HIGH TEMPERATURE LOW CYCLIC FATIGUE BEHAVIOUR OF DIRECTIONALLY SOLIDIFIED Ni-BASE ALLOY DK3

研究了镍基定向凝固高温合金DK3和普通铸造合金K3在760℃应变控制和应力控制下的高温低周疲劳行为。结果表明:这两种合金的高温低周疲劳行为可以用常规的应力疲劳曲线来表征。DK3合金不存在“过渡疲劳寿命”N_T,K3合金则很低。在各种不同应变或应力水平下,DK3合金的低周疲劳寿命高于K3合金,当应力水平为785至980MPa时,其寿命约差1倍,当应力水平为490至685MPa时,则差2倍多。     

用CAXA电子图板求解冲模压力中心

在模具设计中 ,冲裁模压力中心通常采用解析法或图解法求解。本文提出一种用CAXA绘图软件在设计制图时直接求解的方法 ,快速直接 ,简单方便 ,精度较高。     

Analysis of Intermetallic Phases Formed on Surface Vapor Oxidized H13 Hot Work Steels in Molten Aluminum

In this paper, the author dipped surface vapor oxidized H13 steel specimens into 700℃ molten aluminum liquid for a certain period of time. Analyze the intermetallic phases formed on the H13 samples surface with optical microscope and X-ray diffraction method. The observation of immersion test sample's cross-section shows that Fe3O4 film will protect die substrate from molten aluminum erosion. The identification of the intermetallic phases reveals that they consist of 2parts, which is named as the composite layer and the compact layer. Further investigations are made in order to know the phase constituents of the 2 layers, they are Al8Fe2Si (outer composite layer), (AlCuMg) and Al5Fe2 (compact layer),respectively. The experimental results show that on the same specimen, a convex surface with bigger radius of curvature is more likely to be molten and the melting loss speed is also faster than a flat and smooth surface. The thickness of compact layer on a smooth surface is much bigger than that of the convex surface. Therefore, the author supposes the compact layer is favorable in stabilizing the die surface material from further melting loss, as their formation on the die surface, the melting loss speed will decrease.     

环氧氯丙烷下游产品生产现状及市场前景

论述了环氧氯丙烷的主要下游产品环氧树脂、合成甘油、氯醇橡胶等的生产现状、市场前景等,指出:我国氯碱行业应该重视这些环氧氯丙烷下游精细化工产品的开发,以促进我国环氧氯丙烷的发展。     

Influence of volatile matter and deposited carbon on coke yield from coals

The relations between coke yields and the volatile matter content of 30 individual and 30 blended coals were investigated. Coke yields and deposited carbon related to volatile matter content can be expressed in the following equations: CY (%) = 97.89?0.86 VMch+VMc; and DC (%)= ?2.24+0.16 VMch; where: CY=real coke yield; VMch = volatile matter content of charging coal; VMc=volatile matter content of coke, and in the case of <2%; DC = deposited carbon. The test results show excellent correlation with practice.     

关于煤炭硫分分级的探讨

根据国家质量技术监督局的计划安排,国家标准GB／T15224－1994《煤炭质量分级》需要修订。本文主要讨论“煤炭硫分分级”方面的内容。     

容器焊缝错边残余应力与载荷应力的测定研究

本文对焊接容器错边和不错边的焊接接头进行了电测法的残余应力测试，确定了焊接残余应力的大小及方向，并在加载的条件下，对各焊接接头测点进行了综合应力测试，并给出了受载条件下的应力分布。     

PET熔体输送系统中熔体温度自动控制方案

在热媒温度控制系统中以熔体温度作为主参数,组成串极调节系统。投入运行后,熔体温度稳定,调节阀动作平稳,效果良好。     

如何提高预焙铝电解槽阳极质量

预焙阳极的质量已严重制约铝电解技术的发展，必须予以足够的重视．国外在提高阳极质量方面的有效措施，可以供国内阳极工厂技术改造及科研攻关借鉴．     

氯化聚丙烯改性胶粘剂的合成及粘附性能研究

以甲苯为溶剂，过氧化二苯甲酰(BP0)为引发剂，通过自由基聚合，采用甲基丙烯酸羟乙酯(HEMA)和苯乙烯(St)接枝改性氯化聚丙烯(CPP)。研究了不同苯乙烯用量、不同反应温度、不同反应时间、不同引发剂用量对改性氯化聚丙烯胶粘剂粘附性能的影响，得出较佳的工艺条件为反应温度90℃，反应时问2h，原料配比m(CPP)：m(HEMA)：m(St)：m(BPO)=50：0．5：0．6：0．15。