Fabrication of Functionally Graded SiO2‐Mo Material by Centrifugation and Floc‐Casting of Highly Concentrated Slurry

To fabricate functionally graded materials, a highly concentrated slurry of SiO₂‐Mo system was prepared and centrifugal force was applied in an attempt to achieve a graded composition. Subsequently, we formed a homogeneous green body with compositional gradation by floc‐casting at 80°C, which was then fired at 1750°C for 10 min in Ar. The sintered body had compositional ratios of SiO₂ and Mo as well as electrical conductivities that changed gradually along the direction of centrifugal force. The results demonstrate that centrifugation and control of slurry characteristics such as flocculation are effective in fabricating functionally graded SiO₂‐Mo materials.     

Self‐Expansion Behavior of Silk Fibroin Film

Summary: Silk fibroin cast film was prepared using a ternary solvent system of CaCl₂/CH₃CH₂OH/H₂O (1/2/8 in mole ratio). A drying temperature at casting influenced crystal structure of fibroin. When a drying temperature was set lower than 9 °C, the cast film became amorphous. When a drying temperature was set higher than 40 °C, a fibroin film of silk‐II structure was obtained. In order to produce a fibroin film of silk‐I structure, a preferable temperature range was from 20 to 26 °C. The crystal transformation from random coil structure into silk‐I could be made through exposure of an amorphous film to water vapor. As for the crystal transformation from silk‐I into silk‐II, the treatment with a glycerin solution was effective. In the course of the treatment a film showed self‐thinning and self‐expanding. The expansion ratio exceeded 40% at maximum. The film produced accompanying self‐expansion was ductile in nature.

The apparent self‐expansion percentage as a function of initial thickness of the film. The ductility of the film was classified into four stages from the observation of recovery behavior after folding: ?, very soft; ?, soft; ?, middle; ?, hard (see Figure 5 ).     

High temperature catalytic combustion of methane and propane over hexaaluminate catalysts: NOx emission characteristics

Several hexaaluminate-related materials were prepared via hydrolysis of alkoxide and powder mixing method for high temperature combustion of CH₄ and C₃H₈, in order to investigate the effect of the concentration of the fuels, O₂ and H₂O on NO_x emission and combustion characteristics. Among the hexaaluminate catalysts, Sr_0.8La_0.2MnAl₁₁O₁₉₋ prepared by the alkoxide method exhibited the highest activity for methane combustion and low NO_x emission capability. NO_x emission at 1500 °C was increased linearly with O₂ concentration, whereas water vapor addition decreased NO_x emission in CH₄ combustion over the Sr_0.8La_0.2MnAl₁₁O₁₉₋ catalyst. In the catalytic combustion of C₃H₈ over the Sr_0.8La_0.2MnAl₁₁O₁₉₋ catalyst, the amount of NO_x emitted was raised in the temperature range between 1000 and 1500 °C when the C₃H₈ concentration increased from 1 to 2 vol.%. It was found that NO_x emission in this temperature range was reduced effectively by adding water vapor.     

Fish intake and serum levels of organochlorines among Japanese women

This study evaluates background serum levels of selected organochlorine compounds among Japanese women of reproductive age and investigates whether lifestyle factors, especially dietary factors, may be associated with these levels. A cross-sectional study was performed on 80 Japanese women, aged 26-43 years, who complained of infertility and were confirmed not to have endometriosis. The serum levels of total toxic equivalency (TEQ), 18 polychlorinated dibenzo-p-dioxins (PCDDs)/polychlorinated dibenzofurans (PCDFs), 4 coplanar polychlorinated biphenyls (cPCBs), 36 ortho-substituted polychlorinated biphenyls (PCBs), and 13 chlorinated pesticides or their metabolites were measured and data were collected on the women's age, residence, occupation, body mass index (BMI), smoking and alcohol habit and 6 dietary intakes (fish, meats, rice, vegetables, fruits and dairy products). The serum median level of total TEQ was 25.1 pg TEQ/g lipid, that of PCDDs/PCDFs/cPCBs was 11.5 pmol/g lipid, that of PCBs was 0.46 nmol/g lipid, and that of total pesticides was 1.32 nmol/g lipid. The serum levels of total TEQ, PCDDs/PCDFs/cPCBs, PCBs and pesticides were positively associated with age (P for trend=0.003, 0.01, 0.005 and 0.01, respectively) and frequent fish consumption (P for trend=0.002, 0.003, 0.0003 and 0.006, respectively). Other lifestyle factors were not associated with serum organochlorine levels. The present study suggests that Japanese women who consume fish frequently in their reproductive period tend to accumulate organochlorines in their bodies.     

Imaging of optical disc using reflection-mode scattering-type scanning near-field optical microscopy

A phase-change optical disc was observed using a reflection-mode scattering-type scanning near-field optical microscope (RS-SNOM). In an a.c.-mode SNOM image, the 1.2 microm x 0.6 microm recording marks were successfully observed although the data were recorded on the groove. In contrast, no recording marks could be resolved in a d.c.-mode SNOM image. These results are in good agreement with those from a numerical simulation using the finite difference time domain method. The resolution was better than 100 nm with a.c.-mode SNOM operation and the results indicate that recording marks in phase-change optical media can be directly observed with the RS-SNOM.     

