纳米β-Ni(OH)2与球型Ni(OH)2的热性能比较研究

用配位沉淀法合成出纳米级Ni（OH）2，并对其进行XRD，TEM，DSC分析，分析结果表明，所得纳米β-Ni（OH）2为可用作电极材料的β-Ni（OH）2，粒径为30－40nm，且热分解温度比普通球镍低10℃左右，摩尔分解热比普通球镍低4－7kJ，从理论上分析了产生此现象的原因。     

中温换热器检查及修复方案

经分析认为中温换热器缺陷出现的主要原因是H2 S腐蚀。采取更换短管以及补焊上段下管板的措施进行修复 ,取得了满意的效果     

Autolisp在开发V画面体视图自生成系统中的应用

介绍了近年来体视投影技术的应用及发展，并提出了用AutoCAD的内嵌开发工具Autolisp语言结合Visualisp中的对话框控制语言DCL来开发体视图自动生成系统的新思路．根据V画面体视投影原理，推导出了V画面体视变换矩阵．给出了该系统的程序流程框图及相应的功能模块．并将该系统的界面和基本功能进行了展示，从而为体视自生成技术的研究开辟了新的道路．     

分割电极片状压电致动器——(二)位移特性及狭缝宽度对其影响的实验研究

研究了悬臂梁式分割电极片状压电致动器的位移特性。理论分析表明，分割电极狭缝宽度会减小致动器自由端的位移输出，但当狭缝宽度小于致动器电极宽度的１０％时，可忽略狭缝宽度的影响。致动器端部位移的测试结果大于理论计算值。与现有磁头悬浮臂尺寸相近的致动器，在２０Ｖ～５０Ｖ的电压驱动下均可获得１μｍ～２μｍ的致动位移。对９８５０道／厘米的密度磁盘，该位移能覆盖至少一个磁道宽度，满足磁头定位两级伺服系统对第二级致动器位移的基本要求。     

浅谈ispLSI及其应用

本文以ｉｓｐＬＩＳＩ１０００系列为例，对ｉｓｐ技术及ｉｓｐＬＳＩ器件进行了较为详细的介绍，并结合具体设计实例，介绍ｉｓｐＬＳ开发工具的使用。     

Synthesis, characteristics and oxygen-sensitive properties of SrMgxTi 1 − xO3 nanocrystals

SrMg_xTi_{1 - x}O₃ nanocrystals (x = 0.1–0.6) were synthesized by the stearic acid gel method. Powder samples were characterized by X-ray diffraction and X-ray photoelectron (XP) spectroscopy. The results showed that the lattice parameter a and the O 1s XP spectrum changed not only with the Mg content x but also with the grain size d of the samples. The conductivity of a thick film specimen fabricated on an aluminium oxide wafer was investigated in a nitrogen—oxygen atmosphere.     

Clinical and experimental observation of xilixin granule combined with radiotherapy in treating malignant-tumors

Thirty six patients of pulmonary or nasopharyngeal carcinoma were treated with Xilixin granule (XLXG) combined with radiotherapy and compared their efficacy with that of 31 patients treated by Zhenqi Fuzheng granule combined with radiotherapy for control. Results showed that the symptoms of Yin Deficiency syndrome in treated group were obviously improved, the leucocyte decreased by 5.6%, while in control group it reached 25.8%, the 3 year survival rate was significantly higher in treated group (75.0%) than that in control group (51.6%). Animal experiment revealed that XLXG had the effects of tumor inhibition, it could increase white blood cells, platelets and hemoglobin of patients, especially in using large dosage. These results suggested that XLXG have some protective effect against radiotherapeutic damage in patients with malignant tumor.     

Pore size control of porous silica by sol-gel process

Porous silica glass was prepared by sol-gel process from tetraethoxysilane (TEOS). The effects of solvents (water, ethanol), drying condition, heat treatment temperature on specific surface area and pore size distribution of porous silica were investigated. Gelation process accelerates with an increase of H₂O content, while retards with the increase of ethanol amount. Structure changes during heat treatment were studied by means of DTA, XRD. TEM micrographs show that the gel particles shrink after heated at 500°C, thus the average pore size decreases.     

Effect of processing history on the properties of Ag-based tapes

The Bi-system tapes and coils were prepared by the powder-in-tube method. The effect of processing and heat treatment on the properties of the tapes and coils was studied. It is found that the shearing stress produced by the rolling process may destroy the 2223 phase, and the destroyed 2223 phase cannot be recovered by heat treatment, whereas the pressing stress produced by the uniaxial pressing process only makes the 2223 phase grains break, and the broken 2223 phase can be closed by the heat treatment. TheJ _c values of the rolling samples, pressing sample, and the coil with a diameter of 35 mm are over 1.3×10⁴, 2.5×10⁴, and 4×10³ A/cm² (77 K, 0 T), respectively.     

溶胶－凝胶法制备Pb（Zr，Ti）O_3玻璃陶瓷过程中的结构变化

本文介绍溶胶－凝胶法制备均匀ＰｂＺｒ－Ｔｉ－Ｂ－Ｓｉ凝胶玻璃，并通过适当热处理在凝胶玻璃中原位生长Ｐｂ（Ｚｒ；Ｔｉ）Ｏ３微晶的新工艺·利用ＩＲ谱考察了凝胶玻璃中的元素键合结构随温度的变化．结合热分析和ＸＲＤ；ＳＥＭ技术，研究了Ｐｂ（Ｚｒ，Ｔｉ）Ｏ３微晶在凝胶玻璃中的生长过程及该材料的结构特点．发现Ｐｂ２（Ｚｒ，Ｔｉ）２Ｏ６＋ｘ立方焦绿石介稳过渡相的纳米微晶首先出现于该体系中，并在更高的温度下先后完全转变成三方和四方Ｐｂ（Ｚｒ，Ｔｉ）Ｏ３钙钛矿相．电子显微观察结果表明，该工艺制备的Ｐｈ（Ｚｒ；Ｔｉ）Ｏ３玻璃陶瓷具有均匀的细晶结构．