Hydroxyapatite/tricalcium silicate composites cement derived from novel two-step sol-gel process with good biocompatibility and applications as bone cement and potential coating materials

Tricalcium silicate (C₃S) and hydroxyapatite (HAp) composites were fabricated through the sol-gel process. The aim of this research is to improve the biocompatibility of C₃S through HAp addition and study the potential of using this as coating materials. The composites (HAp/C₃S) were characterised by Fourier transform infrared spectrometry, thermal gravity-differential thermal analysis and X-ray diffraction. The working and setting times of cement pastes were tested using Gillmore needle. Mechanical properties were examined by nanoindentation and material testing system. In vitro biocompatibility of the materials were studied by cell attachment and viability of L929 and MG-63 cells. HAp/C₃S as a coating material on gelatin film were measured with the surface roughness and imaged by scanning electron microscope. With the addition of HAp, no undesirable free CaO was detected with the synthesis by the sol-gel preparation. The pH values of HAp added groups were between 7.54 and 8.76, which were much lower than pure C₃S group (pH?=?11.75). For in vitro studies, the presence of HAp could effectively enhance the cell attachment and viability of both L929 and MG-63 cells grown in the extract or directly on the composites. However, the mechanical properties of the composites were impaired as compared to pure C₃S. Lastly, HAp/C₃S cement could be evenly coated on gelatin film. HAp is successfully demonstrated to improve C₃S biocompatibility with this new composites HAp/C₃S. C-75 (75% C₃S and 25% HAp), in particular, has good biocompatibility, relatively high compressive strength and can be uniformly coated onto gelatin film. Thus, C-75 is a promising material for further investigation as a coating on other biopolymers.     

Preparation and characterization of mullite whisker reinforced ceramics made from coal fly ash

Ceramics with mullite whiskers were prepared from coal fly ash and Al₂O₃ raw materials, with AlF₃ used as an additive. The phase structures and microstructures of the ceramics were identified via X-ray diffraction and scanning electron microscopy, respectively. The results show that pickling of coal fly ash is an effective method for enhancing the flexural strength of ceramics. Sintering temperature and AlF₃ addition were also key factors influencing the creation of ideal ceramics. The ceramic made from pickled coal fly ash, 6?wt% AlF₃, and sintered at 1200?°C, exhibited the highest flexural strength of 59.1?MPa, and had a bulk density of 1.32?g/cm³ and porosity of 26.8%. The results show that ceramic materials made under these conditions are ideal candidates for manufacturing ceramic proppants for the exploitation of unconventional oil and gas resources.     

The analysis and comparison of two novel kinds of focusing elements as reflectors

In this article, two novel kinds of focusing elements as reflectors are analyzed and compared. One is the grooved Fresnel zone plate reflector with continuous phase‐correcting. The other called subzone paraboloid reflector, has the profile that consists of a series of paraboloids. Their diffraction efficiencies and bandwidths are described. The two elements still preserve the advantages of Fresnel zone plates, namely, low profile, high efficiency, and simple fabrication. Two dual‐reflector antennas using the proposed focusing elements as the main reflectors are simulated and the results show that these antennas have good radiation performances. © 2014 Wiley Periodicals, Inc. Int J RF and Microwave CAE 25:101–108, 2015.     

基于Cortex-M的嵌入式设备固件更新方法研究

本文提出了一种基于分散加载技术实现Boot程序和用户应用程序在同一个工程编写开发的固件更新方法 .通过编写分散加载规范文件在工程中实现代码存储区分区.为了保证固件更新的稳定性和可靠性,在固件下载过程中引入CRC校验、丢包错包重传等容错技术.实验结果 验证了方法的有效性和可靠性.