Gravure offset printing of polymer inks for conductors

A gravure offset printing process has been developed for Ag-filled polymer conductor ink. Pad printing and roller type printing have been used. Curing and electrical properties have been studied. A roller type of gravure offset printing has been used to evaluate the printing process and pad printing to print on the non-planar substrates. Based on differential scanning calorimetry (DSC) and resistivity measurements during ink curing, it was found that the ink had an optimum curing temperature of 140 °C. Square resistance of 300 and 150 μm wide lines can be as low as 20 and 28 mΩ/sq., respectively, for 7–8.5 μm thick line. The minimum line width was 70 μm. This minimum line width can be reduced with different ink solvents, but in this case the line thickness suffers and the square resistance increases, respectively.     

Raman investigation of single oxidized carbon nanotubes

The oxidation process of single-walled carbon nanotubes via nitric acid treatment was followed by IR-, UV-Vis-NIR, and single bundle Raman spectroscopy. The introduction of functional, oxygen-containing groups is revealed by an additional absorption band at 1725 cm⁻¹, characteristic of carbonyl stretch vibrations. No significant shift of the optical absorption bands could be detected after oxidation. The combination of atomic force microscopy and confocal scanning resonance-enhanced Raman microscopy was used to investigate thin bundles and, eventually, individual nanotubes in detail. These experiments enabled determination of the dependence of the Raman intensity of the G-line (around 1590 cm⁻¹) on the bundle height for both non-oxidized and oxidized tubes. The Raman cross-section of the oxidized tubes was found to be reduced by a factor of ˜4, compared to the pristine tubes. This observation is ascribed to all tubes within a bundle that are oxidized to the same degree.     

The ELPI Response and Data Reduction II: Properties of Kernels and Data Inversion

The first part of this article reports the analytical form of the Electrical Low Pressure Impactor (ELPI) kernel functions. In this latter part, the numerical quality of ELPI response matrices is studied and an example of an inversion algorithm is given. The ELPI assemblies with and without an electrical filter stage and with smooth or sintered impaction plates are studied and compared with basic impactor kernels and the kernels for the calculation of the aerosol mass distribution. It is shown that the ELPI assembly with the electrical filter stage and smooth impaction plates should be the best choice for the inversion of data if no bounce occurs. The comparison to a mass impactor shows that the devices are on par in data inversion. The inversion ELPI data is studied with a Bayesian algorithm assuming a bimodal lognormal size distribution of the aerosol. The algorithm includes a novel procedure for obtaining an initial guess of the distribution parameters. To our knowledge, it is also the first algorithm to use ELPI current readings as its input. Simulations and diesel emission measurements show that the proposed algorithm is a useful tool in the study of ELPI data.     

Using a Fragment‐Based Approach To Target Protein–Protein Interactions

The ability to identify inhibitors of protein–protein interactions represents a major challenge in modern drug discovery and in the development of tools for chemical biology. In recent years, fragment‐based approaches have emerged as a new methodology in drug discovery; however, few examples of small molecules that are active against chemotherapeutic targets have been published. Herein, we describe the fragment‐based approach of targeting the interaction between the tumour suppressor BRCA2 and the recombination enzyme RAD51; it makes use of a screening pipeline of biophysical techniques that we expect to be more generally applicable to similar targets. Disruption of this interaction in vivo is hypothesised to give rise to cellular hypersensitivity to radiation and genotoxic drugs. We have used protein engineering to create a monomeric form of RAD51 by humanising a thermostable archaeal orthologue, RadA, and used this protein for fragment screening. The initial fragment hits were thoroughly validated biophysically by isothermal titration calorimetry (ITC) and NMR techniques and observed by X‐ray crystallography to bind in a shallow surface pocket that is occupied in the native complex by the side chain of a phenylalanine from the conserved FxxA interaction motif found in BRCA2. This represents the first report of fragments or any small molecule binding at this protein–protein interaction site.     

Phospholipids and Alzheimer’s Disease: Alterations,Mechanisms and Potential Biomarkers

Brain is one of the richest organs in lipid content. Phospholipids (glycerophospholipids and sphingolipids) are important building blocks of cell membranes, which provide an optimal environment for protein interactions, trafficking and function. Because of that, alterations in their cellular levels could lead to different pathogenic processes in the brain, such as in Alzheimer’s disease (AD), the most common type of dementia among older populations. There is increasing evidence that phospholipid changes occur during pathogenic processes in AD. It is known that lipids are tightly connected with metabolism of the Amyloid Precursor Protein (APP), which produces Amyloid-beta peptide (Aβ), the main component of senile plaques, which represent the main pathological hallmark of AD. However, the mechanism(s) of the lipid-effect on Aβ metabolism and AD pathogenesis is still not completely understood. This review summarizes the current knowledge on phospholipid changes occurring during normal aging and discusses phospholipid changes in the human brain associated with different stages of AD, as well changes in the cerebrospinal fluid and blood/plasma, which are interesting potential biomarkers for AD diagnosis and disease monitoring. At the end, we have discussed future perspectives of phospholipid changes as potential biomarkers and as targets for development of novel treatment strategies against AD.     

