La8/9Sr1/45Na4/45MnO3/0.5x（V2O5）复合体系的电输运及磁电阻

用固相反应法制备了 La8/9Sr1/45Na4/45MnO3/0.5x（V2O5）（x = 0,0.04,0.08,0.12,0.16,0.20）系列样品,通过 X 射线衍射谱、扫描电子显微镜、电阻率–温度（ρ–T）和磁电阻–温度（RM–T）的关系,研究了样品的电输运性质及 RM温度稳定性。结果表明：所有样品表现为从高温区绝缘体导电到低温区金属导电的绝缘体–金属相变,随 V2O5复合量增大,绝缘体–金属转变温度 Tp向高温移动;V2O5复合量较小（x≤0.08）时 ρ–T 曲线出现双峰,V2O5复合量较大（x≥0.12）时 ρ–T 曲线双峰消失;所有样品在低温区随温度降低 RM持续增大,表现出低场磁电阻特征,在高温区的本征磁电阻随 V2O5复合量增大而逐渐减小;对于 x = 0.16、0.20 的样品,在 0.8 T 磁场,319～283 K,RM基本保持 6.4%和 5.8%不变。RM温度稳定性的产生原因可能是表面相引起的隧穿磁电阻与体相引起的本征磁电阻竞争的结果。在高温区体相内部双交换引起的本征磁电阻占优势,在低温区界面的磁无序引起的隧穿磁电阻占优势,最终在中间温区产生不随温度变化的 RM。     

Influence of Zinc Doping upon Magnetic Structure of LaMnO3 System

LaMnO3isaninsulatorwithperovskitestructure ofABO3atwholetemperaturerange.Inthissystem, Mnionistrivalent,andthereexistssuper exchange antiferromagneticcouplinginMn3 O Mn3 .When divalentionisdopedatAsite,thesamplebecomes La1-xAxMnO3(A=Ca,Sr,Ba).Accordingto…     

CaMn1-xWxO3(0.05≤x≤0.20)体系电荷有序的建立与消失

通过对样品磁化强度-温度（M-T）曲线、磁化强度-磁场强度（M-H）曲线、电阻率-温度（ρ-T）曲线及部分样品ESR谱的测量，研究了Mn位w掺杂对Cabin1-x，WxO3（x=0．05，0．07，0．10，0．12，0．14，0．16，0．20）体系磁结构的影响。结果表明，随着W掺杂量的增加，体系磁结构发生了复杂的变化过程。当掺杂量x≤0．07时，体系为铁磁（FM），反铁磁（AFM）和顺磁（PM）态的共存，随掺杂量增加，FM态减弱，AFM态增强；当x=0．10，0．12时，体系建立电荷有序（charge ordering，CO）态，AFM／CO态共存于相变温度以下，且电荷有序温度TCO随掺杂量增加而增加；当x≥0．14时，体系电荷有序（CO）态减弱并消失。     

钙钛矿锰氧化物La0.3Ca0.7Mn0.96W0.04O3在电荷有序相中的磁性质

采用固相法制备了样品La0.3Ca0.7Mn0.96W0.04O3. 通过测量样品的M-T曲线、 M-H曲线和ESR曲线, 研究了La0.3Ca0.7Mn0.96W0.04O3的磁性质. 结果表明： 在265 K时形成电荷有序相（CO相）. 当T＞265 K时, 表现为顺磁;当T＜225 K时, 表现为长程反铁磁（在AFM本底中存在少量FM成分）, 形成少量FM相与AFM/CO相共存;从265～225 K, 随温度降低在电荷有序态下从顺磁向反铁磁转变. 测量了La0.3Ca0.7Mn0.96W0.04O3样品的ESR谱线宽, 样品的顺磁共振线宽ΔHPP的值随着温度的降低是增加的, 表明随着温度的降低样品的铁磁关联增强.     

Gd掺杂对La_(0.67)Sr_(0.33)CoO_3、La_(0.67)Sr_(0.33)MnO_3体系磁行为的影响(英文)

研究了La0.67-xGdxSr0.33CoO3、La0.67-xGdxSr0.33MnO3 (x=0.00, 0.05, 0.10, 0.20, 0.30, 0.40, 0.50, 0.60, 0.67)体系的M-T曲线、M-H曲线。结果表明:随Gd掺杂浓度增高,La0.67-xGdxSr0.33CoO3体系的磁结构表现为团簇玻璃态,x0.10样品的M-T曲线出现了低温区M值急剧上升的奇特现象;La0.67-xGdxSr0.33MnO3体系的磁结构从长程铁磁有序向团簇玻璃态、反铁磁状态转变,x≥0.50样品的M-T曲线在低温区急剧下降。两种体系呈现的不同现象,来源于Gd与Co、Mn不同的耦合作用和Co的自旋态的转变。     

