水溶性氨基丙烯酸漆的研制

研制了高温烘烤 (145～ 15 0℃ )和中温烘烤 (12 0～ 12 5℃ )两种水溶性氨基丙烯酸漆。当羟基树脂的玻璃化温度为 - 5～ 0℃ ,丙烯酸和丙烯酸羟乙酯占总单体的质量分数分别为 7 5 %～ 8 5 %和 8 0 %～ 12 0 % ,羟基树脂和氨基树脂的质量比为 (0 0 5∶1 0 0 )～ (0 10∶1 0 0 ) ,颜基质量比为 0 2 9∶1 0 0时 ,两种漆的附着力达到 1级 ,抗冲击强度 >490N·cm ,柔软性 <1mm ,硬度 >2H ,光泽度 >80 (45℃ ) ,耐水 (2 0～ 2 5℃ ) 1d以上 ,遮盖力及施工性能良好     

纸制备SiC/Si层状陶瓷复合材料的微观结构和性能

本文以纸为原料,通过叠层设计、低温碳化和高温渗硅制备了具有层状结构特征的SiC/Si陶瓷复合材料。并采用XRD、SEM和三点弯曲等分析测试手段对其相组成、微观结构和力学性能进行了分析。结果表明:纸碳化后为非晶形的碳;渗硅后试样的相组成为β-SiC相、自由Si相和残C相。叠层纸碳化后的微观结构为含有大量扁长空洞的碳骨架,渗硅后得到的SiC陶瓷复合材料具有明显的层状结构特征。三点弯曲实验表明,SiC/Si陶瓷复合材料的强度高达290MPa,达到了常规反应烧结SiC陶瓷的强度水平;且其断裂方式为非灾难性断裂,分析认为这与材料的层状结构形貌有关。     

环境因子对破乳优势菌生长的影响

从油田油泥中富集、培养筛选出两株具有破乳活性的优势菌，并对影响破乳菌生长的主要环境因素进行了试验研究。试验表明：这两株破乳优势菌的最佳生长周期为60～72h，最佳温度为30℃左右，最佳pH值为6-8之间。     

Properties of modified polyacrylonitrile membranes prepared by copolymerization with hydrophilic monomers for water–ethanol mixture separation

A new kind of terpolymer membrane was employed to separate a permselective water–alcohol mixture. This membrane was prepared via the copolymerization of acrylonitrile, sodium salt styrene sulfonic acid (SStSA), and hydroxyethyl methacrylate in dimethylsulfoxide with azobisisobutyronitrile as an initiator. The reaction mechanism, resultant structure, and polymer composition were confirmed by IR and elemental analysis. The effects of the feed composition on the polymer composition, mechanical properties, thermal properties, and degree of swelling were investigated. It was found that water permeated through the membrane preferentially in a water/alcohol system. The flux increased with the increase of SStSA, but the separation factor decreased drastically with higher SStSA. For a 50 wt % water–ethanol mixture, a flux of 0.65 kg/m² h and a separation factor of 212 were obtained at 30°C when the membrane containing the highest SStSA content was used. The capacities of the metal ions absorbed by the membranes were investigated in the study. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 90: 244–250, 2003     

天然橡胶不同硫化体系磨耗微观结构的研究

通过对天然橡胶不同硫化体系硫化胶磨耗前后的红外光谱分析，得知常温下硫化胶的磨耗历程是具有氧化反应的力化学反应，单，双硫键较多的硫化胶具有较好的耐磨性。     

Mathematical model of shear rate of polymer melt dynamic extruding through capillary

With superimposing a sine vibration of displacement on the extruding direction of a polymer melt, the characterization formula of the shear rate of a polymer melt within a capillary was set up. By making use of the experimental equipment of a constant velocity type dynamic rheometer of capillary (CVDRC) designed by the authors, the calculating steps of the shear rate of the polymer melt at the wall of the capillary under a vibration force field were established. Through measuring and analyzing the instantaneous data of capillary entry pressure, capillary volume rate, and their phase‐difference under the superimposed vibration, the polymer melt's shear rate at the wall of the capillary can thus be calculated. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 95: 1056–1061, 2005     

全水发泡硬质聚氨酯泡沫塑料技术研究进展

对CFC 11发泡替代技术中全水发泡技术路线进行了分析 ,指出水作为发泡剂存在的优点与不足。着重阐述了全水发泡中几种主要因素如水的用量、聚醚多元醇性质和结构以及异氰酸酯指数对泡沫性能的影响 ,并对国外近些年来全水发泡用聚醚多元醇研究现状进行了详细论述     

The Torque Transmission Capabilities of the Adhesively-Bonded Tubular Single Lap Joint and the Double Lap Joint

With the wide application of fiber-reinforced composite materials in aircraft, space structures and robot arms, the design and manufacture of composite joints have become a very important research area because they are often the weakest areas in composite structures.

In this paper, the stress and torque transmission capabilities of the adhesively-bonded tubular single lap joint and the double lap joint were experimentally tested. In order to compare the experimental results with the calculated results, the stress and torque transmission capabilities were analyzed by the 3-dimensional finite element method taking into consideration the nonlinear properties of the adhesive.

From the experiments it was found that the torque transmission capabilities of the adhesively-bonded double lap joint was 2.7 times as large as that of the single lap joint. Also, it was found that the fatigue limit of the double lap joint was 16 times as large as that of the single lap joint.     

UHMWPE改性PP共混物的力学性能

研究了UHMWPE型号及UHMWPE的用量对PP材料力学性能的影响。结果表明:在PPH/PPR/PPB为60/20/20时分别加入UHMWPE2401和UHMWPE2402,可起到增强增韧的效果,在开炼机上制试样UHMWPE2402的效果要好于UHMWPE2401,注射制样为UHMWPE2401好于UHMWPE2402;随UHMWPE含量的增加,PPH/PPR/PPB共混物的缺口冲击强度大体呈直线上升趋势,在UHMWPE2401为20份时,达到29 4kJ/m2。     

Preparation and the properties of PMR‐type polyimide composites with aluminum nitride

A new polyimide composite was developed relying on the concept of in situ polymerization of monomer reactants polyimide. High thermal conductive, low dielectric constant and dielectric loss, and thermal‐stable composites were successfully demonstrated by incorporating aluminum nitride powder into the polyimide. The weight percent of aluminum nitride was up to 80%. The thermal and dielectric properties follow the classic composite theories. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 89: 3913–3917, 2003