Effect of Extrusion Ratio on the Microstructure and Mechanical Properties in an Al-Cu-Mg-Ag Alloy

In order to examine the effect of extrusion ratio on the microstructure and mechanical behavior in Al-Cu-Mg-Ag alloy, the Al-6.3 Cu-0.48 Mg-0.4 Ag alloy was subjected to extruding with different extrusion ratios of 17, 30 and 67. The results indicate that the grains are refined and the strength is improved effectively with increasing extrusion ratio. However, further investigation shows that the extrusion ratio of 30 is more effective than the lower extrusion ratio(17) and the higher extrusion ratio(67) to refine the grains in the T6-temper alloy. Moreover, the sample with an extrusion ratio of 30 obtains more precipitates and superior mechanical properties after T6 treatment. This study supports the idea that there exists a critical extrusion ratio for grain refinement and improvement of mechanical properties for the T6-temper alloy. Recrystallization and precipitation during T6 treatment were introduced to explain the effects of extrusion ratio on the microstructure and mechanical properties of the Al-Cu-Mg-Ag alloys.     

外场在材料制备和加工过程中的应用

总结了近几年来电流、磁场、振动、微重力场和超重力场等外场在金属凝固过程的应用,及其对固态相变过程的影响;从理论上分析和论述了外场影响凝固过程和固态相变的作用机理,并展望了外场技术的发展前景.     

耐磨锰钢中共晶体的球化

对Ｃａ变质处理的奥氏体－贝氏体耐磨锰钢进行了热力学二维点阵错配度计算，采用ＴＥＭ和ＳＥＭ观察及电子探针分析，发现ＣａＳ可以作为共晶体（奥氏体－渗碳体）的异质核心而使共晶体球化．     

悬浮处理对铸造热锻模具钢组织与性能的影响

研究了悬浮处理对铸造热锻模具钢（ＪＣＤ钢）的显微组织和力学性能的影响。结果表明,悬浮处理后的铸造热锻模具钢,结晶组织得到细化,偏析倾向减小,铸件硬度从ＨＲＣ３９５提高到４４１５,冲击韧性从２０２６Ｊ／ｃｍ２提高到５４８２Ｊ／ｃｍ２,抗热疲劳性提高了约一倍,断面力学性能的均匀性和耐磨性均有较大幅度的提高,可满足热锻模具使用性能的要求。     

超声波对原位Mg2Si/Al复合材料中初生Mg2Si形态的影响

采用光学显微镜和场发射扫描电镜,研究超声波对原位 Mg2Si/Al 复合材料中初生 Mg2Si 形态的影响。研究结果表明：超声波处理使初生Mg2Si的晶粒尺寸从150μm降低到20μm,初生Mg2Si形态发生改变。在二维形貌中,未实施超声波振动处理的初生Mg2Si晶粒生长为含有空腔的粗大颗粒,共晶组织生长于其中,相应的三维形态为含有漏斗状空腔的八面体和十四面体。超声波处理后的初生Mg2Si晶粒变成细小、实心三维形态的颗粒,颗粒棱角已发生钝化效应。     

Austenite－bainite Medium Mn Steel with Nodular Carbide Modified by La Compound

Ａｕｓｔｅｎｉｔｅ－ｂａｉｎｉｔｅＭｅｄｉｕｍＭｎＳｔｅｅｌｗｉｔｈＮｏｄｕｌａｒＣａｒｂｉｄｅＭｏｄｉｆｉｅｄｂｙＬａＣｏｍｐｏｕｎｄＸｕＺｈｅｎｍｉｎｇ（许振明）；ＪｉａｎｇＱｉｃｈｕａｎ（姜启川）；ＺｈａｏＹｕｇｕａｎｇ（赵宇光）；ＨｅＺｈｅｎ...     

铸造Cr12模具钢共晶碳化物的粒化

铸造Ｃｒ１２模具钢中共晶碳化物呈网状分布，经多元复合变质剂变质处理，共晶组织发生细化，离异共晶数量增多；经热处理后，碳化物变成粒状且均匀分布于基体中，冲击韧性得到明显提高，为铸造Ｃｒ１２模具钢的应用提供了保证。     

离心铸造条件对Mg_2Si/Al梯度复合材料组织与性能的影响

采用离心铸造法制备了内外层特别是内层富含细小Mg2Si颗粒的铝基梯度复合材料。研究了模具离心转速和预热温度对Mg2Si/Al梯度复合材料内层显微组织和性能的影响。研究结果表明,随着模具离心转速的增大,铸件内层Mg2Si颗粒相分布趋于均匀,颗粒相体积分数、显微硬度和耐磨性能均有较大幅度提高。而模具预热温度对铸件内层颗粒相体积分数及性能影响较小。在模具离心转速为1560 r/min,预热温度为300℃的条件下,铸件内层性能达到最佳值,磨损率仅为相同干滑动摩擦磨损条件下HT200的1/30~1/40。     

碳化物团球化奥氏体—贝氏体新型抗磨中锰钢

在中锰钢基础上，采用变质处理获得新型铸态抗磨钢：碳化物团球化奥氏体－贝氏体钢，它具有高强韧性，高耐磨性，是一种有广阔应用前景的新型抗磨材料。     

STRUCTURAL ZONING DIAGRAM OF SOLID SOLUTION Fe-Mn-C ALLOY AT 1000℃

本文根据76个成分点的试验结果及文献[1]中的有关结论,建立了含有不同稳定性大小奥氏体区的较为完整的Fe-Mn-C系合金1000℃固溶处理后的组织图,并对各类锰钢的化学成分范围及组织变化规律进行了分析与讨论。工业用锰钢的成分和组织可依据该组织图进行合理选择。