Preparation of TiB2 sintered compacts by hot pressing

A sintered compact of titanium diboride (TiB₂) was prepared by hot pressing of the synthesized TiB₂ powder, which was obtained by a solid-state reaction between TiN and amorphous boron. Densification of the sintered compact occurred at 20 MPa and 1800° C for 5 to 60 min with the aid of a reaction sintering, including the TiB₂ formation reaction between excess 20 at % amorphous boron in the as-synthesized powder (TiB₂ + 0.2B) and intentionally added 10 at % titanium metal. A homogeneous sintered compact of a single phase of TiB₂, which was prepared by hot pressing for 30 min from the starting powder composition [(TiB₂ + 0.2B) + 0.1 Ti], had a fine-grained microstructure composed of TiB₂ grains with diameters of 2 to 3 m. The bulk density was 4.47 g cm^–3, i.e. 98% of the theoretical density. The microhardness, transverse rupture strength and fracture toughness of the TiB₂ sintered compact were 2850 kg mm^–2, 48 kg mm^–2 and 2.4 MN m^–3/2, respectively. The thermal expansion coefficient increased with increasing temperature up to 400° C and had a constant value of 8.8 x 10^–6 deg^–1 above 500° C.     

Reaction control of TiB2 formation from titanium metal and amorphous boron

TiB₂ powder was synthesized by a controlled formation reaction from titanium metal and amorphous boron. Precursory TiB₂ formed by the pretreatment of the mixed powder (mole ratio: B/Ti=2.0) at 600° C for 60 min in an argon stream. Hollow TiB₂ powder with an average grain size of 15m was obtained by subsequent heat treatment above 900° C for more than 60 min in an argon stream. The formation reaction of TiB₂ powder was further controlled by pretreatment of the mixed powder at 600° C for 60 min in a hydrogen and argon stream and subsequent heat treatment at 1000° C for 360 min in an argon stream, when hollow-free TiB₂ powder was formed by a milder formation reaction between amorphous boron and the reformed titanium metal with hydrogen diffused lattice.     

Mechanical Properties of Alumina/Silicon Carbide Whisker Composites

The improvement of mechanical properties of Al₂O₃/SiC whisker composites has been studied with emphasis on the effects of the whisker content and of the hot-pressing temperature. Mechanical properties such as fracture toughness and fracture strength increased with increasing whisker content up to 40 wt%. In the case of the high SiC whisker content of 40 wt%, fracture toughness of the sample hot-pressed at 1900° decreased significantly, in spite of densification, compared with one hot-pressed at 1850°. Fracture toughness strongly depended on the microstructure, especially the distribution of SiC whiskers rather than the grain size of the Al₂O₃ matrix.     

Role of tungsten in promoting selective reduction of NO with CO over Ir/WO3–SiO2 catalysts

Catalytic hydrogenation of naphthalene to decalin was studied over a carbon-supported rhodium catalyst in supercritical carbon dioxide solvent at 333 K, and the results were compared with those in an organic solvent. cis-, trans-Decalin and tetralin were formed from the beginning of the reaction in supercritical carbon dioxide. Higher concentration of hydrogen in carbon dioxide solvent and on the active site, and also the suppression of desorption of partially hydrogenated tetralin molecules from the active site would be responsible for higher selectivity to cis-decalin in supercritical carbon dioxide than that in an organic solvent.     

Development of three-electrode type micro-electrochemical reactor on anodized aluminum with photon rupture and electrochemistry

Photon rupture with a focused single pulse of pulsed YAG-laser irradiation was used to fabricate an aluminum electrochemical micro-reactor. Porous type anodic oxide film formed on aluminum specimens was irradiated in solutions with a pulsed Nd-YAG laser beam through a convex lens to fabricate micro-channels, micro-electrode, and through holes (for reference electrode, solution inlet, and outlet). During irradiation, specimens were moved by a computer controlled XYZ stage. After irradiation, the surface of the micro-channel and through hole were again treated to form anodic oxide film and the surface of the micro-electrode was treated electrochemically to provide an Au layer. The calculated volume of the micro-reactor including micro-channel and through holes is about 1.5 μl. The cyclic voltammogram of the micro-electrochemical cell was measured in K₃Fe(CN)₆/K₄Fe(CN)₆ with both static and flowing solution at different scanning rates. The anodic and cathodic peak currents were measured and the values depended on scanning rate and ion concentration when the solution was static. With the flowing solution, limiting currents were observed and the anodic limiting current was increased with the cubic root of the solution flow rate.     

