钛合金双层辉光放电离子无氢渗碳制备工艺研究

采用双层辉光离子无氢渗碳的方法对钛合金进行表面强化处理,提高了钛合金的表面强度,改善了其耐磨性;同时避免了氢脆的产生.研究表明钛合金Ti6Al4V双辉离子无氢渗碳合理的工艺参数为:温度880℃～980℃;气压28～40Pa;工件与源极之间距离6～14mm;源极电压600V～800V:阴极电压260V～400V;保温时间2～5 h.处理后在钛合金表面形成了高硬改性层,耐磨擦性显著提高.     

Synthesis and characterization of LiNi0.95-xCoxAl0.05O2 for lithium-ion batteries

Samples of LiNi0.95-xCoxAl0.05O2 （x = 0.10 and 0.15） and LiNiO2, synthesized by the solid-state reaction at 725℃ for 24 h from LiOH-H2O, Ni2O3, Co2O3, and AI（OH）3 under an oxygen stream, were characterized by TG-DTA, XRD, SEM, and electrochemical tests. Simultaneous doping of cobalt and aluminum at the Ni-site in LiNiO2 was tried to improve the cathode performance for lithium-ion batteries. The results showed that co-doping （especially, 5 at.% A1 and 10 at.% Co） definitely had a large beneficial effect in increasing the capacity （186.2 mA.h/g of the first discharge capacity for LiNio.s.42OoaoAlo.0502） and cycling behavior （180.1 mA-h/g after 10 cycles for LiNio.85CooaoAlo.osO2） compared with 180.7 mA.h/g of the first discharge capacity and 157.7 mA.h/g of the tenth discharge capacity for LiNiO2, respectively. Differen- tial capacity versus voltage curves showed that the co-doped LiNio.95_xCoxmlo.osO2 had less intensity of the phase transitions than the pristine LiNiO2.     

PLC在DU型多功能组合机床电控系统改造中的应用

从机床自动控制的实际需要出发，以DU型多功能组合机床为例，介绍了一种利用PLC的顺序编程控制功能来改造机床电控系统的具体方法。     

影响Ti合金热稳定性的因素

综述了合金元素、环境气氛、相变、涂层等因素对Ti合金热稳定性的影响.     

乙醇冷媒液中复配缓蚀剂的研究

通过失重法测定了A3钢、铜、铝在20%乙醇冷媒液中的腐蚀速率和复配缓蚀剂的缓蚀效果，筛选出不含 NO-2的复配缓蚀剂.该缓蚀剂可以有效减缓碳钢、不锈钢、紫铜和铝合金材料在乙醇冷媒液中的腐蚀，同时提高冷媒液的稳定性，改善其冰点和沸点.     

Al—Li—Cu—Mg合金应力腐蚀性能及机理研究

利用恒应变速率方法研究了Al—Li—Cu—Mg合金的应力腐蚀开裂,包括时效条件及外加电位对应力腐蚀的影响,同时研究了试样表面相对氢浓度与外加电位及应力腐蚀时间的关系,实验结果表明,合金的应力腐蚀性能取决于时效条件,其中峰时效条件下最差,自然时效条件下最好,应力腐蚀敏感性及试样表面氢浓度与外加电位有关,阳极电位增加应力腐蚀敏感性,阴极电位低于临界电位时加速应力腐蚀,认为合金在应力腐蚀过程中阳极溶解与氢脆机制联合作用。     

单源低能离子束辅助沉积类金刚石薄膜结构及性能研究

用单源低能氩离子束辅助沉积（ＩＢＡＤ）法制备了非晶碳薄膜．氩离子能量为４００－１５００ｅＶ．膜面光滑致密，与衬底的结合力较高。用Ｒａｍａｎ，ＦＴＩＲ，ＨＲＴＥＭ，ＴＥＤ，ＳＥＭ，ＥＲＤ及ＲＢＳ研究了薄膜的形貌、结构和组分，测量了膜的电阻率、显微硬度及摩擦系数．薄膜为无定形的类金刚石（ＤＬＣ）．其中含氢约为２０５ａｔ．－％，碳原子与氢原子几乎没有形成Ｃ－Ｈ键．随着离子束能量及束流的增加，显微硬度、摩擦系数增加，电阻率减小．硬度增加是由于薄膜致密度的增加，而电阻率降低是由于膜中金刚石键（ｓｐ~３键）含量减少的缘故．     

Preparation and properties of （K0.5Na0.5）NbO3-LiNbO3 ceramics

The lead-free piezoelectric ceramics （1-x）（K0.5Na0.5）NbO3-xLiNbO3（abbreviated as KNLN） were synthesized by a traditional solid state reaction. The effects of Li^＋ on the sintering characteristic, the phase structure and piezoelectric properties of KNLN ceramics were investigated. The sintering temperature of KNN-based ceramics is decreased by doping Li^＋ and the range of the sintering temperature is narrow. The KNLN ceramics exhibit an enhanced piezoelectric properties with the piezoelectric constant d33 value of 180-200 pC/N, The electromechanical coupling coefficients kp is 35%-40%. The results show that （1-x）（K0.5Na0.5）-NbO3-xLiNbO3 （x=0.05, 0.06） is a promising high-temperature lead free piezoelectric ceramic.     

环形件惯性摩擦焊接过程塑性区演化的数值模拟研究

基于弹塑性有限元理论,采用特殊的摩擦模型描述工件的摩擦行为,建立了GH4169环形件惯性摩擦焊接过程的热力耦合模型。计算并分析了惯性摩擦焊接过程中接头塑性区的分布、扩展规律及其与工件轴向缩短的关系,并计算了塑性区金属塑性变形速率的分布和变化情况。对摩擦焊接过程中塑性区的分布规律做了定性的实验验证,塑性区分布的计算结果和实验结果吻合较好。     

声发射方法测定SiCw／Al复合材料的界面强度

对ＳｉＣｗ／Ａｌ复合材料形变断裂过程中的声发射（ＡＥ）特征的研究表明，用ＡＥ技术能准确测定ＳｉＣ纤维的断裂次数，并能测定其断枝长度，从而测定了纤维和基体间的界面强度和ＳｉＣ纤维的断裂强度。