Rheological phase reaction synthesis and electrochemical performance of LiFe2/3Mn1/3PO4/C cathode for lithium-ion batteries

LiFe_2/3Mn_1/3PO₄/C composite was prepared by the rheological phase reaction using LiH₂PO₄, Li₂CO₃, FePO₄, Mn(Ac)₂·4H₂O and ascorbic acid as starting materials. The crystal structure and morphology of as-synthesized sample were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The analysis of XRD results showed that the obtained sample was single-phase with orthorhombic olivine-type structure (Pnma space group). SEM micrographs revealed that the sample was aggregates, with an irregular morphology. The initial discharge capacity was 166.9, 149.1, 139.6, 112.8, 82.93 mAh g^??1 at the rate of 0.1, 0.5, 1, 2, and 10 C, respectively. And when the rate was 0.1, 0.5, 1, 2, and 10 C, the capacity retention was 92.2%, 90%, 92.9%, 97.6%, 91.5% after 50, 100, 200, 200, 500 cycles, respectively.

     

Modernization of Air Supply Unit for Oxidation Towers Used in Bitumen Production

Chemical and Petroleum Engineering - The hydrodynamics of oxidation towers used for bitumen production were studied using a model tower having transparent walls. Experiments were carried out in two...     

Modeling the Destruction of an Anisotropic Composite Barrier in Interaction with Slender Strikers at an Angle

Journal of Engineering Physics and Thermophysics - A numerical investigation has been made into the interaction of slender (5–20 calibers) steel cylinder strikers with orthotropic compost...     

Motion of a Robot Mower with Directional Control

Russian Engineering Research - The stability of robot-mower motion in a specific direction is considered. The direction is regulated by means of an angular sensor and a programmable controller...     

Quantitative Analysis of Valley–Orbit Coupling in Germanium Doped with Group-V Donors

Semiconductors - The wave functions of electrons localized at P, As, and Sb shallow donors in Ge are calculated in the envelope function approximation taking into account valley–orbit...     

Personalized web service recommendation through mishmash technique and deep learning model

Multimedia Tools and Applications - Discovering the relevant web services for specific applications in the dynamically changing business world becomes very critical. Researchers have used many...     

Analyzing the Conditions for the Electrolytic Formation of Ensembles from Metal Nanowires in the Pores of Track Membranes

Theoretical Foundations of Chemical Engineering - The effect of the electrolyte composition, mass-transfer conditions, pore diameter, interpore distance, and electric parameters on the formation of...     

Phase formation,structure and properties of light-weight aluminosilicate proppants based on clay-diabase and clay-granite binary mixes

One of the drawbacks of fusible clays is the narrow sintering interval due to a sharp increase in the amount of iron-silicate melt at a temperature of 1000–1100 °C, which hardens in the form of a glass phase upon cooling. This leads to a relatively low mechanical strength of the calcined samples and causes the danger of melting the granular material surface from such clays during the firing process. To increase the strength of samples of fusible clays, the influence of diabase and granitoid rocks was considered. It was found that the strengthening effect of diabase and granitoid rock additives in an amount of 20–50% in a mixture with fusible clay is due to an increase of total content of the crystalline phase (mullite, cristobalite and residual quartz) from 18–20% in clays without additives to 22–28 % - in mixtures with diabase and to 28–34% - with granitoid additives) at a temperature of 1050–1100 °C. This increase is due to the activation of synthesis processes of secondary mullite and crystallization from alkali-rich feldspar melt of amorphous silica, released from the structure of clay minerals. The established influence of the igneous rocks used made it possible to develop compositions and propose process flow sheet for producing aluminosilicate proppants based on fusible clays. The use of granitoid and diabase rocks in an amount of 20–70% with fusible clays produces lightweight aluminosilicate proppants with bulk density of 1.40–1.46 g/cm³ at temperature range of 1050–1100 °C, which can endure destructive pressures up to 34.5–52 MPa.     

Graphical Methodology to Study the Corona Onset Voltage for Electrostatic Precipitation of Nanoparticles

Theoretical Foundations of Chemical Engineering - The corona onset voltage is an important operating parameter in the electrostatic precipitation of nanoparticulate, however, its experimental...