Preparation of ZrC/SiC porous self-supporting monoliths via sol-gel process using polyethylene glycol as phase separation inducer

We present a straightforward method via sol-gel process using polyethylene glycol (PEG) as phase separation inducer to prepare zirconium carbide/silicon carbide (ZrC/SiC) porous monoliths. Organic/inorganic hybrid gels are prepared using zirconium oxychloride, furfuryl alcohol, and tetraethyl orthosilicate as major starting materials. In the presence of PEG, crack-free hybrid monoliths are obtained by drying the wet gels under ambient pressure, whereas in the absence of PEG, the wet gels break into pieces as expected. PEG plays a key role in maintaining the macroscopic shape of the monoliths. After ceramization at 1300–1500?°C, ZrC/SiC porous monoliths are obtained. SEM and mercury intrusion porosimetry data show that PEG also has strong influence on the microstructures of the monoliths. The compressive strengths of the ceramic monoliths are in the range of 0.3 to 0.7?MPa. And their compressive behavior starts to differ due to the changes in their microstructures, especially the pore structure.     

Molten salt synthesis of MAX phases in the Ti-Al-C system

The molten salt method was used to synthesise the MAX phase compounds Ti₂AlC and Ti₃AlC₂ from elemental powders. Between 900–1000?°C, Ti₂AlC was formed alongside ancillary phases TiC and TiAl, which decreased in abundance with increasing synthesis temperature. Changing the stoichiometry and increasing the synthesis temperature to 1300?°C resulted in formation of Ti₃AlC₂ alongside Ti₂AlC and TiC. The type of salt flux used had little effect on the product formation. The reaction pathway for Ti₂AlC was determined to be the initial formation of TiC_1-x templating on the graphite and titanium aluminides.     

Preparation of biaxially textured Ce1-x(Y0.2Zr0.8)xOδ buffer layers on RABiTS NiW tapes by chemical solution deposition

Highly (100)-oriented Ce_1-x(Y_0.2Zr_0.8)_xO_δ (CYZO) films were prepared on biaxially textured NiW substrates by a chemical solution deposition approach using metal inorganic salts as starting materials. It has been found that both the preferential orientation and surface roughness of CYZO films decrease gradually with increasing of the doping percentage of Y³⁺ and Zr⁴⁺ ions. The epitaxial growth relationship of (220)_CYZO//(200)_NiW and [00?l]_CYZO//[001]_NiW was demonstrated by XRD texture measurement as well as atomic resolution STEM observation. XRD, Raman and XPS spectra results indicate that Y³⁺ and Zr⁴⁺ ions were indeed introduced into CeO₂ lattice to substitute Ce⁴⁺ ions and form cubic fluorite CYZO solid solution. Moreover, CeO₂ buffer layer can be endowed a strong enough capability to prevent element diffusion through co-doping of yttrium and zirconium, provided that an optimal doping ratio of them is adopted. This will provide a new approach to fabricating strong-barrier single buffer layer for coated conductor.     

Hierarchical micro-nanostructured albite-based glass-ceramic for high dielectric strength insulators

A novel glass-ceramic material based on albite type Na-rich feldspar has been synthesized by conventional ceramic process. High crystallinity, >94%?Vol.% is obtained by fast sintering which allows energy saving processing. Albite is the main crystalline phase and tetragonal SiO₂ is a secondary phase. Electrical properties were examined by complex impedance, DC measurements, and dielectric breakdown test. Dielectric characterization shows a non-Debye type dielectric behavior with low dielectric constant, 4.6 at 1?MHz, low dielectric losses, (～10^?3 at 1?MHz, and a large dielectric strength, ～60?kV/mm), that it is the largest value reported in ceramic insulators. Those dielectric properties are attained by the low glassy phase content in the samples and their unique micro-nanostructure. All these properties make this novel material a very promising candidate in the market of ceramic electrical insulator, highlighting for high-voltage applications.     

