Ring hydrogenation of naphthalene and 1-naphthol over supported metal catalysts in supercritical carbon dioxide solvent

Catalytic ring hydrogenations of naphthalene and 1-naphthol were studied over several supported metal catalysts in supercritical carbon dioxide solvent at low temperature. Higher concentration of hydrogen in supercritical carbon dioxide and lower reaction temperature were responsible for higher catalyst activity and selectivities to the desired partial ring hydrogenated products as compared with those observed in organic solvent for the same catalyst.     

Functional metal-porphyrazine derivatives and their polymers, 10. Secondary fuel cells based on oxygen reduction on platinum electrode modified by polymers and metal-phthalocyanines

Secondary fuel cells based on oxygen reduction of platinum electrode modified by polymers and metal-phthalocyanine (Mt = Fe(III), Co(II), Ni(II), and Cu(II)) were studied. The discharge curves for the platinum electrode modified by poly(2-vinylpyridine) (or polystyrene) and Co-phthalocyanine in 30% KOH aqueous solution, for a 30 min charge at 500 μA, followed by a 100 μA discharge showed a stable plateau at about ?0.24 V SCE (Saturated Calomel Electrode). The open circuit voltage (vs. Zn) of the cell was 1.2 V, and the discharge capacity was of 46 A · h/kg. For this battery there was no significant decay in its characteristics after more than 30 charge-discharge cycles. In Mt-phthalocyanines, the values decreased in the order of Co(II) > Fe(III) > > Cu(II) > Ni(II). From a cyclic voltammogram for the electrode modified by the polymer and Co-Pc, the cathodic reactions were discussed.     

Vinyl polymerization by metal complexes. XVIII. Kinetics of the polymerization of acrylonitrile initiated by imidazole-copper-(II) complexes

A study on the kinetics and mechanism of the polymerization of acrylonitrile initiated by imidazole and 2-substituted imidazole-copper-(II) complexes was made in dimethyl sulfoxide solution at 40–70°C. The rate of polymerization, Rp, could be expressed as follows: The overall activation energies of these polymerization processes are in a range from 14.2 to 69.1 KJ mole^-1. From the data of electronic spectra and electron paramagnetic resonance, it was confirmed that the polymerization in question could be initiated by free radicals which were formed by the reduction of copper-(II) complex to copper-(I) complex, and the latter formed a new complex with polyacrylonitrile resulted.     

Abnormal metabolism of polyunsaturated fatty acids and phospholipids in diabetic glomeruli

Studies were done on changes in phospholipid content and fatty acid composition of phospholipids and on the role of the acylation pathway in synthesis of phospholipids in the development of abnormal fatty acid composition in the glomeruli of rats 2 and 10 mo after induction of diabetes with streptozotocin. The proportions of individual phospholipids in the glomeruli of rats were not changed 2 mo after induction of diabetes, but the proportion of phosphatidylethanolamine (PE) decreased and that of sphingomyelin increased 10 mo after induction of diabetes. In contrast, in liver the proportion of PE was increased and that of phosphatidylcholine was decreased. These results showed that changes of individual phospholipids in glomeruli were time-dependent and tissue-specific. Two mo after induction of diabetes, the main change in the phospholipid fatty acid composition of diabetic glomeruli was a decrease in arachidonic acid (AA); the main change in serum free fatty acids (FFA) was an increase in linoleic acid (LA) and a decrease in AA. Ten mo after induction of diabetes, the main changes in the phospholipid fatty acid composition of glomeruli were an increase in LA and a decrease in AA; the main change of the serum FFA composition was a decrease in AA. Thus, the fatty acid composition of glomerular phospholipids was not directly correlated to that of the serum in diabetic rats. Acyl-CoA synthetase and acyltransferase activities increased in diabetic glomeruli with either AA or LA as substrate, but activity toward LA increased more at 2 mo after induction of diabetes. Acyl-CoA synthetase activity increased in diabetic glomeruli with LA as substrate, but that did not change with AA as substrate at 10 mo after induction of diabetes. Furthermore, acyltransferase activity decreased in diabetic glomeruli with AA as substrate, although that did not change with LA as substrate at 10 mo after induction of diabetes.     

Melt‐spinning process of a tetrafluoroethylene– hexafluoropropylene copolymer

An industrial melt‐spinning process of tetrafluoroethylene– hexafluoropropylene copolymer (FEP) using an extruder was studied. The novel “spinneret,” having both a large‐diameter spinning nozzle and a high‐temperature vessel, was used to solve the problem of filament breakage on the spinning line caused by high melting viscosity of FEP. The extruder, with its long feed zone, was newly designed to function with a geared pump. The strength of fibers increased with drawing of as‐spun fiber. FEP fibers up to six denier were continuously produced through long‐run production. According to this new process, FEP fibers can be supplied for textile or industrial application. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 84: 2366–2371, 2002     

One-Step Synthesis of Luminescent Nanoparticles of Complex Oxide, Strontium Aluminate

An organic aqueous solution of metal acetylacetonate precursors was subjected to spray pyrolysis in order to fabricate SrAl₂O₄:Eu (SAO) nanoparticles. Non-agglomerated luminescent SAO nanoparticles, having a spherical shape with a size of 10–30 nm, were achieved in a single step, while only submicrometer-sized SAO particles were obtained from the conventional ultrasonic pyrolysis of the metal nitrates. Without any post-annealing process, the as-prepared SAO nanoparticles were observed to exhibit a strong photoluminescence, which is comparable with that of the submicrometer-sized SAO particles. A mechanism for the formation of the nanoparticles is also discussed.     

Role of electron-phonon interaction in lattice dynamics and superconductivity of oxide spinel LiTi2O4

The lattice dynamics of an oxide spinel LiTi₂O₄ is studied by taking account of the electron-phonon (EP) interaction derived on the basis of the realistic tight-binding bands fitted to the first-principles bands. Due to the characteristic dependences of the EP interaction on wavevectors and vibrational modes, a remarkable frequency renormalization of the O vibrational modes, which hybridize with the Ti vibrational modes, is obtained over a wide region of the Brillouin zone. The overall features of the calculated phonon density of states are in agreement with those observed by the inelastic neutron scattering measurements. By using the EP interaction and the renormalized phonon frequencies we have calculated the EP spectral function ² F(). The superconducting transition temperature, gap function, and tunneling spectra are calculated by solving the Éliashberg equation. The results agree well with the observations.     

Correction to: Development of a behavioral trajectory measurement system (Bucket-ANTAM) for organisms moving in a two-dimensional plane

Artificial Life and Robotics -     

REVISE: A Tool for Measuring and Mitigating Bias in Visual Datasets

International Journal of Computer Vision - Machine learning models are known to perpetuate and even amplify the biases present in the data. However, these data biases frequently do not become...