Salt-assisted solution combustion synthesis of NiFe2O4: Effect of salt type

The effects of three types of salt including NaF, KCl, and NaCl on the properties of NiFe₂O₄ nanoparticles using salt-assisted solution combustion synthesis (SSCS) have been investigated. The synthesized powders were evaluated by SEM, TEM, FTIR, XRD, and VSM analysis. Also, the specific surface area (SSA), as well as size distribution and volume of the porosities of NiFe₂O₄ powders were determined by the BET apparatus. The visual observations showed that the intensity and time of combustion synthesis of nanoparticles have been severely influenced by the type of salt. The highest crystallinity was observed in the synthesized powder using NaCl. The SSA has also been correlated completely to the type of salt. The quantities of SSA was achieved about 91.62, 64.88, and 47.22 m²g^-1 for the powders synthesized by KCl, NaCl, and NaF respectively. Although the magnetic hysteresis loops showed the soft ferromagnetic behavior of the NiFe₂O₄ nanoparticles in all conditions, KCl salt could produce the particles with the least coercivity and remanent magnetization. Based on the present study, the salt type is a key parameter in the SSCS process for the preparation of spinel ferrites. Thermodynamic evaluation also showed that the melting point and heat capacity are important parameters for the proper selection of the salt.     

Mesoporous silica coated gold nanorods: a multifunctional theranostic platform for radiotherapy and X-ray imaging

Journal of Porous Materials - The development of theranostic nanostructures is one of the most advanced branches of pharmaceutical and medical sciences in the world today. Due to the unique...     

Theoretical and experimental analyses of rheological,compatibility and mechanical properties of PVMQ/XNBR-g GMA/XNBR/GO ternary hybrid nanocomposites

Iranian Polymer Journal - Effects of graphene oxide (GO) on various properties of rubber hybrid nanocomposites based on PVMQ/XNBR-g-GMA/XNBR (phenyl-vinyl-methyl-polysiloxane/carboxylated nitrile...     

Effect of Co addition on microstructural and mechanical properties of WC–B4C–SiC composites

In this study, the effect of Co addition on microstructural and mechanical properties of WC-B₄C–SiC composites sintered by spark plasma sintering (SPS) method was investigated. For this purpose, three batches of WC-B₄C–SiC with different contents of Co (10 vol%, 15 vol%, and 20 Vol %) were sintered at 1400 °C. The results of X-ray diffraction (XRD) analysis of the samples indicated the formation of W₂B₅, W₃CoB₃ as well as the remained C phases and unreacted SiC phase. It was observed that by increasing the Co content, the amount of W₂B₅ phase reduces and W₃CoB₃ and C contents increase. Therefore, W₂B₅ peaks were not detected in the sample containing 20vol% Co. Relative density values above 97% were obtained for all the composites. However, a decrease was observed in relative density by increasing the Co content in the composites. The highest flexural strength (510 ± 42 MPa), fracture toughness (10.34 ± 0.82 MPa m^1/2), and hardness (20.63 ± 0.75 GPa) were also obtained for the sample containing 10vol% Co compared to the other samples. In addition, Transgranular fracture of SiC as well as pulling out of W₃CoB₃ and W₂B₅ particles were observed in the fracture surface micrographs of the samples. The presence of micro-cracks in the SiC grains, fracture of W₃CoB₃ grains, and crack deflection was reported as dominant toughening mechanisms.     

Optical properties of multi-stacked BaTiO3/SrTiO3 thin films synthesized via chemical method

In this work, the BaTiO₃ and SrTiO₃ thin films as well as BaTiO₃/SrTiO₃ lamellar composites are synthesized via sol-gel spin-coating method. The formation of corresponding phases from their sols is investigated by virtue of X-ray diffraction on their powders, which confirms the formation of tetragonal structure for BaTiO₃, but cubic structure for SrTiO₃. The field emission scanning electron microscopy images show that crack-free films with different morphologies are formed in each sample. Likewise, by changing periodicity of the samples, the morphology of the composite samples is changed. As the number of layers increases from 1 to 20, the band gap reduces from 4.38 eV to 4.10 eV for BaTiO₃ samples and from 4.13 eV to 3.80 eV for SrTiO₃ samples confirmed by UV–Vis spectra. The band gap of periodicity = 1 sample is higher than that of BaTiO₃, while band gaps of periodicity = 2 and 5 composites mount between those of BaTiO₃ and SrTiO₃. In addition, the refractive indices of multi-stacked composites are about 0.2 lesser than refractive indices of BaTiO₃ sample in high wavelengths. The periodicity dependence of optical frequency dielectric constant, dielectric loss, impedance, Urbach tail, extinction coefficient, and electric modulus of multi-stacked composites are also studied.     