Transport Property of La0.67-xSmxSr0.33MnO3 at Heavy Samarium Doping （0.40≤x≤0.60）

The influence of heavy samarion （Sm） doping （0.40≤x≤0.60） on magnetic and electric properties of La0.67-xSmxSr0.33MnO3 was investigated by measuring the magnetization-temperature （M - T） curves, magnetization-magnetic density （ M - H） curves, resistivity-temperature （ρ- T） curves and magnetoresistivity-temperature （ MR - T） curves of the samples under different temperatures. It is found that, form from long-range ferromagnetic order to spin-cluster glass with the increase of Sm doping amount, the samples transstate and anti-ferromagnetic state; and when x = 0.60, the transport property becomes abnormal under magnetic background; and the magnetic structure changes and extra magnetic coupling induced by doping leads to colossal magnetoresistance effect. The transport mechanism of metallic conduction at low temperature is mainly electron-magneton interaction and can be fitted by the formula ρ = ρ0 ＋ AT^4.5, and the insulatorlike transport mechanism on high temperature range is mainly the function of variable-range hopping and can be fitted by the formula ρ = ρ0exp（T0/T）^1/4. In the formulas above, p is resistivity, T is temperature, and A, ρ0, T0 are constants.     

缺氧La1-xNaxMnO2．825体系磁电性质

利用提高固相反应法烧结温度的方法制备了La1-xNaxMnO2.825(x=0.05,0.10,0.15,0.20)缺氧体系,测量了样品的XRD谱、红外光谱、拉曼光谱、M-T曲线、ESR谱线、ρ-T曲线.实验结果表明:与La1-xNaxMnO3体系相比,缺氧体系的磁化强度变小,居里温度Tc下降,出现了多相共存现象,原因是缺氧造成的Mn3 /Mn4 的比例变化,以及样品中氧含量的不均匀性;缺氧体系的电阻率升高,大部分样品表现为绝缘态,原因是氧空位引起的晶格作用、自旋作用与Mn3 /Mn4 的双交换作用的共同竞争.     

锶位掺钠对La0.67Sr0.33MnO3体系晶格结构和磁电特性的影响

通过红外光谱和Raman光谱分析了锶(Sr)位掺钠(Na)对La0.67Sr0.3333MnO3体系晶格结构的影响.结果表明:由于Na 的半径小于Sr2 的,Na对Sr位替代后使A位平均离子半径减小,导致Mn-O-Mn键长、键角变化,出现了Jahn-Teller效应.另外,通过实验和计算得到了体系的磁化强度-温度(magnetization-temperature,M-T)曲线,电阻率-温度(resistivity-temperature,p-T)曲线和磁电阻-温度(magnetoresistance-temperature,MR-T)曲线,研究了晶格畸变和双交换作用,发现通过调节Sr位掺Na的摩尔分数获得了室温区的庞磁电阻效应.     

深井石油射孔弹的研制

前言随着我国石油工业的发展,深井和超深井的钻探越来越多.目前,深井已钻到7150米以上,井温超过200℃,井压超过1500大气压.深井和超深井多采用双层甚至三层套管水泥层固井,常常需要使用高比重的压井泥浆.因此,对于深井和超深井的射孔,必     

V掺杂对La_(0.45)Ca_(0.55)MnO_3电荷有序态及输运性质影响的研究

采用标准固相反应法制备了La0.45Ca0.55Mn1-xVxO3(x=0.00,0.06,0.10,0.12)多晶样品。通过XRD、ρ-T曲线、M-T曲线和ρ-T拟合曲线,研究了Mn位V5+离子掺杂对体系的电荷有序相及输运性质的影响。实验结果表明:随着V5+离子的掺杂量的增加,电荷有序相(CO)逐渐削弱,当x=0.10时,CO相基本融化但还有部分残留,当x=0.12时CO相完全融化;对低掺杂(x=0.00,0.06)样品,表现出复杂磁相:随温度降低,发生顺磁-电荷有序-反铁磁相变,40 K附近,在反铁磁背景下产生再入型自旋玻璃态;随掺杂量增加,体系的电阻率逐渐减小,当掺杂量x≥0.10时,样品发生金属-绝缘体相变,其相变温度随着掺杂量的增加而向高温移动。对于金属型导电机制满足自旋波散射和电-磁子之间的散射,而绝缘体导电机制有两种情况:x≤0.10的样品满足变程跃迁模型ρ=ρ0exp(T0/T)1/4,x=0.12的样品则满足小极化子绝热最近邻跃迁模型ρ=ATexp(Eα/κBT),通过掺杂实现了从变程跃迁到绝热小极化子最近邻跃迁。