The prospects of non-volatile phase-change RAM

Phase-change read-and-write memory (PRAM) is a promising memory that can solve the problems of conventional memory—scalability, read/write speed, and reliability. We will review the opportunities and technical challenges of PRAM. The most important challenge of PRAM is the reduction of the writing current. Various approaches to reduce the writing current will be reviewed and the prospects of PRAM are discussed.     

A Mass Transport Model for Drying Wood under Isothermal Conditions

Mass transport in wood during drying can have different mechanisms at different periods of drying. Depending on the current moisture content (MC) and the structure of the wood, the driving forces for the mass transport are essentially different. Above the fiber saturation point (FSP), the lumens are partially saturated and the transport of liquid (free) water occurs as a consequence of capillary action. On the other hand, below the FSP, bound water within the cell walls is conveyed by diffusion, and water vapor in the lumens moves under influence of pressures gradient. Based on these considerations, a unified model is presented that takes into account the transport of the different moisture phases. Simulation of the drying of a Norway spruce sample at 50°C from about 135 to 7% MC is carried out using the finite element method (FEM). Comparison between the simulated average MC and the experimental observations obtained from X-ray computed tomography (CT) shows reasonable agreement. Possible simplifications in the model are briefly discussed as well as some aspects of the numerical implementation. Finally, the influence of absolute permeability on the average MC is studied.     

The influence of NaCl and CO2 on the atmospheric corrosion of magnesium alloy AZ91

The influence of NaCl and CO₂ on the atmospheric corrosion of magnesium alloy AZ91 is studied in the laboratory. Samples were exposed under carefully controlled air and flow conditions; the relative humidity was 95%, the temperature was 22.0°C and the concentration of CO₂ was < 1 ppm or 350 ppm. Different amounts of sodium chloride (0–70 μg/cm²) were added before exposure. The corrosion products were analyzed by gravimetry, ion chromatography, X‐ray diffraction and scanning electron microscopy. Mass gain and metal loss results are reported. The combination of high humidity and NaCl is very corrosive towards AZ91. However, the NaCl‐induced corrosion is inhibited by ambient concentrations of CO₂. Exposure in the absence of CO₂ gives rise to heavy pitting, with brucite, Mg(OH)₂, being the dominant corrosion product. In the presence of CO₂ a layer of hydrated magnesium hydroxy carbonate, Mg₅(CO₃)₄(OH)₂ · 5 H₂O forms. A tentative corrosion mechanism is presented that explains the behavior in the two environments.