Synthesis,calcination and characterization of Nanosized ceria powders by self-propagating room temperature method

Nanometric ceria powders with fluorite-type structure were obtained by applying self-propagating room temperature method. The obtained powders were subsequently thermally treated (calcined) at different temperatures for different times. Powder properties such as specific surface area, crystallite size, particle size and lattice parameter have been studied. Roentgen diffraction analysis (XRD), BET and Raman scattering measurements were used to characterize the as-obtained (uncalcined) powder as well as powders calcined at different temperatures.It was found that the average diameter of the as-obtained crystallites is in the range of 3–5 nm whereas the specific surface area is about 70 m²/g. The subsequent, 15 min long, calcination of as-obtained powder at different temperatures gradually increased crystallite size up to ～60 nm and reduced specific surface down to 6 m²/g. Raman spectra of synthesized CeO_2?y depicts a strong red shift of active triply degenerate F_2 g mode as well as additional peak at 600 cm^?1. The frequency of F_2 g mode increased while its line width decreased with an increase in calcination temperature. Such a behavior is considered to be the result of particle size increase and agglomeration during the calcination. After the heat treatment at 800 °C crystallite size reached value larger than 50 nm. Second order Raman mode, which originates from intrinsic oxygen vacancies, disappeared after calcination.     

The Effect of Ozonation on the Size Fractions of Manganese

Manganese is a commonly found substance in groundwater in Finland. As a powerful oxidant, ozone can be used for the oxidizing of manganese even without raising the pH. The SFS (Finnish Standards Association) standard has set the accepted limit for soluble manganese to 0.45 μm. However, some research papers have used the limit of 30 kD (kilodalton) for soluble manganese. This research concentrates on the size fractions of manganese in four samples of untreated groundwater and in four samples of ozonized groundwater when treated with 0.45 μm, 0.20 μm, 100 kD, 30 kD, and 10 kD filters. In all tests, nearly all manganese contained in raw water penetrated all filters. There were slight variations in the flocculation of manganese in ozonized groundwater; nevertheless, hardly any reduction in manganese levels took place beyond 100 kD. After ozonation, there were two water samples which surpassed the manganese limit of 50 μgl^?1 set for domestic water when the filtration was 0.20 μm and another two samples when the filtration was 100 kD.     

The Role of Vitamin A in Retinal Diseases

Vitamin A is an essential fat-soluble vitamin that occurs in various chemical forms. It is essential for several physiological processes. Either hyper- or hypovitaminosis can be harmful. One of the most important vitamin A functions is its involvement in visual phototransduction, where it serves as the crucial part of photopigment, the first molecule in the process of transforming photons of light into electrical signals. In this process, large quantities of vitamin A in the form of 11-cis-retinal are being isomerized to all-trans-retinal and then quickly recycled back to 11-cis-retinal. Complex machinery of transporters and enzymes is involved in this process (i.e., the visual cycle). Any fault in the machinery may not only reduce the efficiency of visual detection but also cause the accumulation of toxic chemicals in the retina. This review provides a comprehensive overview of diseases that are directly or indirectly connected with vitamin A pathways in the retina. It includes the pathophysiological background and clinical presentation of each disease and summarizes the already existing therapeutic and prospective interventions.     

Piloting of anionic polymerization of styrene in tetrahydrofurant

Anionic polymerization of styrene in THF with n‐butyllithium/alpha‐methylstyrene initiator is described as a first step in preparation of a styrenic block copoly‐mer. In order to suppress rapid decay of living alpha‐methylstyrene unimers, which occurred at room temperature, the initiation reaction was carried out at ?20(+5)°C. The kinetic parameters of this decay reaction were determined and used for process optimization. By combining experiments with modelling of styrene propagation reaction all key process parameters were defined for l‐L, 38‐L, and 189‐L reactors. A good match was demonstrated between the model and experimental propagation exotherm for semibatch reaction conditions. Overall, it was demonstrated that technical grade THF and styrene could be used at pilot plant scale to prepare well‐defined polymers up to Mn 22 000 via the “living” polymerization mechanism. The resulting polymers had narrow molecular weight distributions (1.06 < Mw/Mn < 1.30).     

Films from oat spelt arabinoxylan plasticized with glycerol and sorbitol

The development of packaging films based on renewable materials is an important and active area of research today. This is the first extensive study focusing on film‐forming properties of an agrobiomass byproduct, namely, oat spelt arabinoxylan. A plasticizer was needed for cohesive film formation, and glycerol and sorbitol were compared. The tensile properties of the films varied with the type and amount of the polyol. With a 10% (w/w) plasticizer content, the films containing glycerol had higher tensile strength than the films containing sorbitol, but with a 40% plasticizer content, the result was the opposite. Sorbitol‐plasticized films retained their tensile properties better than films with glycerol during 5 months of storage. The films were semicrystalline with similar crystallinity indices of 0.20–0.26. The largest crystallites (9.5 nm) were observed in the film with 40% glycerol. The softening of films with 40% (w/w) glycerol started at a significantly lower relative humidity (RH) than that of the corresponding sorbitol‐containing films. The films with sorbitol also had lower water vapor permeability (WVP) than the films with glycerol. The films plasticized with 10% (w/w) sorbitol had a WVP value of 1.1 g mm/(m²·d·kPa) at the RH gradient of 0/54%. The oxygen permeability of films containing 10% (w/w) glycerol or sorbitol was similar: 3 cm³·μm/(m²·d·kPa) at 50–75% RH. A higher plasticizer content resulted in more permeable films. Permeation of sunflower oil through the films was not detected. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009