1/f noise in large-area Hg<Subscript>1−x</Subscript>Cd<Subscript>x</Subscript>Te photodiodes

The 1/f noise in photovoltaic (PV) molecular-beam epitaxy (MBE)-grown Hg_1−xCd_xTe double-layer planar heterostructure (DLPH) large-area detectors is a critical noise component with the potential to limit sensitivity of the cross-track infrared sounder (CrIS) instrument. Therefore, an understanding of the origins and mechanisms of noise currents in these PV detectors is of great importance. Excess low-frequency noise has been measured on a number of 1000-μm-diameter active-area detectors of varying “quality” (i.e., having a wide range of I-V characteristics at 78 K). The 1/f noise was measured as a function of cut-off wavelength under illuminated conditions. For short-wave infrared (SWIR) detectors at 98 K, minimal 1/f noise was measured when the total current was dominated by diffusion with white noise spectral density in the mid-10⁻¹⁵A/Hz^1/2 range. For SWIR detectors dominated by other than diffusion current, the ratio, α, of the noise current in unit bandwidth i_n(f = 1 Hz, V_d = −60 mV, and Δf = 1 Hz) to dark current I_d(V_d = −60 mV) was α_SW-d = i_n/I_d ∼ 1 × 10⁻³. The SWIR detectors measured at 0 mV under illuminated conditions had median α_SW-P = i_n/I_ph ∼ 7 × 10⁻⁶. For mid-wave infrared (MWIR) detectors, α_MW-d = i_n/I_d ∼ 2 × 10⁻⁴, due to tunneling current contributions to the 1/f noise. Measurements on forty-nine 1000-μm-diameter MWIR detectors under illuminated conditions at 98 K and −60 mV bias resulted in α_MW-P = i_n/I_ph = 4.16 ± 1.69 × 10⁻⁶. A significant point to note is that the photo-induced noise spectra are nearly identical at 0 mV and 100 mV reverse bias, with a noise-current-to-photocurrent ratio, α_MW-P, in the mid 10⁻⁶ range. For long-wave infrared (LWIR) detectors measured at 78 K, the ratio, α_LW-d = i_n/I_d ∼ 6 × 10⁻⁶, for the best performers. The majority of the LWIR detectors exhibited α_LW-d on the order of 2 × 10⁻⁵. The photo-induced 1/f noise had α_LW-P = i_n/I_ph ∼ 5 × 10⁻⁶. The value of the noise-current-to-dark-current ratio, α appears to increase with increasing bandgap. It is not clear if this is due to different current mechanisms impacting 1/f noise performance. Measurements on detectors of different bandgaps are needed at temperatures where diffusion current is the dominant current. Excess low-frequency noise measurements made as a function of detector reverse bias indicate 1/f noise may result primarily from the dominant current mechanism at each particular bias. The 1/f noise was not a direct function of the applied bias.     

Effect of Sb implantation on copper silicides formation and morphology after annealing of Cu/Si structures

In this work, the solid state reaction between a thin film of copper and silicon has been studied using Rutherford backscattering spectroscopy, X-ray diffraction, scanning electron microscopy and microprobe analysis. Cu films of 400 and 900 Å thicknesses are thermally evaporated on Si(1 1 1) substrates, part of them had previously been implanted with antimony ions of 5×10¹⁴ or 5×10¹⁵ at. cm⁻² doses. The samples are heat-treated in vacuum at temperatures in the range 200–700 °C for various times. The results show the growth and formation of Cu₃Si and Cu₄Si silicides under crystallites shape dispatched on the sample surface, independently of the implantation dose. On the other hand, it is established that the copper layer is less and less consumed as the antimony dose increases, resulting in the accumulation of Sb⁺ ions at silicide/Si interface and in the silicide layer close to surface. The exposure of samples to air at room temperature shows the stability of Cu₄Si phase whereas the Cu₃Si silicide disappears to the benefit of the silicon dioxide formation. The observed phenomena are discussed.     

Effect of the Distribution of Manganese Ions on the Properties of Mn-Doped (Ba,Y)TiO3 PTCR Ceramics

The electrical properties and microstructure of (Ba,Y)TiO₃ PTCR ceramics were studied. The results indicate that the Mn ions increase the intergranular barrier height and produce a high-resistance layer on the grain surface. The temperature-dependent resistances of the grain bulk, surface layer, and grain boundaries, the temperature coefficient of resistance, and the magnitude of the varistor effect were assessed as a function of Mn content.     

