本文利用钙盐法生产柠檬酸时排出的工业废渣--柠檬酸石膏废渣作原料,通过水热合成法生产石膏晶须.具体的制备过程为:向含80%柠檬酸石膏的乳浊液中加入50%的H2SO4,柠檬酸石膏与50%的H2SO4质量比为500:1,再加入表面活性剂溴代十六烷基吡啶,其中表面活性与石膏质量比为3:100,最后在120℃水热反应20min,生成半水石膏晶须,经220℃干燥得到产品.实验结果表明:未加入表面活性剂进行水热反应,得到石膏晶须平均长径比约为10,晶须长度为50～100μm;加入溴代十六烷基吡啶进行水热反应,得到平均长径比约为80、长为200～400μm的经济附加值高,应用广泛的无水石膏晶须.     

PDP红色荧光粉的制备动态

阐述了现有PDP红色荧光粉存在的问题,并重点从改进生产工艺和制备纳米级红色荧光粉对近几年改善PDP红色荧光粉质量的相关研究工作进行了阐述.     

乙二醇二乙醚二胺四乙酸铁（Ⅲ）催化分解过氧化氢反应机理研究

提出了「Ｆｅ＾Ⅲ（ＥＧＴＡ）」＾－催化分解Ｈ２Ｏ２的反应为链式自由基反应,反应中间体包括「Ｆｅ＾Ⅲ（ＥＧＴＡ）（ＨＯ）＾」Ｆｅ＾Ⅱ（ＥＧＴＡ）＾「和ＨＯ２．ＨＯ．自由基。     

La_(0.8)M_(0.2)CrO_3(M=Ca,Mg,Sr)对硫—氧燃料电池催化性能的影响

通过共沉淀法制备得到La_(0.8)M_(0.2)CrO_3(M=Ca,Mg,Sr)作为阳极催化剂,分别以钇稳定氧化锆(YSZ)粉体和La_(0.6)Sr_(0.4)Co_(0.2)Fe_(0.8)O_(3-δ)(LSCF)粉体作为硫—氧燃料电池的电解质材料和阴极材料。发现在700～800℃时,La_(0.8)Ca_(0.2)CrO_3对硫—氧燃料电池具有明显的催化效果,测得800℃时单电池开路电压为560 mV。La_(0.8)M_(0.2)CrO_3(M=Ca,Mg,Sr)作为硫—氧燃料电池的阳极催化剂,催化效果为:La_(0.8)Ca_(0.2)CrO_3La_(0.8)Mg_(0.2)CrO_3La_(0.8)Sr_(0.2)CrO_3。     

二氧化硫-空气质子交换膜燃料电池的组装与性能

组装二氧化硫-空气质子交换膜燃料电池,探讨水流速度、SO_2气体流速和流向等因素对二氧化硫-空气质子交换膜燃料电池电流和稳定开路电压的影响。实验结果表明,SO_2气流方向从下而上,水流方向从上而下为最佳;在单电池的电极面积为5 cm~2时,水流速度和气流分别为1.0,40 mL·min~(-1),电池的稳定开路电压和电流分别为220 mV和16.25 mA,达到最大值。     

ZnO纳米粒子在煤气脱硫中的应用

以碱式碳酸盐为前驱体，在400℃下焙烧成了粒径30纳米的ZnO纳米粒子，添加到以硫酸渣为主的煤气脱硫剂中，可提高脱硫剂的反应活性和延长使用寿命。     

Preparation and Performance of Sm1-xCaxCrO3-δ as New Interconnect Materials for IT-SOFC

为了探索适用于中温固体氧化物燃料电池的连接材料,采用柠檬酸法制备了Sm1-xCaxCrO3-δ(x=0,0.1,0.2,0.3,0.4)粉体,研究了Ca2+掺杂对材料烧结性能、电性能和热膨胀性能等的影响。实验结果表明,Sm0.7Ca0.3CrO3-δ材料在空气中700℃时电导率为29.8 S·cm-1,氢气气氛中600°C时为1.68 S·cm-1。在30~1000℃温度范围内随着Ca2+掺杂量从0.1增加到0.4,平均热膨胀系数(TECs)值从7.34×10–6增大到8.05×10-6 K-1,与其它常用固体氧化物燃料电池材料热匹配性良好。     

NdFeO3 as anode material for S/O2 solid oxide fuel cells

Sulfur-oxygen solid oxide fuel cells (S/O2-SOFCs) can improve the utilization ratio of energy via converting the combustion heat of sulfur into electrical energy directly, and sulfur trioxide which is an intermediate in sulfuric acid industry can be obtained directly via S/O2-SOFCs. The anode material NdFeO3 was prepared via sol-gel method, the phase stability of NdFeO3 in sulfur vapor or sulfur dioxide atmosphere was investigated. The single cell, consisting of NdFeO3-SDC/SDC/LSM-SDC structure, was fabricated by the screen-printing method and tested by the home-built equipment with sulfur vapor or sulfur dioxide as the fuel. As indicated by X-ray diffraction (XRD) analysis, NdFeO3 was stable in sulfur vapor or sulfur dioxide atmosphere at 800℃, the phase composition of the mixture of NdFeO3 and SDC (Sm doped CeO2) did not change after the mixture was calcined at 800℃ for 4 h. The transmission electron microscope (TEM) photograph revealed that the average grain size of NdFeO3 powder was about 80 nm. With sulfur vapor or SO2 as the fuel, the maximum open circuit voltages (OCVs) of the single cell were 409 mV at 620℃ and 474 mV at 650℃, respectively; the maximum power densities of single cell were 0.154 mW/cm2 at 620℃ and 0.265 mW/cm2 at 650℃, respectively.     

水热合成法工艺条件对柠檬酸石膏晶须形貌的影响

利用工业废渣柠檬酸石膏作原料,通过水热合成法生产石膏晶须。结果表明:向含80%柠檬酸石膏的乳浊液中加入溴代十六烷基吡啶表面活性剂,其加入量与石膏质量比为3∶100;在酸性条件下于120℃水热反应20m in,生成物经220℃干燥可得到长径比约为80、长为200～400μm的无水石膏晶须。     

酒石酸铁（Ⅲ）催化H_2O_2分解反应动力学研究

本文确定了酒石酸铁（Ⅲ）催化分解Ｈ_２Ｏ_２反应在ｐＨ＝２．００－４．６０范围内及温度为２９１Ｋ时的速率方程，结果表明：反应速率与ｐＨ呈＂∧＂型相关性。酒石酸氢铁（Ⅲ）是该反应主要活性催化物，并具有过氧化氢酶模式。