Short-term irradiation behavior of minor actinide doped uranium plutonium mixed oxide fuels irradiated in an experimental fast reactor

A fuel irradiation program is being conducted using the experimental fast reactor ‘Joyo’. Two short-term irradiation tests in the program were completed in 2006 using a uranium and plutonium mixed oxide fuel which contains minor actinides (MA-MOX fuel). The objective of the tests is the investigation of early thermal behavior of MA-MOX fuel such as fuel restructuring and redistribution of minor actinides. Three fuel pins which contained MA-MOX: 2% neptunium and 2% americium doped uranium plutonium mixed oxide (Am,Pu,Np,U)O_2−x fuel were supplied for testing. The first test was conducted with high-linear heating rate of approximately 430 W cm⁻¹ for only 10 min. After the first test, one fuel pin was removed for examinations. Then the second test was conducted with the remaining two pins at nearly the same linear power for 24 h. In these tests, two oxygen-to-metal molar ratios were used for fuel pellets as a test parameter. Non-destructive and destructive post-irradiation examinations results are discussed with early on the behavior of the fuel during irradiation.     

Gene Expression over Time during Cell Transformation Due to Non-Genotoxic Carcinogen Treatment of Bhas 42 Cells

The Bhas 42 cell transformation assay (Bhas 42 CTA) is the first Organization for Economic Cooperation and Development (OECD)-certificated method used as a specific tool for the detection of the cell-transformation potential of tumor-promoting compounds, including non-genotoxic carcinogens (NGTxCs), as separate from genotoxic carcinogens. This assay offers the great advantage of enabling the phenotypic detection of oncotransformation. A key benefit of using the Bhas 42 CTA in the study of the cell-transformation mechanisms of tumor-promoting compounds, including non-genotoxic carcinogens, is that the cell-transformation potential of the chemical can be detected directly without treatment with a tumor-initiating compound since Bhas 42 cell line was established by transfecting the v-Ha-ras gene into a mouse fibroblast cloned cell line. Here, we analyzed the gene expression over time, using DNA microarrays, in Bhas 42 cells treated with the tumor-promoting compound 12-O-tetradecanoylphorbol-13-acetate (TPA), and NGTxC, with a total of three repeat experiments. This is the first paper to report on gene expression over time during the process of cell transformation with only a tumor-promoting compound. Pathways that were activated or inactivated during the process of cell transformation in the Bhas 42 cells treated with TPA were related not only directly to RAS but also to various pathways in the hallmarks of cancer.     

Determination of dissolved natural thorium and uranium in Horonobe and Mizunami Underground Research Laboratory groundwater and its thermodynamic analysis

At two underground research laboratories situated at Horonobe and Mizunami, Japan, trace amounts of natural thorium and uranium dissolved in deep groundwater were investigated with the help of chemical pre-concentration method. The groundwater was sampled from underground boreholes under the geochemical condition of no atmospheric exposure, and the colloid contribution was checked by in situ two size-fractionated ultrafiltration systems. A rough decrease by half in the concentration after in situ filtration suggested the presence of natural colloids and suspended matter that were carriers of a portion of the elements. The Th and U concentrations in groundwater after 10 kDa filtration was evaluated as dissolved species, and was identified thermodynamically using existing hydrogeological and geochemical data, such as the mineral components in the groundwater at a given pH, ionic strength, concentration of co-existing ions, redox potential, and a hypothetical solubility-limiting solid phase. The crystalline solid phase of tetravalent thorium and uranium dioxides made the solubility very low compared with that of the amorphous phase.     

Experiments and simulations of uniaxial ratchetting deformation of Sn–3Ag–0.5Cu and Sn–37Pb solder alloys

This paper discusses uniaxial ratchetting deformation of lead-free solder alloy Sn–3Ag–0.5Cu and lead-containing solder alloy Sn–37Pb, which were subjected to tension–compression loading with several stress amplitudes and stress ratios, minimum stress over maximum stress. First the uniaxial ratchetting tests were conducted with three maximum stresses and four stress ratios. All tests were conducted using cylindrical bulk specimens of the solder alloys at 313 K. The test results show that there are differences in the ratchetting deformation behavior of the two solder alloys; the larger ratchetting strain occurs in the lead-containing solder alloy than in the lead-free solder alloy. The ratchetting deformation was simulated by the dislocation based constitutive model proposed by Estrin et al. (J Eng Mater Technol 118:441, 1996). The evolution equation of the back stress employed in the constitutive model was modified considering a dynamic recovery term. The effect of the modification of the back stress evolution is discussed by comparing the simulations with the corresponding experimental results. The simulations suggest that the recovery term in the kinematic hardening rule plays an important role in fitting the simulation to the experimental results of the ratchetting deformation of the solder alloys.     

Acute illness induces the release of aversive odor cues from adult, but not prepubertal, male rats and suppresses social investigation by conspecifics.

The present study examined odorant communication during acute illness provoked by injection of lipopolysaccharide (LPS; 100 μg/kg) and how these effects vary between prepubertal and adult conspecifics. Exposure to odor of LPS-treated adult male rats produced increased avoidance in both sexes of adults and prepubertal male partners. This response was not found when they were exposed to odor of LPS-treated prepubertal males. Even a 2.5-fold higher load of LPS in prepubertal males failed to produce aversive odor cues, suggesting that the difference in the odor is not a simple issue of dose/body volume. Both estradiol benzoate (20 μg/kg) and testosterone propionate (500 μg/kg), but not dihydrotestosterone (500 μg/kg) pretreatment in prepubertal males administered LPS restored the expression of aversive odor. These hormone treatments per se did not influence odor properties of prepubertal males, indicating that estrogen receptors may play a key regulatory role in the expression of aversive odor in LPS-treated prepubertal rats. These data suggest that the expression of sickness-related odor emerges through puberty, and likely involves a complex interaction between inflammation and sex steroids across development. (PsycINFO Database Record (c) 2010 APA, all rights reserved)