Alternative technologies for biotechnological fuel ethanol manufacturing

The challenges of implementing biorefineries on a global scale include socioeconomic, financial, and technological constraints. In particular, the development of biorefineries is tightly linked to the continued availability of fermentation raw materials. These constraints can be relaxed by the use of diverse raw materials, while advances that confer higher flexibility would enable biotechnological plant managers to swiftly react to volatile markets. In conventional processes, Saccharomyces cerevisiae grows on a relatively limited range of substrates, and produces only a single product—ethanol. Given the observed maturity of the S. cerevisiae fermentation technology, alternatives to baker's yeast may be needed to tip the economic balance in favour of biotechnological ethanol. These alternative fermentation technologies may allow a greater diversity of substrates to be used to produce an individually tailored mix of ethanol and other chemicals. Copyright © 2007 Society of Chemical Industry     

Sesamin is a potent and specific inhibitor of Δ5 desaturase in polyunsaturated fatty acid biosynthesis

Incubation with sesame oil increases the mycelial dihomo-γ-linolenic acid content of an arachidonic acid-producing fungus,Mortierella alpina, but decreases its arachidonic acid content [Shimizu, S., K. Akimoto, H. Kawashima, Y. Shinmen and H. Yamada (1989)J. Am. Oil Chem. Soc. 66, 237–241]. The factor causing these effects was isolated and identified to be (+)-sesamin. The results obtained in experiments with both a cell-free extract of the fungus and with rat liver microsomes demonstrated that (+)-sesamin specifically inhibits Δ5 desaturase at low concentrations, but does not inhibit Δ6, Δ9 and Δ12 desaturases. Kinetic analysis showed that (+)-sesamin is a noncompetitive inhibitor (K_i for rat liver Δ5 desaturase, 155 μM). (+)-Sesamolin, (+)-sesaminol and (+)-episesamin, also inhibited only Δ5 desaturases of the fungus and liver. These results demonstrate that (+)-sesamin and related lignan compounds present in sesame seeds or its oil are specific inhibitors of Δ5 desaturase in polyunsaturated fatty acid biosynthesis in both microorganisms and animals. On leave from Suntory Ltd.     

Carbon fiber from natural biopolymer Bombyx mori silk fibroin with iodine treatment

Carbon fibers were prepared from silk fibers after an iodine treatment and the carbon yield, fiber morphology, structure and mechanical properties were investigated. A single or multi-step carbonization process was used for the preparation. In the single step process, silk fibroin (SF) fibers were heated from 25 to 800 °C with a heating rate of 5 °C min⁻¹ under Ar atmosphere. However, the carbon fiber obtained was partially melted and was too fragile to handle. For better performance, SF fibers were treated with iodine vapor at 100 °C for 12 h and untreated and iodinated SF fibers were heated from 25 to 800 °C by a multi-step carbonization process, which was defined based on the optimum thermal degradation rate of silk. In this multi-step process, the carbon fibers obtained from iodinated SF were structurally intact and stable in appearance, and the carbon yield achieved was ca. 36 wt.%, much higher than the value for untreated SF. X-ray diffraction, Raman spectroscopy and transmission electron microscopic observation revealed that the obtained carbon fibers from both untreated and iodinated SFs had a basically amorphous structure. The strength of carbon fibers prepared from iodinated SF using the multi-step carbonization was considerably increased compared to that of untreated SF. According to viscoelastic measurement, by heating above 280 °C the iodine introduced intermolecular cross-linking of the SF, and its melt flow was inhibited which produced a higher yield and better performance of the carbon fiber.     

Production of dihomo-γ-linolenic acid byMortierella alpina 1S-4

The mycelial dihomo-γ-linolenic acid content of an arachidonic acid-producing fungus,Mortierella alpina 1S-4, was found to increase, with an accompanying marked decrease in its arachidonic acid content, on cultivation with sesame oil. The resultant mycelia were found to be a rich source of dihomo-γ-linolenic acid. This unique phenomenon was suggested to be due to specific repression of the conversion of dihomo-γ-linolenic acid to arachidonic acid by the oil. After fractionation of the oil with acetone into oil and non-oil fractions, it was found that the effective factor(s) was present in the non-oil fraction. In a study on optimization of the culture conditions for the production of dihomo-γ-linolenic acid byM. alpina 1S-4, a medium containing glucose, yeast extract and the non-oil fraction was found to be suitable for the production. Under the optimal conditions in a 50-1 fermentor, the fungus produced 107 mg of dihomo-γ-linolenic acid/g dry mycelia (2.17 g/l of culture broth). This value accounted for 23.1% of the total fatty acids in the lipids extracted from the mycelia. The mycelia were also rich in arachidonic acid (53.5 mg/g dry mycelia, 11.2%). Other major fatty acids in the lipids were palmitic acid (24.1%), stearic acid (7.0), oleic acid (20.1), linoleic acid (6.6) and γ-linolenic acid (4.1). On leave from Suntory Ltd.     

Silica-supported cobalt catalysts for the selective reduction of nitrogen monoxide with propene

Catalytic behavior of silica-supported transition metals for NO reduction with propene in the presence of oxygen was investigated. While both silica and cobalt oxides did not show any activity for the selective NO reduction, impregnated CoO/SiO₂ prepared from cobalt acetate showed good activity although the preparation conditions had significant effect on the activity. It was suggested that highly dispersed surface Co²⁺ ions on silica are responsible for the catalytic activity.