Smart ultrasonic sensors systems: potential of aluminum nitride thin films for the excitation of the ultrasound at high frequencies

We investigated the potential of the aluminum nitride films to excite ultrasonic waves at frequencies >50?MHz. The deposition process of the aluminum nitride thin film layers on silicon substrates was investigated and optimized regarding their piezoelectric behavior. Large single element transducers were deposited on silicon substrates with aluminum electrodes, under different parameters for the magnetron sputter process, like pressure and bias voltage. Special test setup and a measuring station were created to characterize the sensors. Acoustical measurements were carried out in pulse echo mode up to 500?MHz and the values of piezoelectric charge constant (d₃₃) were determined. As a result, two parameter sets were found for the sputtering process to obtain an excellent piezoelectric charge constant of about 7.2?pC/N maximum. Then the sputtering process with these parameters was used to deposit sensors on various substrate materials and with different electrode sizes.     

Exergy analysis of incremental sheet forming

Research in the last 15 years has led to die-less incremental forming processes that are close to realization in an industrial setup. Whereas many studies have been carried out with the intention of investigating technical abilities and economic consequences, the ecological impact of incremental sheet forming (ISF) has not been studied so far. Using the concept of exergy analysis, two ISF technologies, namely single sided and double sided incremental forming, are investigated and compared to conventional forming and hydroforming. A second exergy analysis is carried out with the purpose of examining the environmental impact of different forming technologies from a supply chain perspective. Therefore, related upstream activities (die set production, aluminum sheet production and energy conversion and supply) are included into the exergy analysis. The entire supply chain is modeled with Matlab/Simulink. The results of both analyses suggest that ISF is environmentally advantageous for prototyping and small production runs.     

Reduction of the elongation at break of thermoplastic polyolefins through melt blending with polylactide and the influence of the amount of compatibilizers and the viscosity ratios of the blend components on phase morphology and mechanics

The objective of this work is the synthesis of a polypropylene/ethylene‐propylene‐rubber (TPO)/polylactide (PLA)/compatibilizer (PVM) blend to reduce the elongation at break of TPO by blending TPO with brittle PLA. Three TPO types with different viscosities were melt blended with PLA and an ethylene/n‐butylacrylate/glycidyl methacrylate terpolymer (PVM) as reactive compatibilizer. All blends had a constant PLA amount of 30 wt%. Two parameters were varied in the experiments, viscosity of the TPO types, and amount of PVM used in the blends. Both parameters played important roles in reducing the nominal elongation at break compared to pure TPO foils and influencing the phase morphology of extruded blend foils. The nominal elongation at break could be reduced by 100‐150% through blending TPO with PLA and PVM. Characterization regarding the blend morphology, especially the size and shape of the dispersed PLA phase in the TPO matrix was done by Environmental Scanning Electron Microscopy (ESEM) images. Investigations of the morphology showed that size and shape of dispersed PLA phases are dependent on the viscosity ratios of the blend components and on the amount of compatibilizer in the blend. AFM images of the polymer blends reveal soft rubbery layers around the dispersed PLA phases. POLYM. ENG. SCI., 56:905–913, 2016. © 2016 Society of Plastics Engineers     

Analyses of structurally modified quasi‐solid‐state electrolytes using electrochemical impedance spectroscopy for dye‐sensitized solar cells

Electrochemical properties of structurally modified quasi‐solid‐state electrolytes were examined using porous substrates (PSs). The PS was prepared into two categories by a phase inversion method with a brominated poly(phenylene oxide) (BPPO): the sponge and finger types. Effects of the humidification and cosolvent compositions on the morphology of the PS were analyzed by scanning electron microscopy. In all cases of the PSs, a higher V_OC was observed of about 0.1 V than that of a liquid electrolyte owing to a suppressed back electron charge transfer. In addition, the PS prepared by the polymer solution of 1 : 4 : 1 (BPPO : N‐methyl‐2‐pyrrolidone : butyl alcohol) with the humidification process showed better photovoltaic properties in terms of the current density and conversion efficiency owing to the appropriate combinations of pore size, tortuosity, and interconnectivity. Effects of the pore structures were intensively examined using electrochemical impedance spectroscopy. The impedance results revealed that large pores at the surface layers are advantageous for a lower R_S and R_TiO2. Meanwhile, the straight inner structure is beneficial for the facile I^?/I₃^? diffusion, thus lowering R_Pt. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 39739.     

Anwendungen des Kern-Overhauser-Effekts. I. Strukturuntersuchungen an Z/E-isomeren 2,3-Diarylazetidin-3-olen

Applications of the Nuclear Overhauser Effect. I. Investigations of the Structure of Z/E Isomeric 2,3-Diarylazetidin-3-oles The relative configurations of Z/E-isomeric 2,3-diaryl-azetidin-3-oles are determined by mass spectrometry and ¹H-n.m.r.-NOE-measurements. The increase of the C(2)-H line intensity by saturation of the OH-signals demonstrates the Z-position of the 2,3-diaryl groups in the isomers 2a .