Brillouin-Scattering Study of the Elastic Constants of ErVO4

The room-temperature elastic constants of ErVO₄ were considerably smaller than those of isostructural silicate and phosphate analogs. The generally "less-rigid" crystalline lattice and weaker metal-oxygen bond-strength in the RVO₄ (R = rare earth elements) phases indicates that these materials are of interest for potential applications as an interphase component in toughened oxide ceramic composites.     

Copolymerizations of macromonomer prepared by addition-fragmentation chain transfer polymerization of methyl acrylate trimer

Summary An oligomer of the methyl acrylate unsaturated trimer bearing 2-carbomethoxy-2-propenyl ω-end group (M _n = 1300, M _w/M _n = 1.7, and functionality > 0.7) was copolymerized as a macromonomer (0.02 mol/L) with styrene (1.0 mol/L) in benzene at 60 °C. The amounts of monomer and macromonomer in the feed simultaneously decreased with increasing time to indicate copolymer formation, and the macromonomer was found to be as reactive as styrene toward poly(styrene) radicals. The M _ns of the copolymers were 13900–22000 depending on conversion. No resonance due to the unsaturated <ω-end group bound to the poly(styrene) chain was detected by ¹H-NMR spectroscopy, indicating that no fragmentation of adduct radical of the end group to expel the poly(methyl acrylate trimer) radical. Polymerization of ethyl methacrylate (1.0 mol/L) in the presence of the macromonomer (0.02 mol/L) resulted in a mixture of the unreacted macromonomer and homopolymer of ethyl methacrylate. No end group bound to the poly(ethyl methacrylate) was detected by ¹H-NMR spectroscopy, excluding the possibility of addition fragmentation chain transfer to the macromonomer to expel an oligomer radical of the methyl acrylate trimer. Addition of the poly(methacrylate) radical to the macromonomer is extremely slow under the present conditions of copolymerization. Received: 27 March 2003/Revised version: 30 April 2003/ Accepted: 30 April 2003 Correspondence to Bunichiro Yamada     

A new concept for determining triglyceride composition of fats and oils by liquid chromatography

The matrix concept was used to characterize the chromatographic rules in the elution of molecular species of triglyceride. To prove the hypothesis experimentally, cacao butter, palm oil, linseed oil, olive oil, rapeseed oil and triglyceride of “Ogonori” (Gracilaria verrucosa) were examined. A matrix model was suggested to help determine the individual molecular species of naturally occurring triglycerides.     

Striped‐pattern deterioration and morphological analysis of injection moldings comprising polypropylene/ethylene α‐olefin rubber blends. I. Influence of ultraviolet irradiation

Unique deterioration with a periodical striped pattern on the injection moldings of polypropylene/rubber blends is reported. After exposure to ultraviolet irradiation with a sunshine fade meter, striped patterns appeared on the injection moldings along the flow direction of the molten resin during the filling process of injection molding, even though the initial specimen showed no sign of any stripe pattern on its surface. The stripe was carefully observed with ultrasonic echo imaging, scanning electron microscopy, transmission electron microscopy, and Fourier transform infrared spectroscopy. As a result, a number of microvoids were observed inside the injected body at a depth of 50–100 μm from the surface. It became clear that the difference in the number of voids along the flow direction formed the stripe pattern. Surprisingly, these voids occurred in domains comprising a rubber phase. The distribution of voids in depth indicated the existence of a trace of a snakelike flow caused inside the injected body during the injection‐molding process. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2007     

Synthesis of Ba2NaNb5O15 Powders and Thin Films Using Metal Alkoxides

Transparent and highly oriented Ba₂NaNb₅O₁₅ (BNN) thin films have been prepared by using metal alkoxides. A homogeneous precursor solution was prepared by the controlled reaction of NaOC₂H₅, Nb(OC₂H₅)₅, and barium metal. The BNN precursor included a molecular-level mixture of NaNb(OC₂H₅)₆ and Ba[Nb(OC₂H₅)₆]₂ in ethanol. The alkoxy-derived powder crystallized to a low-temperature phase, and then transformed to orthorhombic BNN (tungsten bronze) at 600°C. BNN precursor films on substrates crystallized to orthorhombic BNN at 800°C via the low-temperature phase. Highly (002) oriented BNN films of tungsten bronze structure were successfully prepared on MgO (100) substrates at 700°C by using BNN underlayer.     

Hydrophobic effects on protein/nucleic acid interaction: enhancement of substrate binding by mutating tyrosine 45 to tryptophan in ribonuclease Tl

Hydrophobic effects on binding of ribonuclease Tl to guaninebases of several ribonucleotides have been proved by mutatinga hydrophobic residue at the recognition site and by measuringthe effect on binding. Mutation of a hydrophobic surface residueto a more hydrophobic residue (Tyr45 – Trp) enhances thebinding to ribonucleotides, including mononucleotide inhibitorand product, and a synthetic substrate-analog trinudeotide aswell as the binding to dinucleotide substrates and RNA. Enhancementson binding to non-substrate ribonucleotides by the mutationhave been observed with free energy changes ranging from –2.2 to – 3 .9 kJ/mol. These changes are in good agreementwith that of substrate binding, –2.3 kJ/mol, which iscalculated from Michaelis constants obtained from kinetic studies.It is shown, by comparing the observed and calculated changesin binding free energy with differences in the observed transferfree energy changes of the amino acid side chains from organicsolvents to water, that the enhancement observed on guaninebinding comes from the difference in the hydrophobic effectsof the side chains of tyrosine and tryptophan. Furthermore,a linear relationship between nucleolytic activities and hydrophobicityof the residues (Ala, Phe, Tyr, Trp) at position 45 is observed.The mutation could not change substantially the base specificityof RNase Tl, which exhibits a prime requirement for guaninebases of substrates.     