Synthesis,characterization and magnetic properties of polythiophene/SrFe12-x(ZrZn)0.5xO19 nanocomposite as a microwave absorber

Ferrites are an important group of magnetic materials which are used as absorbers. The incorporation of ferrite and conducting polymer achieves great enhancement in microwave absorption properties. The nanocomposites of hexagonal ferrites embedded by conducting polymers such as polypyrrole, polyaniline and polythiophene (PTH) have been paid much attention. In the present study, strontium hexagonal ferrite doped by Zr and Zn with the final formula of SrFe_12-x(ZrZn)_0.5xO19 considering x = 0.9 and embedded by PTH was produced to achieve a nanocomposite with the highest microwave absorbing ability. In this study, after synthesis of SrFe₁₂O₁₉(ZrZn)_0.5xO19 and PTH, the nanocomposite was prepared by in situ polymerization. Wrapping the ferrite particles and PTH chains could form nanocomposite properly, and therefore acceptable interactions were observable between SrFe_12-x(ZrZn)_0.5xO19ferrite particles and PTH polymer chains in the composites. Assessing the X-ray diffraction (XRD) patterns of SrFe_12-x(ZrZn)_0.5xO19, PTH, and PTH/SrFe_12-x(ZrZn)_0.5xO19 nanocomposite indicated that the PTH characteristic peak shifts slightly and its peak intensity reduces, which may be attribute to the coating of PTH polymer chains onto SrFe_12-x(ZrZn)_0.5xO19 particles. We revealed also lower magnetic properties in the obtained nanocomposite. The morphological assessment also suggested that PTH could effectively coat the SrFe_12-x(ZrZn)_0.5xO19 particles. The synergistic effect of SrFe_12-x(ZrZn)_0.5xO19 particle plus PTH leads to microwave absorption percentage higher than 95% by PTH/SrFe_12-x(ZrZn)_0.5xO19 nanocomposite. Overall, nanocomposite creating by coupling interaction between SrFe_12-x(ZrZn)_0.5xO19 particles (x = 0.9) and PTH can effectively lead to achieve the highest rate of absorption of electromagnetic waves.     

Targeted design of polyaniline-graphene oxide,barium-strontium titanate,hard-soft ferrite,and polyester multi-phase nanocomposite for highly efficient microwave absorption

The current paper focuses on synthesizing a high-efficiency microwave absorber via incorporating the nanofillers of graphene oxide-polyaniline (GO-PANI), barium-strontium titanate (BST), and soft-hard ferrite within the polyester matrix. The nanocomposite magnets of (Ba_0.5Sr_0.5Fe₁₂O₁₉)_1-x hard/(CoFe₂O₄)_x soft (x = 0.2, 0.5, and 0.8) were prepared using sol-gel auto-combustion method. The GO-PANI and BST were successfully synthesized by in situ polymerization and improved polymerization, respectively. The phase structure, chemical structure, morphology, and microwave absorption properties of the synthesized nanocomposites were characterized by X-ray diffractometer (XRD), Fourier-transform infrared spectroscopy (FT-IR), and scanning electron microscope (SEM), vector network analyzer (VNA) techniques, respectively. The results showed that the synergistic effects of the combination of dielectric (BST), conductive (GO-PANI), and magnetic materials (hard-soft ferrites) provided the reflection loss values of less than ?20 dB (>99% absorption) in the X-band region. The minimum reflection loss of ?35 dB (>99.99% absorption) was obtained by the optimal formulation including (Ba_0.5Sr_0.5Fe₁₂O₁₉)_0.2 (CoFe₂O₄)_0.8, and the weight ratio of 1: 2 for both BST/soft-hard ferrite and hard-soft ferrite + BST/GO-PANI with the thickness of 1 mm. According to the results, the thickness factor plays a key role in improving the impedance matching. Consequently, the proposed nanocomposite can be employed as a novel kind of microwave absorbers with good impendence matching and high absorption.     

Water-soluble Copolymers of N-vinylpyrrolidone and Vinyl Acetate: Synthesis, Characterization, and Monomer Reactivity at High Conversions

Homogeneous copolymers of N-vinylpyrrolidone (VP) and vinyl acetate (VA) which form clear aqueous solutions were prepared by free radical polymerization in a solution of isopropanol alcohol, using 2,2-azobisisobutyronitrile as an initiator. They were characterized by FTIR, ¹H-NMR, and element analysis studies. The reactivity ratios of the monomer were computed by the Extended Kelen–Tüdós method at high conversions, using data from both ¹H-NMR and elemental analysis studies. The reactivity ratios of VP and VA in a homogenous copolymer were observed to be very different from that of a heterogeneous copolymer. Additional information was obtained by finding out the sequence length distribution for copolymers.     

Mechanistic study of electrochemical oxidation of 4-tert-butylcatechol: A facile electrochemical method for the synthesis of new trimer of 4-tert-butylcatechol

The electrochemical trimerization of 4-tert-butylcatechol via anodic oxidation of 4-tert-butylcatechol (1) is described. The mechanism of trimerization has been studied in aqueous solution using cyclic voltammetry and controlled-potential coulometry. The electrochemical synthesis of trimer 3a has been successfully performed in an undivided cell in good yield and purity.     

Novel Route to Propylene Carbonate: Selective Synthesis from Propylene Glycol and Carbon Dioxide

High surface area zirconium phosphate in an amorphous phase exhibits high activities for water-related reactions such as hydrolysis of ethyl acetate and esterification of acetic acid with ethanol. The zirconium phosphate is insoluble during the reaction, is recoverable by simple filtration, and can be reused at least five times without any treatment.