Synthesis of Ti3SiC2 by spark plasma sintering(SPS)of elemental powders

Ti3SiC2 materials have been fabricated by spark plasma sintering of the elemental powders with the addition of Al.At the heating rate of 80℃/min and under the pressure of 30MPa,the ideal synthesis temperature of Ti3SiC2 is in the range of 1150-1250℃.The addition of Al is in favor of the formation of Ti3SiC2.The synthesized compound has the molecular of Ti3Si0.8Al0.2C2 and lattice parameters of α=0.3069nm,c=1.7670nm.Its grain is plane-shape with a size of about 50μm in the elongated dimension.The prepared material has Vickers hardness of 3.5-5.5GPa(at 1N and 15s) and is as readily machinable as graphite‘s.     

烧结参数对温压Fe-2Ni-2Cu-1Mo-1C材料抗拉强度的影响

采用温压方法制备了高密度Fe-2Ni-2Cu-1Mo-1C材料,并研究了烧结温度和烧结时间对温压Fe-2Ni-2Cu-1Mo-1C材料烧结密度和抗拉强度的影响。结果表明:常规温压和模壁润滑温压的烧结密度和抗拉强度随烧结温度和时间的变化而变化,模壁润滑温压的烧结密度和抗拉强度均大于常规温压的;温压材料的抗拉强度为烧结温度和烧结时间的函数,常规温压和模壁润滑温压的抗拉强度随烧结温度和时间变化的线性回归方程(R为相关系数)分别为σb=575 211 153 6f(t,T),R=0.972和σb=595 208 688 3f(t,T),R=0.997。     

Effects of Thermal Exposure on the Tensile and Fatigue Properties of Cast Ti—47Al—2Cr—2Nb--0.15B Alloy

测量了铸造Ti—47Al—2Cr—2Nb-0．15B(原子分数，％)合金的高温疲劳强度以及650℃／100h和800℃／100h热暴露后的拉伸性能和疲劳强度，采用X射线衍射和扫描电镜等方法分析了经热暴露后合金基体组织的变化和表面层的结构．随暴露温度的提高，合金的室温塑性和疲劳强度降低，650℃附近有一转折点，大于650℃时上述性能加速下降；合金高温疲劳性能具有相似的变化规律．显微分析表明，在热暴露或高温疲劳实验时，表面形成的脆性层是导致合金性能降低的直接原因；而随温度的提高，表面层由渗氧层转变为氧化层是导致合金性能随温度变化出现转折的原因．     

使用Visual C+ +实现串行通讯

以VisualC 为工具，探讨了在RS-232C接口协议下DTE设备之间通讯的实现问题。     

高温烟气过滤筒制作工艺研究

本文对除尘净化设备常用的过滤材料进行了综述对比 ,提出了一种新型的过滤材料 ,该过滤材料可以在高温下直接使用 ,有利于简化除尘净化设备。同时对用这一新型的过滤材料制作过滤筒的工艺进行了初步探讨和研究。     

软包装标牌模具的设计和加工

分析了零件的工艺特点 ,介绍了此类软包装高速冲模的结构 ,以及模具中的计数装置、凸模上吹气卸料和收料装置 ,并对该模具的加工工艺做了详细的介绍     

Tribological behavior of high specific strength PTFE-Al alloy composite

Solid lubricants lead to substantial weight savings relative to the use of liquid lubricant, especially in the weight-conscious aerospace industry. A new PTFE-Al alloy composite（A） containing 60% area proportion of PTFE composite was developed. Another type of common metal-plastics multilayer composite, also called DU, was selected for a comparative investigation. Friction and wear tests were carried out in an oscillating sliding tribotester in air at an oscillating frequency of 0.13 Hz and contact mean pressures from 10 to 80 MPa. The composites slid against a 38CrMoAlA steel shaft. The results show that the composite A exhibits low coefficient of dry sliding friction less than 0.1 and long wear life of 2 000 m. This is because the composite A can provide a sufficient solid lubrication during the whole tests. SEM examination of the transfer films for the composite A confirms that uniform, thin and coherent transfer films are prerequisites for low friction and good wear resistance.     

下喷式环流反应器环隙气含率影响因素

下喷式环流反应器是一种用于强化气-液两相反应过程的新型装置，虽然已在工业上有了较广泛的应用，但对其理论研究远未成熟，其工业装置的设计仍依赖于实验和经验。本文借助实验室自制实验装置，对下喷式环流反应器环隙气含率的影响规律进行了研究。首先，对喷射器的吸气量进行了测量，获得了不同条件下喷射器最大吸气量的性能曲线；在此基础上，分别研究了气相流量、液相流量以及喷射器安装位置对环隙气含率的影响规律。结果表明：气相流量和液相流量对气含率具有重要的影响，随着气相流量和液相流量的增大，气含率快速提高，而喷嘴位置对气含率的影响相对较小；考虑到增加气相流量和液相流量所需要的能耗和设备代价，通过增加液相流量来达到提高气含率的目的是优选方案。     

以葡萄糖为辅助底物发酵生产1,3-丙二醇的研究

采用Klebsiellapneumoniae对葡萄糖作为辅助底物发酵生产 1 ,3 丙二醇进行了研究。结果表明葡萄糖单独作为底物发酵时不生成 1 ,3 丙二醇。以葡萄糖和甘油为混合底物时 ,则可以显著提高菌体浓度 ,但是 1 ,3 丙二醇浓度和甘油到 1 ,3 丙二醇转化率没有提高。在甘油为底物的批式发酵过程中 ,通过流加葡萄糖作为辅助底物可以提高甘油到 1 ,3 丙二醇的摩尔转化率 ,同时可缩短发酵时间。通过选择合适的葡萄糖流加速率 ,较以甘油为单一底物的发酵结果 ,1 ,3 丙二醇的摩尔转化率最高可达0 649,提高了 53 4% ;生产强度为 1 0 0 5g/ (L·h) ,提高了 1 39 9%。     

三聚氰胺改性脲醛树脂粉体胶粘剂的研制

用三聚氰胺改性脲醛树脂改善了胶粘剂的耐沸水性,并有效地降低了游离甲醛含量。三聚氰胺改性脲醛树脂粉体胶粘剂应用更广泛,性能更可靠。