A series of La0.7-xSmxSr0.3MnO3, La0.7-xGdxSr0.3MnO3, and La0.7-xDyxSr0.3MnO3 （x=0.00, 0.10, 0.20, 0.30） samples were prepared by the solid-state reaction method. The influence of the substitution of Sm, Gd, and Dy for La on the magnetic and electric properties and on the magnetoresistance （MR） was studied through measurements of M-T curves and p-T curves. The results showed that： lattice distortion induced by substitution of Sm, Gd, and Dy for La and extra magnetism of substitution had great influence on the magnetic and electric properties of pcrovskite manganites; substitution of magnetic rare earth element for La was an effective way to change Curie temperature and to strengthen MR in perovskite manganites; and appropriate substitution proportion would generate large MR near room temperature.     

La_(0.4)Ca_(0.6)Mn_(1-x)Ga_xO_3体系的电荷有序相

用固相反应法制备La0.4Ca0.6Mn1-xGaxO3(x=0,0.08,0.10,0.12,0.15)系列多晶样品。通过X射线衍射(XRD)图谱、电阻率-温度(ρ-T)曲线、磁化强度-温度(M-T)曲线和电子自旋共振(ESR)图谱,研究Ga3+替代Mn3+对La0.4Ca0.6Mn1-xGaxO3体系电荷有序相的影响。结果表明,当Ga掺杂量高达15%时电荷有序相仍然没有被破坏。这是因为Ga3+是非磁性离子,而La0.4Ca0.6MnO3是CE型反铁磁电荷有序相结构,Ga3+替代Mn3+只是仅仅起到把体系中的长程自旋序破坏为短程自旋序的作用,同时随Ga替代量增大,Mn3+与Mn4+的比远离双交换的最佳摩尔配比(Mn3+∶Mn4+=2∶1),不利于双交换,因而非磁性的Ga3+替代Mn3+难以破坏La0.4Ca0.6MnO3的电荷有序相。     

基于MEMS技术的倾角传感器的研制

倾角传感器可广泛应用于工业自动化、工程机械、医疗设备等领域,基于MEMS技术和单片机技术研制的倾角传感器,具有7段LCD显示和标准RS-485通讯接口,体积小、功耗低,既可作为检测仪表使用,也可作为测控单元连接到现场总线实现联网检测,该传感器已投入实际应用,效果良好。     

Dy替代Y对Y_(1-x)Dy_xCrO_3体系磁性质的影响

用固相反应法制备了Y1-xDyxCrO3(x=0,0.1)多晶样品。通过X射线衍射(XRD)图谱检测了样品的结构,测量了样品的磁性,作了磁化强度-温度(M-T)曲线、磁化强度-磁场(M-H)曲线,研究了Dy3+替代Y3+对Y1-xDyxCrO3体系磁性质的影响。结果表明,Dy3+替代多铁性YCrO3中的Y3+对YCrO3的磁性有效大影响。YCrO3在奈尔温度TN=139 K以下呈倾角反铁磁,显示弱铁磁性;Dy3+替代Y3+后的Y0.9Dy0.1CrO3样品,在50 KT142 K温区,少量Dy3+在两相邻Cr3+产生的倾角反铁磁内场作用下沿内场反方向排列,使铁磁性减弱;在T50 K温区,Dy3+-O2--Dy3+层的铁磁性与Cr3+-O2--Cr3+层的铁磁性耦合,铁磁性增强。     

110kV变电站备自投装置的探讨

分析了各型号主变、线路及备自投装置的特点和实现方法,对各保护装置之间的二次回路配合进行了总结,为以后相关类型工作提供一定的参考。     

输电线路机巡与人巡效果对比及协同巡检建议

从可见光巡检方式、红外检测方式、重大及紧急缺陷、线路典型缺陷等角度对南方电网2012—2014年输电线路直升机巡检(机巡)及地面人工巡检(人巡)数据进行了对比分析,总结了机巡及人巡在输电线路巡检工作中的效果,以及输电线路机巡及人巡的特点,对实施输电线路协同巡检提出了建议。     

架空输电线路直升机、无人机及地面人工巡视互补机制探讨与研究

为了提高架空输电线路运行精益化管理水平,降低运行成本,规范输电线路巡视模式,分别从线路电压等级、巡视任务、巡视部位、巡视地形、巡视配合周期等多个方面探讨和研究了直升机、无人机及地面人工巡视互补机制,建立了新型而高效的输电线路运行模式.     

