶ／ｐＨ．并证明了此过程为一步两电子、两质子还原过程：Ｑ＋２Ｈ￣＋＋２ｅ＝ＱＨ＿２．ＤＭＦ作为非质子溶剂，具有很好的稳定自由基的作用．向缓冲溶液中加入ＤＭＦ后，化合物１３－ＳＯ＿３Ｎａ－ＤＤＨＡ为两步单电子还原过程，相应溶液中的光诱导电子转移吸收光谱证实了以上电化学的结果．