Radon and radon progeny are present indoors, in houses and others dwellings, representing the most important contribution to dose from natural sources of radiation. Most studies have demonstrated an increased risk of lung cancer at high concentration of radon for both smokers and nonsmokers. The work presents a comparative analysis of the radon exposure data in the two radon-prone areas, ?tei, Transylvania, (Romania), in the near of old Romanian uranium mines and in the granitic area of Torrelodones town, Sierra de Guadarrama (Spain). Measurements of indoor radon were performed in 280 dwellings (Romania) and 91 dwellings (Spain) by using nuclear track detectors, CR 39. The highest value measured in ?tei area was 2650 Bq m^− 3 and 366 Bq m^− 3 in the Spanish region. The results are computed with the BEIR VI report estimates using the age-duration model at an exposure rate below 2650 Bq m^− 3. We used the EC Radon Software to calculate the lifetime lung cancer death risks for individuals groups in function of attained age, radon exposures and tobacco consumption. A total of 233 lung cancer deaths were observed in the ?tei area for a period of 13 years (1994-2006), which is 116.82% higher than expected from the national statistics. In addition, the number of deaths estimated for the year 2005 is 28, which is worth more than 2.21 times the amount expected by authorities. In comparison, for Torrelodones was rated a number of 276 deaths caused by lung cancer for a period of 13 years, which is 2.09 times higher than the number expected by authorities. For the year 2005 in the Spanish region were reported 32 deaths caused by pulmonary cancer, the number of deaths exceeding seen again with a factor of 2.10 statistical expectations. This represents a significantly evidence that elevated risk can strongly be associated with cumulated radon exposure.     

Steam oxidation of ytterbium disilicate environmental barrier coatings with and without a silicon bond coat

The current generation of multilayer Si/Yb₂Si₂O₇ environmental barrier coatings (EBCs) are temperature limited by the melting point of Si, 1414°C. To investigate higher temperature EBCs, the cyclic steam oxidation of EBCs comprised of a single layer of ytterbium disilicate (YbDS) was compared to multilayered Si/YbDS EBCs, both deposited on SiC substrates using atmospheric plasma spray. After 500 1-h cycles at 1300°C in 90 vol%H₂O-10 vol%air with a gas velocity of 1.5 cm/s, both multilayer Si/YbDS and single layer YbDS grew thinner silica scales than bare SiC, with the single layer YbDS forming the thinnest scale. Both coatings remained fully adherent and showed no signs of delamination. Silica scales formed on the single layer coating were significantly more homogeneous and possessed a markedly lower degree of cracking compared to the multilayered EBC. The single layer EBC also was exposed at 1425°C in steam with a gas velocity of 14 cm/s in an alumina reaction tube. The EBC reduced specimen mass loss compared to bare SiC but formed an extensive 2nd phase aluminosilicate reaction product. A similar reaction product was observed to form on some regions of the bare SiC specimen and appeared to partially inhibit silica volatilization. The 1425°C steam exposures were repeated with a SiC reaction tube and no 2nd phase reaction product was observed to form on the single layer EBC or bare SiC.     

MicroRNAs and Extracellular Vesicles as Distinctive Biomarkers of Precocious and Advanced Stages of Breast Cancer Brain Metastases Development

Triple negative breast cancer presents higher mortality and poorer survival rates than other breast cancer (BC) types, due to the proneness to brain metastases formation, which are usually diagnosed at advanced stages. Therefore, the discovery of BC brain metastases (BCBM) biomarkers appears pivotal for a timely intervention. With this work, we aimed to disclose microRNAs (miRNAs) and extracellular vesicles (EVs) in the circulation as biomarkers of BCBM formation. Using a BCBM animal model, we analyzed EVs in plasma by nanoparticle tracking analysis and ascertained their blood-brain barrier (BBB) origin by flow cytometry. We further evaluated circulating miRNAs by RT-qPCR and their brain expression by in situ hybridization. In parallel, a cellular model of BCBM formation, combining triple negative BC cells and BBB endothelial cells, was used to differentiate the origin of biomarkers. Established metastases were associated with an increased content of circulating EVs, particularly of BBB origin. Interestingly, deregulated miRNAs in the circulation were observed prior to BCBM detection, and their brain origin was suggested by matching alterations in brain parenchyma. In vitro studies indicated that miR-194-5p and miR-205-5p are expressed and released by BC cells, endothelial cells and during their interaction. These results highlight miRNAs and EVs as biomarkers of BCBM in early and advanced stages, respectively.     

The transformation of formaldehyde on CoZSM-5 zeolites

The interaction of formaldehyde molecules with Co²⁺ ions in CoZSM-5 zeolites of various compositions containing various proportions between Co²⁺ in exchange positions and in oxide-like clusters, as well as the transformation of formaldehyde sorbed in zeolites was followed by IR spectroscopy. The interaction of formaldehyde with Co²⁺ resulted in a weakening of CO bond, what can be partially due to π-back donation of d electrons of Co²⁺ to π^* antibonding orbitals of formaldehyde. Only Co²⁺ in exchange positions (contrary to Co²⁺ in oxide-like clusters) were able to interact with formaldehyde. IR studies illustrated also that formaldehyde molecules are oxidized to formate ions, by either Co³⁺ or Co²⁺ as oxidants. According to IR results Co³⁺ and Co²⁺ are reduced mostly to Co⁺ and metallic Co.     

