HIGH TEMPERATURE LOW CYCLIC FATIGUE BEHAVIOUR OF DIRECTIONALLY SOLIDIFIED Ni-BASE ALLOY DK3

研究了镍基定向凝固高温合金DK3和普通铸造合金K3在760℃应变控制和应力控制下的高温低周疲劳行为。结果表明:这两种合金的高温低周疲劳行为可以用常规的应力疲劳曲线来表征。DK3合金不存在“过渡疲劳寿命”N_T,K3合金则很低。在各种不同应变或应力水平下,DK3合金的低周疲劳寿命高于K3合金,当应力水平为785至980MPa时,其寿命约差1倍,当应力水平为490至685MPa时,则差2倍多。     

Analysis of Intermetallic Phases Formed on Surface Vapor Oxidized H13 Hot Work Steels in Molten Aluminum

In this paper, the author dipped surface vapor oxidized H13 steel specimens into 700℃ molten aluminum liquid for a certain period of time. Analyze the intermetallic phases formed on the H13 samples surface with optical microscope and X-ray diffraction method. The observation of immersion test sample's cross-section shows that Fe3O4 film will protect die substrate from molten aluminum erosion. The identification of the intermetallic phases reveals that they consist of 2parts, which is named as the composite layer and the compact layer. Further investigations are made in order to know the phase constituents of the 2 layers, they are Al8Fe2Si (outer composite layer), (AlCuMg) and Al5Fe2 (compact layer),respectively. The experimental results show that on the same specimen, a convex surface with bigger radius of curvature is more likely to be molten and the melting loss speed is also faster than a flat and smooth surface. The thickness of compact layer on a smooth surface is much bigger than that of the convex surface. Therefore, the author supposes the compact layer is favorable in stabilizing the die surface material from further melting loss, as their formation on the die surface, the melting loss speed will decrease.     

关于煤炭硫分分级的探讨

根据国家质量技术监督局的计划安排,国家标准GB／T15224－1994《煤炭质量分级》需要修订。本文主要讨论“煤炭硫分分级”方面的内容。     

石蜡聚苯乙烯微球的制备

通过悬浮聚合技术合成了石蜡聚苯乙烯微球，研究了合成过程中引发剂浓度及交联剂用量对微球粒径及其分布的影响。     

相转移催化法合成多聚乙二醇二环氧甘油醚

以多聚乙二醇和环氧氯丙烷为原料合成了多聚乙二醇二环氧甘油醚。NaOH为催化剂,季铵盐为相转移催化剂。结论为:作为催化剂NaOH固体效果优于NaOH溶液;四正丁基硫酸氢铵(TBAS)催化醚化反应效果最佳,GC监测表明,二醚的选择性达98％以上;n(多聚乙二醇):n(环氧氯丙烷):n(NaOH):n(TBAS)= 1:10:7:0．08;反应温度55-60℃;反应时间1．5 h;产率83％。     

钢筋阻锈剂在工业厂房中的应用

介绍了钢筋阻锈剂的基本性能、使用范围和方法。     

稀磷酸澄清槽泥浆泵改用单螺杆泵的实践

磷酸生产中输送稀磷酸澄清槽淤渣的泥浆泵，各厂的运行情况都不够理想。介绍了三种类型泥浆泵的运行情况，针对淤渣中会出现块结垢物影响泥浆泵长期运行，在单螺杆泵进料腔内设置破碎送料器后，取得了较理想的效果，从而提高了磷酸装置的运转率和磷得率。     

2,4,6-三甲氧基脱氧安息香的合成新方法

以1,3,5-三甲氧基苯替代间苯三酚为原料和苯乙腈反应,用甲苯替代不易回收且安全性较差的乙醚为溶剂,通过Hoesch反应制备得到2,4,6-三甲氧基脱氧安息香,产品经HNMR和MS定性.因醚键的保护作用降低了羟基的反应活性,抑制了副反应,使得方法改进后,Hoesch反应的单步收率提高到81.3%.考察了原料配比、反应时间及ZnCl2用量对反应的影响,得到了较佳的反应条件为1,3,5-三甲氧基苯与苯乙腈的摩尔配比为1.2∶1,反应时间为28 h,ZnCl2与苯乙腈的摩尔配比为0.3∶1.