Strength of pure alumina ceramics above 1 GPa

Up to now, commercially available alumina ceramics were claimed to have strength between 400 and 550 MPa. However, our study shows strength ~ 2 times higher for commercially available alumina than commonly believed. The average and characteristic strength, measured on 31 pure alumina ceramic discs by ball on three balls (B3B) test, were 1205 ± 93 MPa and 1257 MPa, respectively, with a Weibull modulus of m = 11.8. Tested specimens were in form of discs with a diameter of 5 mm and thickness 0.5 mm. The grain size distribution of the alumina is bimodal with an average grain size of ~ 850 nm measured at the surface. The fracture reveals a mixed transgranular / intergranular failure mode. To avoid incorporation of additional flaws, the discs were tested as sintered. The characteristic flexural strength measured in B3B was recalculated according to Weibull theory for standard 4-point bending bars of size 3 × 4 × 45 mm as bend 856 MPa. The measured strength of nearly 900 MPa shows the potential of strength for high purity alumina ceramics.     

Towards Diastereomeric Pure Salts with Antisolvent Methods

Chiral molecules, especially enantiomers and diastereomers of purity > 99 %, present a significant market share within the chemical, pharmaceutical, and flavor industries. Antisolvent precipitations, both batch and semicontinuous operations to serve the current trends in flow chemistry were demonstrated to be environmentally benign and efficient tools in achieving high optical purities. Although salts are known to be insoluble in supercritical CO₂, instabilities of the nascent salts were detected and applied for increasing efficiency. Diastereomeric excess values of the crystalline products exceeded 99 % in maximum of three consecutive steps both by repeated resolution with half molar equivalent of the amine to the acid and by direct recrystallization of the salts.     

La0.6Sr0.4Co0.2Fe0.8O3-δ nanofiber cathode for intermediate-temperature solid oxide fuel cells by water-based sol-gel electrospinning: Synthesis and electrochemical behaviour

Water-based sol-gel electrospinning is employed to manufacture perovskite oxide La_0.6Sr_0.4Co_0.2Fe_0.8O_3-δ (LSCF) nanofiber cathodes for intermediate-temperature solid oxide fuel cells. LSCF fibrous scaffolds are synthesized through electrospinning of a sol-gel solution employing water as the only solvent. Morphological characterizations demonstrate that the LSCF fibers have highly crystalline structure with uniform elemental distribution. After heat treatment, the average fiber diameter is 250 nm and the porosity of the nanofiber tissue is 37.5 %. The heat treated LSCF nanofibers are applied directly onto a Ce_0.9Gd_0.1O_1.95 (CGO) electrolyte disk to form a symmetrical cell. Electrochemical characterization is carried out through electrochemical impedance spectroscopy (EIS) in the temperature range 550?°C–950?°C, and reproducibility of the electrochemical performance for a series of cells is demonstrated. At 650?°C, the average measured polarization resistance R_p is 1.0 Ω cm². Measured performance decay is 1 % during the first 33?h of operation at 750?°C, followed by an additional 0.7 % over the subsequent 70?h.     

A simple model for the semicontinuous heterophase polymerization: Ethyl methacrylate as a case example

A simple but comprehensive model considering homogeneous and micellar nucleation, coagulation, entry of radicals to particles and to micelles and radicals' exit from particles, is presented. The model is validated, in a starved semicontinuous heterophase polymerization of ethyl methacrylate, at three monomer addition rates. The model accurately describes the overall and instantaneous conversion, the average particle density and diameter, and the number and weight average molar masses evolutions over time. It is found that even though the average number of radicals is much smaller than 0.5, the system is not 0-1. An empirical function was used to describe the gel effect. The homogeneous nucleation was the prevailing mechanism for particle formation and large exit rates of radicals were observed. POLYM. ENG. SCI., 60: 223–232, 2019. © 2019 Society of Plastics Engineers     

High‐intensity sweeteners in espresso coffee: ideal and equivalent sweetness and time–intensity analysis

The efficient substitution of sucrose by a sweetener in beverages requires the application of some sensory techniques. First, one must determine the concentrations of the sweeteners under study, equivalent in sweetness to the ideal sucrose concentration. In addition, it is fundamental to determine which is most similar to sucrose. The objectives of this study were to determine the ideal sweetness for espresso coffee and the equivalent concentrations in sweetness of different sweeteners, as well as characterise the time–intensity profile of each sweetener in relation to sweetness. The sweeteners evaluated were sucralose, aspartame, neotame, a cyclamate/saccharin mixture (2:1) and stevia. The sucrose concentration considered ideal by consumers was 12.5% (w/v), and the equivalent concentrations of the sweeteners were 0.0159% for sucralose, 0.0549% for aspartame, 0.0016% for neotame, 0.0359% for the cyclamate/saccharin mixture and 0.0998% for stevia. The time–intensity analysis indicated that possibly the sweeteners neotame, aspartame and sucralose would be the best substitutes for sucrose.     

Physical Stability of Octenyl Succinate–Modified Polysaccharides and Whey Proteins for Potential Use as Bioactive Carriers in Food Systems

The high cost and potential toxicity of biodegradable polymers like poly(lactic‐co‐glycolic)acid (PLGA) has increased the interest in natural and modified biopolymers as bioactive carriers. This study characterized the physical stability (water sorption and state transition behavior) of selected starch and proteins: octenyl succinate–modified depolymerized waxy corn starch (DWxCn), waxy rice starch (DWxRc), phytoglycogen, whey protein concentrate (80%, WPC), whey protein isolate (WPI), and α‐lactalbumin (α‐L) to determine their potential as carriers of bioactive compounds under different environmental conditions. After enzyme modification and particle size characterization, glass transition temperature and moisture isotherms were used to characterize the systems. DWxCn and DWxRc had increased water sorption compared to native starch. The level of octenyl succinate anhydrate (OSA) modification (3% and 7%) did not reduce the water sorption of the DWxCn and phytoglycogen samples. The Guggenheim–Andersen–de Boer model indicated that native waxy corn had significantly (P < 0.05) higher water monolayer capacity followed by 3%‐OSA‐modified DWxCn, WPI, 3%‐OSA‐modified DWxRc, α‐L, and native phytoglycogen. WPC had significantly lower water monolayer capacity. All Tg values matched with the solid‐like appearance of the biopolymers. Native polysaccharides and whey proteins had higher glass transition temperature (Tg) values. On the other hand, depolymerized waxy starches at 7%‐OSA modification had a “melted” appearance when exposed to environments with high relative humidity (above 70%) after 10 days at 23 °C. The use of depolymerized and OSA‐modified polysaccharides blended with proteins created more stable blends of biopolymers. Hence, this biopolymer would be suitable for materials exposed to high humidity environments in food applications.