Effect of specimen size and loading conditions on spalling of concrete

Different qualities of concrete have been fire tested using different geometries of the specimens as well as different load levels and load configurations. The main objective with the study was to examine a test methodology consisting of a full‐scale test and different small scale‐tests for determining the probability of spalling and the amount of spalling of fire exposed concrete structures. A reference specimen was defined as a one‐sided fire exposed slab with the dimensions 1800 × 1200 mm² giving an exposed area of 1500 × 1200 mm². A number of concrete qualities with different probabilities for spalling, were tested using the reference specimen. These tests showed that the reference specimens worked well giving the expected test results. Small specimens were manufactured in different shapes with the same concrete as the one used in the reference tests. These small specimens were tested either at the same time as the reference specimens in the large furnace or afterwards on a small‐scale furnace where the fire exposed surface was 450 × 360 mm². The test results clearly show the increased probability and the increased amount of spalling by using external compressive loading. The results also show that by using pre‐stress through bars or wires the load can be lost due to heating of the bars/wires which results in a decreased amount of spalling. The boundary of the specimen also affects the amount of spalling. The spalling around the edges was in all tests less than the spalling on the central parts of the exposed area. It could also be noted that the spalling did not pass completely through any of the specimens. The reason for this is probably that the water/vapour could migrate out from the unexposed surface of the specimen. Copyright © 2006 John Wiley & Sons, Ltd.     

Detection of failure sites by focused ion beam and nano-probing in the interconnect of three-dimensional stacked circuit structures

Focused ion beam (FIB) and nano-probing were applied for failure analysis of three-dimensional stacked circuits with copper through-silicon-vias between the stacked chips. The failure analysis was done after high temperature storage and thermal cycling tests. Passive voltage contrast in FIB allowed to pinpoint the open sites. FIB cross-sections showed the presence of opens at the bottom of the copper vias. The failure cause was suspected to be an interlayer particle, which was confirmed by optical profilometry. Nano-probing was used on another sample to pinpoint the failure location through the measurement of the local resistance within the daisy chains. The failure was traced out to be related with surface contamination.     

大型电除尘器的设计、安装及操作要点

探讨了硫酸生产用大型电除尘器的要求、设计参数的选择及结构设计.指出要重视大型电除尘器的设计、制造和安装质量,并精心操作和维护,以实现长周期稳定运行.生产实践表明,只有在各个环节都做到精益求精,才能使国产大型电除尘器的质量和性能尽快达到当今世界先进水平.     

La doping effects on intergrowth Bi2WO6–Bi3TiNbO9 ferroelectrics

La doping effects on intergrowth Bi₂WO₆–Bi₃TiNbO₉ ferroelectric ceramics were studied by X-ray diffraction, electron probe microanalysis and dielectric spectroscopy. It was found that the La³⁺ distribution, ferroelectric phase transition and dielectric relaxation behavior are apparently affected by La doping. With increasing La³⁺ content, the site of dopant ion varies, the grain growth of Bi₅TiNbWO₁₅ is restrained, the Curie temperature is reduced and broadened. Furthermore, two dielectric relaxation loss peaks were observed both in temperature and frequency spectra. The calculated relaxation parameters revealed the oxygen vacancy related to the relaxation process.     

Biaxiale Ermüdung reibrührgeschweißter Strukturelemente

Biaxial fatigue of friction stir welded stiffened panels Within the framework of the European WelAir project, cruciform specimens made from stiffening FSW overlap joints were fatigued in the DLR biaxial test rig. To resemble the loading situation of pressurized fuselage structures, proportional loading without any phase shift, but with different load ratios λ between the loading components in both directions was applied.Natural crack initiation and subsequent crack growth were governed by the stiffness gradient caused by introducing the stringer. Cracks initiated and propagated at run‐in and run‐out locations in a direction perpendicular to the weld seam. The shortest fatigue life was observed for uniaxial loading in welding direction (λ = 0). An additional stress component perpendicular to the joint line (λ > 0) resulted in a higher number of cycles to failure. Similar to single stringer panels, increasing the load ratio also increased the number of cycles to failure for FSW clip‐stringer structural members, but additionally gives a different location of the fatal crack.     

三相异步电动机运行指标的分析

利用电机学理论分析了影响电机起动转矩、起动电流、最大转矩和最小转矩的因素。     

The flame retardant mechanism of polyolefins modified with chalk and silicone elastomer

This paper presents the current understanding of the flame retardant mechanism of Casico?. The study includes the flame retardant effect of each individual component: ethylene–acrylate copolymer, chalk and silicone elastomer, as well as the formation of an intumescent structure during heating. The flame retardant properties were investigated by cone calorimetry and oxygen index tests. To obtain insight into the flame retardant mechanism, heat treatment under different conditions has also been performed. The results indicate that the flame retardant mechanism of Casico is complex and is related to a number of reactions, e.g. ester pyrolysis of acrylate groups, formation of carbon dioxide by reaction between carboxylic acid and chalk, ionomer formation and formation of an intumescent structure stabilized by a protecting char. Special emphasis is given to the formation of the intumescent structure and its molecular structure as evaluated from ¹³C MAS‐NMR and ²⁹Si MAS‐NMR, ESCA and XRD analysis. After treatment at 500°C the intumescent structure consists mainly of silicon oxides and calcium carbonate and after treatment at 1000°C the intumescent structure consists of calcium silicate, calcium oxide and calcium hydroxide. Copyright © 2003 John Wiley & Sons, Ltd.     

Associative properties of perfluorooctyl end‐functionalized polystyrene–poly(ethylene oxide) diblock copolymers

The synthesis of 2,2,3,3‐tetrahydro‐perfluoroundecanoyl end‐functionalized polystyrene–poly(ethylene oxide) block (PS‐block‐PEO‐R_F) copolymers and their matching PS‐block‐PEO diblock copolymers was carried out by sequential anionic polymerization. Viscometry and ¹⁹F NMR studies show that the PS‐block‐PEO copolymers, in contrast to their matching PS‐block‐PEO‐R_F copolymers, exhibit a micellar rather than the associative behavior seen for the latter. However, the presence of an excess of fluorinated acid, used for end‐functionalization, produces a reduction of the associative behavior above the overlap concentration, with the fluorinated acid acting like a surfactant. A competition may also occur between PS—and R_F—mediated micellization. Copyright © 2004 Society of Chemical Industry     

Methacryloxyethyl phosphate‐grafted expanded polytetrafluoroethylene membranes for biomedical applications

Expanded polytetrafluoroethylene (ePTFE) membranes were modified by graft copolymerization with methacryloxyethyl phosphate (MOEP) in methanol and 2‐butanone (methyl ethyl ketone (MEK)) at ambient temperature using gamma irradiation. The effect of dose rate (0.46 and 4.6 kGy h^?1), monomer concentration (1–40 %) and solvent were studied and the modified membranes were characterized by weight increase, X‐ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). XPS was used to determine the % degree of surface coverage using the C? F (ePTFE membrane) and the C? C (MOEP graft copolymer) peaks. Grafting yield, as well as surface coverage, were found to increase with increasing monomer concentration and were significantly higher for samples grafted in MEK than in methanol solution. SEM images showed distinctly different surface morphologies for the membranes grafted in methanol (smooth) and MEK (globular), hence indicating phase separation of the homopolymer in MEK. We propose that in our system, the non‐solvent properties of MEK for the homopolymer play a more important role than solvent chain transfer reactions in determining grafting outcomes. Copyright © 2005 Society of Chemical Industry