The influence of NaCl and CO2 on the atmospheric corrosion of magnesium alloy AZ91

The influence of NaCl and CO₂ on the atmospheric corrosion of magnesium alloy AZ91 is studied in the laboratory. Samples were exposed under carefully controlled air and flow conditions; the relative humidity was 95%, the temperature was 22.0°C and the concentration of CO₂ was < 1 ppm or 350 ppm. Different amounts of sodium chloride (0–70 μg/cm²) were added before exposure. The corrosion products were analyzed by gravimetry, ion chromatography, X‐ray diffraction and scanning electron microscopy. Mass gain and metal loss results are reported. The combination of high humidity and NaCl is very corrosive towards AZ91. However, the NaCl‐induced corrosion is inhibited by ambient concentrations of CO₂. Exposure in the absence of CO₂ gives rise to heavy pitting, with brucite, Mg(OH)₂, being the dominant corrosion product. In the presence of CO₂ a layer of hydrated magnesium hydroxy carbonate, Mg₅(CO₃)₄(OH)₂ · 5 H₂O forms. A tentative corrosion mechanism is presented that explains the behavior in the two environments.     

Exponential Stability of Interval Dynamical Systems with Quadratic Nonlinearity

This article proposes an approach for investigating the exponential stability of a nonlinear interval dynamical system with the nonlinearity of a quadratic type on the basis of the Lyapunov’s direct method. It also constructs an inner estimate of the attraction domain to the origin for the system under consideration.