Thermo-physical properties of as deposited and aged thermal barrier coatings (TBC) for gas turbines: State-of-the art and advanced TBCs

In the perspective of fuelling the future generations of gas turbines by hydrogen rich syngas, the evaluation of the effect of a higher water vapour content into the flue gases on the TBC used, or potentially usable, is a need. For this purpose YPSZ APS TBC with two different microstructures have been exposed for 500?h at different temperatures in the range 1000?°C–1250?°C either in air and air +20% vol. H₂O. The comparison between the different testing conditions has been performed in terms of sintering kinetics and phase stability, as evaluated by thermal diffusivity measurements and Synchrotron X-Rays diffraction, respectively. Furthermore the characterisation of thermal properties of two innovative TBCs (GZO-YPSZ and YAG) potentially able to withstand the CMAS attack and erosive environments, respectively, has been carried out.No clear evidence of a different behaviour of TBC has been observed, at least in the considered aging time and temperature range.     

High‐performance thermosets with tailored properties derived from methacrylated eugenol and epoxy‐based vinyl ester

A renewable chemical, eugenol, is methacrylated to produce methacrylated eugenol (ME) employing the Steglich esterification reaction without any solvent. The resulting ME is used as a low‐viscosity co‐monomer to replace styrene in a commercial epoxy‐based vinyl ester resin (VE). The volatility and viscosity of ME and styrene are compared. The effect of ME loading and temperature on the viscosity of the VE–ME resin is investigated. Moreover, the thermomechanical properties, curing extent and thermal stability of the fully cured VE–ME thermosets are systematically examined. The results indicate that ME is a monomer with low volatility and low viscosity, and therefore the incorporation of ME monomer in VE resins allows significant reduction of viscosity. Moreover, the viscosity of the VE–ME resin can be tailored by adjusting the ME loadings and processing temperature to meet commercial liquid molding technology requirements. The glass transition temperatures of VE–ME thermosets range from 139 to 199 °C. In addition, more than 95% of the monomer is incorporated and fixed in the crosslinked network structure of VE–ME thermosets. Overall, the developed ME monomer exhibits promising potential for replacing styrene as an effective low‐viscosity co‐monomer. The VE–ME resins show great advantages for use in polymer matrices for high‐performance fiber‐reinforced composites. This work is of great significance to the vinyl ester industry by providing detailed experimental support. © 2018 Society of Chemical Industry     

Zein-based anti-browning cling wraps for fresh-cut apple slices

The usage of cling wraps is emerging as an easy and cost-effective approach to protect fresh-cut fruits and vegetables from dust, whilst improving visual appeal on retail counters. This study focused on developing an alternate, protein-based packaging material as a food grade cling wrap for food packaging applications. Zein-based cling wraps were produced, and their physical and mechanical characteristics were evaluated and compared with conventionally used chitosan biopolymer films and commercial synthetic polymer films. Antioxidant potential of the prepared films was studied, and the effectiveness of the developed films as anti-browning cling wraps was evaluated using studies conducted on fresh-cut apple slices at ambient conditions. Anti-browning effects were in par with polymeric counterparts; however, zein cling wraps could better prevent weight loss in apple slices. Zein-based films can be adopted as biodegradable food grade cling wraps as an alternative to chitosan and synthetic polymeric materials.     

Study on the Height of the Mining-Induced Water-Conducting Fracture Zone Under the Q 2l Loess Cover of the Jurassic Coal Seam in Northern Shaanxi,China

A method to calculate the height of a water-conducting fractured zone (HWCFZ) was developed based on the plate and shell theory, and the development of the HWCFZ in bedrock and Q2l loess strata is discussed in detail. First, the subsidence-deflection curve equation of the overlying stratum is theoretically derived, and then the ultimate deflection and free space height of rock strata are calculated. Moreover, the strata tensile strain is calculated by using integral calculus. In addition, the failure state of the rock is analyzed by comparing the theoretically calculated tensile strain with the experimentally measured yield tensile strain, allowing one to attain the maximum value of HWCFZ. This approach was tested at the Jinjitan coal mine; the theoretically predicted, experimentally measured, and numerically computed maximum HWCFZ values were 189.5, 187.3, and 188.5 m, respectively, demonstrating the accuracy of the proposed method. These results are highly significant for safe and environment-friendly coal mining in northwest Shaanxi, China.