Synthesis and Magneto-mechanical Properties of Ce-TZP/La M-Type Hexaferrite Composite

An in situ composite composed of ceria-stabilized tetragonal zirconia polycrystals (Ce-TZP) and La{Co_0.5Fe_0.5(Fe_0.9Al_0.1)₁₁}O₁₉ was synthesized from a powder mixture of Ce-TZP, La(Fe_0.9Al_0.1)O₃, Fe₂O₃, Al₂O₃, and CoO. The dense Ce-TZP dispersed with platelike La{Co_0.5Fe_0.5(Fe_0.9Al_0.1)₁₁}O₁₉ crystals as a second phase were formed after sintering from 1250° to 1350°C. The saturation magnetization of the in situ composite Ce-TZP/La{Co_0.5Fe_0.5(Fe_0.9Al_0.1)₁₁}O₁₉ was proportional to the mass fraction of the hexaferrite second phase in Ce-TZP. The coercivity of the composite with a 20 mass% of second phase decreased from 9.14 to 2.52 kOe (from 728 to 201 kA/m) after the pulverization of the composite. The susceptibility (χ) increased by 15%–25% under uniaxial stress on the composite. The change of the susceptibility (Δχ/χ) value increased with decreasing the mass fraction of the second phase in the composite. The Δχ was found to increase linearly with applied stress and abruptly change on cracking, which is expected for the application in fracture sensing of the composite.     

Formation, Characterization, and Hot Isostatic Pressing of Cr2O3-Doped ZrO2 (0,3 mol% Y2O3) Prepared by Hydrazine Method

In the ZrO₂-Cr₂O₃ system, metastable t -ZrO₂ solid solutions containing up to 11 mol% Cr₂O₃ crystallize at low temperatures from amorphous materials prepared by the hydrazine method. The lattice parameter c decreases linearly from 0.5149 to 0.5077 nm with increased Cr₂O₃ content, whereas the lattice parameter a is a constant value ( a = 0.5077 nm) regardless of the starting composition. At higher temperatures, transformation (decomposition) of the solid solutions proceeds in the following way: t (ss)→ t (ss) + m + Cr₂O₃→ m + Cr₂O₃. Above 11 mol% Cr₂O₃ addition, c-ZrO₂ phases are formed in the presence of Cr₂O₃. The t -ZrO₂ solid solution powders have been characterized for particle size, shape, and surface area. They consist of very fine particles (15–30 nm) showing thin platelike morphology. Dense ZrO₂(3Y)-Cr₂O₃ composite ceramics (∼99.7% of theoretical) with an average grain size of 0.3 μm have been fabricated by hot isostatic pressing for 2 h at 1400°C and 196 MPa. Their fracture toughness increases with increased Cr₂O₃ content. The highest K _Ic value of 9.5 MPa·;m^1/2 is achieved in the composite ceramics containing 10 mol% Cr₂O₃.     

Anatase-Type TiO2 and ZrO2-Doped TiO2 Directly Formed from Titanium(III) Sulfate Solution by Thermal Hydrolysis: Effect of the Presence of Ammonium Peroxodisulfate on their Formation and Properties

Anatase-type TiO₂ powder containing sulfur with absorption in the visible region was directly formed as particles with crystallite in the range 15–88 nm by thermal hydrolysis of titanium(III) sulfate (Ti₂(SO₄)₃) solution at 100°–240°C. Because of the presence of ammonium peroxodisulfate ((NH₄)₂S₂O₈), the yield of anatase-type TiO₂ from Ti₂(SO₄)₃ solution was accelerated, and anatase with fine crystallite was formed. Anatase-type TiO₂ doped with ZrO₂ up to 9.8 mol% was directly precipitated as nanometer-sized particles from the acidic precursor solutions of Ti₂(SO₄)₃ and zirconium sulfate in the presence and the absence of (NH₄)₂S₂O₈ by simultaneous hydrolysis under hydrothermal conditions at 200°C. By doping ZrO₂ into TiO₂ and with increasing ZrO₂ content, the crystallite size of anatase was decreased, and the anatase-to-rutile phase transformation was retarded as much as 200°C. The anatase-type structure of ZrO₂-doped TiO₂ was maintained after heating at 1000°C for 1 h. The favorable effect of doping ZrO₂ to anatase-type TiO₂ on the photocatalytic activity was observed.     

Design of recursive digital filters for the selection or rejection of a particular velocity in seismic signals

In this paper a new type of velocity-selecting/rejecting filter which passes or stops a particular event in a seismic signal is proposed. The velocity-selecting filter is based on a time-space band-pass filter with sharp passband for a particular direction, and similarly, the velocity-rejecting filter is based on a time-space band-stop filter. A technique for designing such filters, in terms of an infinite-impulse-response (IIR) filter, is presented, in which a rotated version of separable filter is used. Finally, numerical examples are included to illustrate the design theory.