Influence of Incubation Time on Ortho-Toluidine Blue Mediated Antimicrobial Photodynamic Therapy Directed against Selected Candida Strains—An In Vitro Study

(1) Background and the aim: The appropriate incubation time in the antimicrobial photodynamic therapy protocol seems to have a huge impact on the efficacy of this process. This is particularly important in relation to Candida strains, due to the size of these cells and the presence of the cell wall. The aims of this study were to determine the optimal incubation time needed for the absorption of toluidine blue by cells of C. albicans, C. glabrata, C. krusei and C. parapsilosis using direct observation by optical microscopy, and to evaluate the efficacy of TBO-mediated aPDT on planktonic cells of these strains. (2) Methods: The microscopic evaluation consisted of taking a series of images at a magnification of 600× and counting the % of stained cells. The in vitro effect of TBO-mediated aPDT combined with a diode laser (635 nm, 400mW, 12 J/cm², CW) on the viability of yeast cells with different incubation times was evaluated. (3) Results: The presence of TBO within the cytoplasm was observed in all tested Candida strains and at all microscopic evaluation times. However, the highest percentages of cells were stained at 7 and 10 min. The highest % reduction of CFU/mL after TBO-mediated aPDT against Candida was obtained for the strain C. albicans ATCC 10,231 and it was 78.55%. (4) Conclusions: TBO-mediated aPDT against Candida was effective in reducing the number of CFU/mL at all assessed incubation times. However, the most efficient period for almost all strains was 7–10 min.     

Anticorrosive polyurethane paints with nano- and microsized phosphates

Two types of phosphate fillers (nanosized aluminum phosphate and microsized aluminum–zinc phosphate) were tested as anticorrosive fillers in 2 K solvent-borne polyurethane paints based on commercial acrylic resin with OH groups and an isophorone diisocyanate-type hardener. Three coating compositions containing commercial fillers (mica/quartz, TiO₂, wollastonite, talc) and also mentioned nanosized aluminum phosphate or microsized aluminum–zinc phosphate were prepared using a pearl-mill as well as a laboratory dissolver, applied onto a steel substrate and cured at room temperature for 14 days. An influence of the type and content of a phosphate filler on properties of polyurethane paints and coatings has been investigated. Incorporation of nanosized aluminum phosphate into coating compositions increases their viscosity while cured paints exhibit reduced adhesion to steel substrates. The results of corrosion tests in a salts spray chamber as well as immersion in an aqueous NaCl solution indicated that the paint system with 9.8 wt.% of applied nanofiller had similar protective properties to a polyurethane coat containing a higher dose (i.e. 15.6 wt.%) of commercial microsized aluminum–zinc phosphate.     

The effect of the surface nanostructure and composition on the antiwear properties of zirconia–titania coatings

This study describes the preparation, surface imaging and tribological properties of titania coatings modified by zirconia nanoparticles agglomerated in the form of island-like structures on the titania surface. Titania coatings and titania coatings with embedded zirconia nanoparticles were prepared by the sol–gel spin coating process on silicon wafers. After deposition the coatings were heat-treated at 500 °C or 1000 °C. The natural tendency of nanoparticles to form agglomerates was used to build separated island-like structures unevenly distributed over the titania surface having the size of 1.0–1.2 μm. Surface characterization of coatings before and after frictional tests was performed by atomic force microscopy (AFM) and optical microscopy. Zirconia nanoparticles were imaged with the use of transmission electron microscopy (TEM). The tribological properties were evaluated with the use of microtribometer operating in ambient air at technical dry friction conditions under normal load of 80 mN. It was found that nanocomposite coatings exhibit lower coefficient of friction (CoF) and considerably lower wear compared to titania coating without nanoparticles. The lowering of CoF is about 40% for coatings heated at 500 °C and 33% for the coatings heated at 1000 °C. For nanocomposites the wear stability was enhanced by a factor of 100 as compared to pure titania coatings. We claim that enhanced tribological properties are closely related to the reduction of the real contact area, lowering of the adhesive forces in frictional contacts and increasing of the composite hardness. The changes in materials composition in frictional contact has secondary effect.     

Different Metabolism and Toxicity of TRANS Fatty Acids,Elaidate and Vaccenate Compared to Cis-Oleate in HepG2 Cells

Trans fatty acids (TFAs) are not synthesized in the human body but are generally ingested in substantial amounts. The widespread view that TFAs, particularly those of industrial origin, are unhealthy and contribute to obesity, cardiovascular diseases and diabetes is based mostly on in vivo studies, and the underlying molecular mechanisms remain to be elucidated. Here, we used a hepatoma model of palmitate-induced lipotoxicity to compare the metabolism and effects of the representative industrial and ruminant TFAs, elaidate and vaccenate, respectively, with those of cis-oleate. Cellular FAs, triacylglycerols, diacylglycerols and ceramides were quantitated using chromatography, markers of stress and apoptosis were assessed at mRNA and protein levels, ultrastructural changes were examined by electron microscopy and viability was evaluated by MTT assay. While TFAs were just slightly more damaging than oleate when applied alone, they were remarkably less protective against palmitate toxicity in cotreatments. These differences correlated with their diverse incorporation into the accumulating diacylglycerols and ceramides. Our results provide in vitro evidence for the unfavorable metabolic features and potent stress-inducing character of TFAs in comparison with oleate. These findings strengthen the reasoning against dietary trans fat intake, and they can also help us better understand the molecular mechanisms of lipotoxicity.