Pr_(0.4)Ca_(0.6)Mn_(1-x)Cr_xO_3的磁性质及电荷有序相

用固相反应法制备了Pr0.4Ca0.6Mn1-xCrxO3(x=0,0.04,0.06,0.08,0.10,0.12),通过X射线衍射(XRD)图谱,磁化强度-温度(M-T)曲线、电子自旋共振(ESR)图谱,并用ESR作出归—化强度-温度(I/I300—T)曲线、谱线宽度-温度(△Bpp-T)曲线,研究Cr3+替代Mn3+对Pr0.4Ca0.6MnO3的磁性质及电荷有序相的影响。结果表明,母体样品Pr0.4Ca0.6MnO3的电荷有序转变温度Tco=267 K,205K~62 K温区是长程反铁磁序,50 K以下在反铁磁背景下出现少量铁磁成分;Cr替代量x=0.06时,电荷有序相已基本被破坏,随温度降低材料从顺磁向反铁磁转变,同时在反铁磁背底下存在铁成分;Cr替代量达到x=0.10时,电荷有序相完全被破坏,250 K以下是反铁磁与铁磁混合相,铁磁成分增多。用有磁性的且与Mn4+有相同电子结构(t32ge0g)的Cr3+替代Mn3+破坏电荷有序相的机制是:Cr3+替代Mn3+引起自旋序的改变从而引起电荷序的破坏,说明在CE型反铁磁体系中,自旋序与电荷序之间存在强耦合相互作用。     

浅谈煤矿机电设备检修

煤矿企业由于其井下作业的受限性与复杂性,使得井下作业安全隐患增大。井下作业中,机电设备的合作频率高,做好煤矿机电设备的管理、检修与维护,确保机电设备运转正常,可以有效降低事故隐患,达到零事故目标。文章笔者结合自己在煤矿企业的工作管理经验,简单陈述了加强煤矿机电设备基础管理工作的方法,叙述了煤矿机电设备检修工作的内容,对煤矿机电设备的技术改造与质量标准化管理进行分析。作为煤矿企业,应重视机电设备的基础管理工作,针对井下作业的复杂性问题,采取有效措施,从而保证机电设备的安全运行。     

大倾角绝缘子保护锌环的腐蚀特征研究

直流输电线路绝缘子通过安装锌环以减少金具的腐蚀,保障线路的运行安全。为了研究锌环寿命的影响因素,本文搭建了绝缘子直流腐蚀实验平台,研究了绝缘子处于不同悬挂角度时,其保护锌环的腐蚀特征及影响因素。发现锌环的腐蚀面积随着绝缘子悬挂倾角的增大而减少,腐蚀深度随着倾角的增加而增大,而腐蚀生成物将加速锌环的腐蚀;绝缘子悬挂倾角增大后,锌环与绝缘子表面存水区域减少,腐蚀电流更加集中是造成该现象的主要原因。同时水流方向和锌环腐蚀生成物堆积更集中,改变了绝缘子表面电场分布,使该区域的电流密度增大,加剧该区域锌环的腐蚀,甚至造成锌环与绝缘子铁帽之间的放电。研究认为,当绝缘子处于大倾角悬挂时,可以增加最低点锌环厚度以提高其使用寿命。该研究成果可为直流输电线路绝缘子金具腐蚀防治提供参考。