针对输变电工程陆续开展基建智慧工地,智慧物联系统平台建设已成为常态,目前建设思路主要是通过基于"大、云、物、移、智"开展新技术、新产品的应用,实现"人、机、料、法、环、测"等施工现场六要素的感知采集,以支撑智慧工地及基建信息化的业务开展.如何实现施工现场感知层数据、视频流数据以及业务数据三类数据的传输,并实现设备安装布设无线化、部署简易化,是重点思考和解决的方向,提出建设以5G(generation)专网为主,无线接入点(access point,AP)网络、远距离(long range,LoRa)通信网络为辅的多网融合方案,开展智慧工地网络层的建设,以支撑智慧工地物联网业务的开展,提供高质量、高体验的网络层支撑.     

Crystallographic structure- and texture-dependent fracture behavior of polycrystalline lead zirconate titanate ceramics

Journal of Electroceramics - The effect of crystallographic structure and texture on the fracture behavior of lead zirconate titanate (PZT) ceramics was investigated. PZT ceramics with Zr/Ti ratio...     

圆柱体平板镦粗应力场的有限元分析

应用刚粘塑性有限元法对圆柱体在两平板间镦粗时的应力场进行了分析 ,给出了毛坯在不同初始高径比时的心部应力随压下量的变化曲线。由此得出 :在变形过程中 ,圆柱体心部存在两向拉应力 ;并且在墩粗过程中 ,当瞬时高径比约为 1 .0时 ,心部σθ、σr 由拉应力转变为压应力。     

10 kV绝缘横担的轻量化设计及应用研究

为充分发挥绝缘横担轻质高强的特点,提高绝缘横担的使用寿命,满足腐蚀严重区域的使用需求,引进高强铝合金材料对10 kV绝缘横担进行轻量化设计及应用研究.从横担芯体、中间固定金具及配套附件三个方面对绝缘横担进行了轻量化的结构设计,采用有限元软件进行了详细的计算分析,为试制提供技术支撑.采用高强铝合金材料对方棒和T形绝缘横担的中间固定金具和配套抱箍进行了试制,并进行了抗弯、抗拉和抗扭测试,结果均满足要求.为了验证铝合金材料金具在绝缘横担中使用的稳定性,对方棒绝缘横担进行了热机循环试验,然后对两端金具进行抗拉试验,结果表现良好.经统计,高强铝合金材料在10 kV绝缘横担中的应用,大幅降低了整体质量(减轻近40％),可大大减少安装运输成本.     

Cardiac Oxidative Signaling and Physiological Hypertrophy in the Na/K-ATPase α1s/sα2s/s Mouse Model of High Affinity for Cardiotonic Steroids

The Na/K-ATPase is the specific receptor for cardiotonic steroids (CTS) such as ouabain and digoxin. At pharmacological concentrations used in the treatment of cardiac conditions, CTS inhibit the ion-pumping function of Na/K-ATPase. At much lower concentrations, in the range of those reported for endogenous CTS in the blood, they stimulate hypertrophic growth of cultured cardiac myocytes through initiation of a Na/K-ATPase-mediated and reactive oxygen species (ROS)-dependent signaling. To examine a possible effect of endogenous concentrations of CTS on cardiac structure and function in vivo, we compared mice expressing the naturally resistant Na/K-ATPase α1 and age-matched mice genetically engineered to express a mutated Na/K-ATPase α1 with high affinity for CTS. In this model, total cardiac Na/K-ATPase activity, α1, α2, and β1 protein content remained unchanged, and the cardiac Na/K-ATPase dose–response curve to ouabain shifted to the left as expected. In males aged 3–6 months, increased α1 sensitivity to CTS resulted in a significant increase in cardiac carbonylated protein content, suggesting that ROS production was elevated. A moderate but significant increase of about 15% of the heart-weight-to-tibia-length ratio accompanied by an increase in the myocyte cross-sectional area was detected. Echocardiographic analyses did not reveal any change in cardiac function, and there was no fibrosis or re-expression of the fetal gene program. RNA sequencing analysis indicated that pathways related to energy metabolism were upregulated, while those related to extracellular matrix organization were downregulated. Consistent with a functional role of the latter, an angiotensin-II challenge that triggered fibrosis in the α1^r/rα2^s/s mouse failed to do so in the α1^s/sα2^s/s. Taken together, these results are indicative of a link between circulating CTS, Na/K-ATPase α1, ROS, and physiological cardiac hypertrophy in mice under baseline laboratory conditions.     

Influences of mullite fibers on mechanical and thermal properties of silica-based ceramic cores

Mullite fibers composite silica-based ceramic cores were successfully prepared by injection molding. The effects of mullite fibers on the mechanical and thermal properties of ceramic cores were investigated. The results indicated that the linear shrinkage was significantly decreased and the porosity was gradually increased with the increase of mullite fibers. In addition, the flexural strength for the room temperature and the simulated casting temperature of 1500°C was increased to a maximum value when the content of mullite fibers was about 1 wt.%, and then decreased with the increase of mullite fibers. The mullite fibers of 1 wt.% presented excellent mechanical properties with a linear shrinkage of .65%, a porosity of 6.96%, and a flexural strength of 17 MPa at room temperature and 34.83 MPa at the simulated casting temperature of 1500°C. Besides, the change in microstructure and properties in various contents of mullite fibers were analyzed.     

LaMgAl11O19-La2Ce2O7 复合陶瓷的高温相稳定性

La2Ce2O7(LC) 和 LaMgAl11O19(LMA) 是两种新型热障涂层材料。 LC 具有优良的热物理及抗腐蚀性能, 但 其断裂韧性差。 LMA 具有良好的综合性能, 特别是力学性能优良。 基于复合材料设计理念, 为充分利用 LC 和 LMA 的优势, 本文探究了制备 LMA-LC 双相复合陶瓷的可行性。 采用高温固相法合成了 LMA 和 LC 粉末, 重 点研究了 LMA 和 LC 的高温稳定性, 初步研究了 LMA-LC 复合陶瓷块材的力学性能。 结果表明： LMA 和 LC 在 高温下发生了化学反应, 反应程度随温度升高而加剧, 主要反应产物为 LaAlO3, 其在低温下的铁弹性可能是复 合陶瓷在室温下具有良好力学性能的原因。     

粉末注射成形耐热不锈钢的工艺研究

以元素混合粉为原料,研究了耐热不锈钢的注射成形工艺.重点讨论了烧结温度、时间及气氛对耐热不锈钢致密度、力学性能及微观组织的影响,获得的最佳工艺为烧结温度1375℃,时间60 min,真空气氛.在此条件下制备了致密度98.12%、抗拉强度510 MPa、铁素体组织的PIM耐热不锈钢.     

金属及合金中钛的光度分析近况

综述了金属及合金中钛的光度测定方法新近进展情况。     

催化动力学光度法在贵金属测定中的实际应用

综述了催化动力学光度法在钌、铑、钯、银、锇、铱、铂等贵金属测定中的实际应用新近发展状况。