Change of the amorphous state by heat treatment below the glass transition temperature

This study was undertaken to elucidate the state of a polymer in the amorphous state through a change of motion of the molecular chain caused by heat treatment below the glass transition temperature. From dielectric measurements of amorphous poly(ethylene terephthalate) heat-treated below T_g, it was found that the average relaxation time, the distribution of relaxation time and the dielectric strength increase with increase of heat treatment. From these results, it was concluded that the amorphous state becomes more random by heat treatment.     

Compressibility of the polymer crystal

Results for the compressibilities of a wide range of polymer crystals along the fibre- and the transverse crystal axes are presented. Good agreement is found between the theoretical and the experimental results of different authors.     

Water electrolysis under microgravity: Part 1. Experimental technique

Water electrolysis was conducted in both alkaline (25 wt.% KOH, 2 wt.% KOH) and acid (0.1N H₂SO₄) solutions for 8 s under microgravity environment realized in a drop shaft. The gas bubble formation of hydrogen and oxygen on platinum electrodes was observed by CCD camera. In alkaline solutions, a bubble froth layer grew on the electrode surface. Hydrogen bubble size was smaller than that of oxygen. The current density at constant potential decreased continually with time. In spite of the growth of a bubble froth layer on the electrode, the electrolysis never stopped, apparently because fresh electrolyte is supplied to the electrode surface by microconvection induced by the gas bubble evolution. In acid solution, hydrogen gas bubbles frequently coalesced on the cathode surface, yielding a larger average bubble than that of oxygen. The current density did not vary at constant potentials from –0.4 to −0.8 V versus reversible hydrogen electrode (RHE), because the effective electrode surface area was significantly reduced by the larger bubble size compared to alkaline electrolyte. The present experiments indicate that, especially in a microgravity environment, the bubble evolution behavior and the resultant current–potential curves are significantly influenced by the wettability of the electrode in contact with the electrolyte.     

The effect of sputter etching on the surface characteristics of dyed aramid fabrics

Three kinds of aramid fabrics, Technora (modified p-aramid), Conex (m-aramid) and Kevlar (p-aramid), were subjected to sputter etching and argon low-temperature plasma treatments after dyeing in black with disperse dyes. The depth of shade increased considerably on Technora and Kevlar with the sputter etching treatment, but not on Conex fabrics. Argon low-temperature plasma treatment had virtually no effect on the depth of shade on the aramid fabrics.     

One-Step Synthesis of Luminescent Nanoparticles of Complex Oxide, Strontium Aluminate

An organic aqueous solution of metal acetylacetonate precursors was subjected to spray pyrolysis in order to fabricate SrAl₂O₄:Eu (SAO) nanoparticles. Non-agglomerated luminescent SAO nanoparticles, having a spherical shape with a size of 10–30 nm, were achieved in a single step, while only submicrometer-sized SAO particles were obtained from the conventional ultrasonic pyrolysis of the metal nitrates. Without any post-annealing process, the as-prepared SAO nanoparticles were observed to exhibit a strong photoluminescence, which is comparable with that of the submicrometer-sized SAO particles. A mechanism for the formation of the nanoparticles is also discussed.     

Electrochemical formation of Sm-Co alloys by codeposition of Sm and Co in a molten LiCl-KCl-SmCl3-CoCl2 system

Electrocodeposition of Sm and Co on a Cu substrate was investigated in a molten LiCl-KCl-SmCl₃ (0.5 mol.%)-CoCl₂ (0.1 mol.%) system at 723 K. Phase of the deposited Sm-Co alloys could be controlled by electrolysis potential. SmCo₃ was formed on a Cu substrate by potentiostatic electrolysis in the potential range of 0.20-0.90 V (vs. Li⁺/Li). Sm₂Co₁₇ was obtained in the potential range of 0.90-1.50 V.     

Anisotropic Thermal Expansion of β-Ca2SiO4 Monoclinic Crystal

Crystals of β-Ca₂SiO₄ (space group P 12₁/ n 1) were examined by high-temperature powder X-ray diffractometry to determine the change in unit-cell dimensions with temperature up to 645°C. The temperature dependence of the principal expansion coefficients (α_i) found from the matrix algebra analysis was as follows: α₁= 20.492 × 10⁻⁶+ 16.490 × 10⁻⁹ ( T - 25)°C⁻¹, α₂= 7.494 × 10⁻⁶+ 5.168 × 10⁻⁹( T - 25)°C⁻¹, α₃=−0.842 × 10⁻⁶− 1.497 × 10⁻⁹( T - 25)°C⁻¹. The expansion coefficient α₁, nearly along [302] was approximately 3 times α₂ along the b -axis. Very small contraction (α₃) occurred nearly along [     01]. The volume changes upon martensitic transformations of β↔α_L' were very small, and the strain accommodation would be almost complete. This is consistent with the thermoelasticity.     

Anatase-Type TiO2 and ZrO2-Doped TiO2 Directly Formed from Titanium(III) Sulfate Solution by Thermal Hydrolysis: Effect of the Presence of Ammonium Peroxodisulfate on their Formation and Properties

Anatase-type TiO₂ powder containing sulfur with absorption in the visible region was directly formed as particles with crystallite in the range 15–88 nm by thermal hydrolysis of titanium(III) sulfate (Ti₂(SO₄)₃) solution at 100°–240°C. Because of the presence of ammonium peroxodisulfate ((NH₄)₂S₂O₈), the yield of anatase-type TiO₂ from Ti₂(SO₄)₃ solution was accelerated, and anatase with fine crystallite was formed. Anatase-type TiO₂ doped with ZrO₂ up to 9.8 mol% was directly precipitated as nanometer-sized particles from the acidic precursor solutions of Ti₂(SO₄)₃ and zirconium sulfate in the presence and the absence of (NH₄)₂S₂O₈ by simultaneous hydrolysis under hydrothermal conditions at 200°C. By doping ZrO₂ into TiO₂ and with increasing ZrO₂ content, the crystallite size of anatase was decreased, and the anatase-to-rutile phase transformation was retarded as much as 200°C. The anatase-type structure of ZrO₂-doped TiO₂ was maintained after heating at 1000°C for 1 h. The favorable effect of doping ZrO₂ to anatase-type TiO₂ on the photocatalytic activity was observed.     

A new refining process for iron oxide using iron ore and its application to hard ferrites

Kawasaki Steel Corporation and Kawatetsu Mining Co., Ltd. have developed a new refining process to extract iron oxide from iron ore to meet the increase in demand for iron oxide for high- grade hard ferrites. This article discusses the quality of iron oxides and the characteristics of the hard ferrite magnets produced from them.