Structural Changes Induced in Nonstoichiometric Titanium Carbide by High-Temperature Deformation

The microstructure evolution in nonstoichiometric titanium carbide is studied during high-temperature deformation at high strain rates and low strains (shock compression) and at slow strain rates and high strains (superplastic regime). The results demonstrate that high-temperature deformation in a broad range of strain rates offers a means of controlling the microstructure of titanium carbide. By varying deformation conditions, one can obtain materials differing in microstructure and chemical composition, in particular, with equilibrium and nonequilibrium microstructures. Accordingly, the physicochemical properties of such materials also differ.     

On the physical and logical topology design of large-scale optical networks

We consider the problem of designing a network of optical cross-connects (OXCs) to provide end-to-end lightpath services to large numbers of label switched routers (LSRs). We present a set of heuristic algorithms to address the combined problem of physical topology design (i.e., determine the number of OXCs required and the fiber links among them) and logical topology design (i.e., determine the routing and wavelength assignment for the lightpaths among the LSRs). Unlike previous studies which were limited to small topologies with a handful of nodes and a few tens of lightpaths, we have applied our algorithms to networks with hundreds or thousands of LSRs and with a number of lightpaths that is an order of magnitude larger than the number of LSRs. In order to characterize the performance of our algorithms, we have developed lower bounds which can be computed efficiently. We present numerical results for up to 1000 LSRs and for a wide range of system parameters such as the number of wavelengths per fiber, the number of transceivers per LSR, and the number of ports per OXC. The results indicate that it is possible to build large-scale optical networks with rich connectivity in a cost-effective manner, using relatively few but properly dimensioned OXCs.     

Effect of anisotropy of tin on thermomechanical behavior of solder joints

Properties of body centered tetragonal tin are highly anisotropic. As a consequence large stresses can develop at the tin grain boundaries due to coefficient of thermal expansion mismatch during temperature excursions. A modeling approach to evaluate the 3D stress states that develop at grain boundaries during thermomechanical fatigue in tin-based solder is presented. Development of significant amounts of stresses in the plane of the grain boundary can cause grain-boundary sliding and surface-relief effects, while those normal to the grain boundary can cause grain-boundary decohesion and cracking.     

Motive Force in a Complex Model of Mass Transfer

Relations for determining a motive force in a complex model of mass transfer as applied to concurrent, countercurrent, and cross motion of the vapor and liquid phases have been introduced. These forces have been compared for different forms of organization of the flow, and their comparison with similar quantities from the known Murphree and Hausen models is presented.     

Experimental characterisation of the drying effect on uniaxial mechanical behaviour of mortar

The main objective of this present study was to evaluate, for a standard mortar, the drying effect on its mechanical behaviour. Numerous uniaxial compression tests were thus performed with loading-unloading cycles. They were carried out on different samples previously preserved under various conditions of conservation: preserved from desiccation, air drying and rapid drying at 60°C. The obtained results showed significant influences of these conditions on the material behaviour (increase in strength, decrease in Young's modulus and Poisson's ratio) and the necessity of taking into account the coupling effects between mechanical—poromechanical behaviours and drying.     

Trajectory control of incompletely restrained parallel-wire-suspended mechanism based on inverse dynamics

This paper discusses parallel wire mechanisms where an end-effector of the mechanism is suspended by multiple wires. The mechanisms enable not only three-dimensional (3-D) positioning but also 3-D orienting of the end-effector, unlike typical wire suspension-type mechanisms such as overhead crane. To discuss the parallel-wire-suspended mechanisms generally, two forms of basic dynamic equations are presented. Then the parallel wire mechanisms are classified into two types based on the basic equations. Dynamical properties of the two types of wire-suspended positioning mechanism are discussed. In this paper, one of the wire-suspended mechanism, incompletely restrained-type parallel wire mechanism, is mainly discussed on its inverse dynamics problem and its trajectory control problem. The inverse dynamics problem for the incompletely restrained-type mechanism plays an important role on its control problem, because the mechanism has low stiffness based on incomplete constraints on the suspended object which is governed by its dynamics. The paper proposes an antisway control method for the suspended object. In the method, the inverse dynamics calculation is used for nonlinear dynamics compensation to control the suspended object of the incompletely restrained parallel wire mechanism.