Fully renewable limonene‐derived polycarbonate as a high‐performance alkyd resin

Limonene‐derived polycarbonate‐based alkyd resins (ARs) have been prepared by copolymerization of limonene dioxide with CO₂, catalysed by a β‐diiminate zinc–bis(trimethylsilyl)amido complex, and subsequent chemical modification with soybean oil fatty acids using triphenylethylphosphonium bromide as the catalyst. This quantitative partial modification was realized via epoxy–carboxylic acid chemistry, affording ARs with higher oil lengths, lower polydispersities and higher glass transition temperatures (T_g) in comparison to a conventional polyester AR based on phthalic acid, multifunctional polyol pentaerythritol and soybean fatty acid. The novel limonene polycarbonate AR and the conventional polyester AR were evaluated as coatings and both the physical drying (without the presence of the oxidative drying accelerator Borchi® Oxy Coat) and chemical curing (with Borchi® Oxy Coat) processes of these coatings were monitored by measuring the König hardness and complex modulus development with time. A better performance was obtained for the alkyd paint containing polycarbonates modified with fatty acids (FA‐PCs), which showed a faster chemical drying, a higher König hardness and a higher T_g in coating evaluation, demonstrating that the fully renewable FA‐PCs are promising resins for alkyd paint applications. © 2019 Society of Chemical Industry     

Calorimetric study of ytterbium orthovanadate YbVO4 polycrystalline ceramics

The heat capacity of ytterbium orthovanadate was first measured by adiabatic calorimetry in the temperature range T?=?12.28–344.06?K. No obvious anomalies were observed on the curve obtained. The values of standard thermodynamic functions in the temperature range T?=?0–400 K were calculated. Based on low-temperature calorimetry data obtained, previously published data on the high-temperature heat capacity of ytterbium orthovanadate were corrected. The anomalous contribution to heat capacity for YbVO₄ was compared with the data known for YbPO₄.     

Preparation of nanocrystalline nickel oxide from nickel hydroxide using spark plasma sintering and inverse Hall-Petch related densification

Nanocrystalline nickel oxide (NiO) was prepared from nickel hydroxide by Spark plasma sintering (SPS) and the mechanisms involved in the densification of NiO were studied. Reverse precipitated nickel hydroxide powders were SPS processed at 400, 600 and 700?°C with 70?MPa pressure. Pure NiO with 12?nm crystallite size formed after 400?°C sintering process. However NiO grains had grown to 18 and 38?nm after 600 and 700?°C sintering respectively. NiO pellets prepared using 600 and 700?°C SPS sintering schedules had relative densities of 83% and 94% respectively. Two displacement rate regimes were observed during densification of NiO in both 600 and 700?°C sintering processes. Decomposition of nickel hydroxide and particle sliding of NiO led to first displacement rate maximum while inverse Hall-Petch based plastic deformation facilitated densification during the constant second displacement rate regime. No densification occurred during sintering holding times indicating the limited role that diffusion played during densification.     

A Giant Frequency Shift in the Raman Spectrum of Water Adsorbed on a Metallic Silver Surface

The Raman spectrum of water adsorbed on a metallic silver surface reveals an anomalously large shift of the vibrational frequency as compared to that in the bulk. The results are compared to data reported by other researchers, and possible interpretations of the observed phenomenon are discussed.     

Role of Elastic Interphase Deformations in the Formation of Crystal Structure of β-Nb Particles Precipitating in a Zr–2.5% Nb Alloy

X-ray diffraction analysis has been used to study the structure of the α-Zr matrix phase and the precipitation of β-Nb particles upon the annealing of a Zr–2.5% Nb deformed alloy. It has been found that the process of the precipitation of the strengthening β-Nb particles in the alloy is accompanied by the appearance of fields of elastic interphase deformations in the matrix α phase of the alloy due to the difference in the specific atomic volumes of the crystal structures of the matrix and precipitated phases. It has been shown experimentally that, as a result of the presence of interphase deformations in the alloy, the bcc crystal structure of the precipitating β-Nb particles undergoes monoclinic distortions.