CuO-SiO2气凝胶@TiO2纳米纤维无牺牲剂光催化还原CO2

采用溶胶-凝胶法制备CuO-SiO2复合气凝胶,通过在气凝胶孔道内填充TiCl4,然后将其气相水解,得到了在CuO-SiO2气凝胶表面生长了高结晶度的TiO2纳米纤维(CuO-SiO2@TiO2),纤维直径～16 nm.通过XPS、UPS、UV-Vis DRS、荧光光谱(PL)等表征了材料的结构及光电性能.结果表明,制备的CuO-SiO2@TiO2对可见光有明显吸收,且荧光强度较商用TiO2(P25)大幅降低,光生电子-空穴对更加稳定.再在纳米纤维上负载CuO,所得CuO-SiO2@TiO2/CuO在可见光区的荧光强度进一步增强.以300 W氙灯为光源,分别以CuO-SiO2@TiO2及CuO-SiO2@TiO2/CuO为催化剂,无牺牲剂条件下光催化还原CO2,4 h后甲醇产率分别为1304.0及1589.0μmol/g-cat,转换频率(TOF)分别为0.038及0.046 h–1.循环实验表明,纳米纤维具有较好的光催化稳定性,经过4次光催化循环实验后,CuO-SiO2@TiO2/CuO的保留率～94％,甲醇产率可达1472.0μmol/g-cat,TOF为0.042 h–1.     

基于聚三唑固化体系的ADN推进剂研究进展

综述了国内外聚三唑固化体系及基于其的二硝酰胺铵(ADN)推进剂应用研究情况,分析了聚三唑固化体系的优缺点,指出了基于聚三唑固化体系的ADN推进剂的应用研究方向.认为聚三唑固化体系具有反应条件温和、对水分不敏感、毒性低等优点,以及玻璃化转变温度偏高、力学性能偏低等缺点.在空间推进、洁净绿色推进以及低特征信号推进剂领域,基...     

塑料换热器在海水淡化中的应用

阐述了塑料换热器在海水淡化中应用的研究状况,分析了塑料换热器所具有的优势如成本更低、更好的防腐防垢性能,质量更轻和能耗更低等,重点讨论了塑料换热器在露点蒸发淡化技术中的应用和有利条件,并对塑料换热器在海水淡化中的应用前景作了进一步的展望。     

Translucent Mg-α-Sialon Ceramics Prepared by Spark Plasma Sintering

The translucent Mg-α-sialon ceramics have been prepared by spark plasma sintering (SPS) α-Si₃N₄ powder with AlN and MgO as the additives at 1850°C for 5 min. The sample possesses a uniform, dense microstructure under the rapid densification of SPS process. The translucent Mg-α-sialon ceramics achieve the maximum transmittance of 66.4% for the sample of 0.5 mm in thickness in the medium infrared region, which could be attributed to the equiaxed microstructure and few glassy phase confirmed by the observation of transmission electron microscopy. The material also exhibits good mechanical properties of high hardness (21.4±0.3 GPa) and fracture toughness (6.1±0.1 MPa·m^1/2).     

4，4’-联苯二甲酸的合成研究

研究了4,4’-联苯二甲酸的合成,以联苯为原料,经过氯甲基化、氯化、水解得到了目标化合物,总收率48％,产品纯度99．2％。     

Effect of aliphatic diacyl adipic dihydrazides on the crystallization of poly(lactic acid)

A series of aliphatic diacyl adipic dihydrazides (ADHs) with different alkyl moieties were synthesized by the reaction between adipic dihydrazide and acyl chloride. Then these ADHs were solution blended with PLA respectively and were evaluated as nucleating agents. Through the investigation of nonisothermal and isothermal crystallization, it was found that both the crystallization rate and the crystallinity of PLA could be enhanced by adding only 1 wt % of ADHs. Especially for ADH‐Oc (ADH‐Octyl), the crystallization rate of PLA increased about 4 times at 105°C. Optical morphology showed that and the size of PLA spherulites decreased and the nucleation density increased with the existence of ADH‐Oc. Meanwhile, the crystal structure of PLA were not discerniblly affected after the addition of ADHs as found by wide‐angle X‐ray diffraction. Thus, this study suggested these ADHs compounds are simple and potential nucleating agents to enhance crystallization ability of PLA. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 42028.     

化学生物学实验课程的建设与教学实践

化学生物学实验课是培养化学生物学专业学生的实验技能和创新意识过程中发挥主导作用的主干实验课。华南农业大学于2008年开设化学生物学实验课,历经多年的课程建设与教学实践,逐渐完善该实验课并形成具有自己特色的化学生物学实验课程。文章主要介绍了该校化学生物学实验课在课程建设、教学方式及成绩考核三方面所做的一些探索和实践。     

退火对PA6结晶和拉伸性能的影响

通过调节退火时间和退火温度,研究了退火工艺对尼龙(PA)6结晶性能以及PA6在不同拉伸速率下的拉伸性能的影响。结果表明,在100℃恒温退火时,随着退火时间的增加,PA6初始熔融温度逐渐升高,熔限减小,γ晶的晶粒尺寸增大,但结晶度变化不大;在5 h退火时间下,随着退火温度的增加,PA6结晶度呈现先增加后降低的趋势,而α晶晶粒尺寸逐渐增大。总体上看,不同拉伸速率下退火时间和退火温度对拉伸强度的影响较小,相对来看,退火温度为100℃时拉伸强度较高,而当退火温度达到200℃时,拉伸强度显著下降;当拉伸速率较高或较低时,不同退火时间下的PA6断裂伸长率相差不大,而当拉伸速率为20,50 mm/min时,随退火时间的增加,断裂伸长率逐渐降低;退火温度为100,130℃的PA6断裂伸长率保持在相对较高值,且拉伸速率越低,其值越高,但随着拉伸速率增加,其下降趋势也最快;高拉伸速率下,退火温度对PA6断裂伸长率影响较小。以上结果表明,当对PA6进行退火处理时,在拉伸性能方面需要考虑拉伸速率的影响。     

沸石粉对PP中VOC散发性能的影响

报道了利用沸石粉减少聚丙烯(PP)中挥发性有机化合物(VOC)的方法.通过调整烘烤、挤出工艺等方法优化了PP中VOC散发性能,并利用气相色谱-质谱联用仪对结果进行表征.结果表明,将PP以110℃烘烤18 h,并与2份沸石粉共混后在挤出机内210℃下真空挤出是最佳挤出工艺.在该条件下,PP中TVOC散发浓度在10307μg/m3左右,表明该方法具有一定的开发价值.     

C/C复合材料表面TaC涂层的制备和生成机制

报道了一种在C/C复合材料基体上制各抗烧蚀TaC涂层的新方法.采用红外光谱、XRD及SEM表征了生成TaC涂层的Ta源:TaO2F·rH2O·TaF5.采用SEM观察了不同温度下转变生成的TaC涂层的形貌.在1200℃高温热处理,TaC涂层形貌为细颗粒状,在1800℃高温热处理后,TaC涂层为柱状晶.TaC的生成机制为:TaO2F·rH2O·TaF5高温分解凝聚生成的Ta2O5沉积在C/C复合材料基体表面,碳原子在Ta2O5中扩散反应生成TaC,TaC涂层形貌可由生成Ta2O5的凝聚成核理论解释.