Crystallographic characteristics and microwave dielectric properties of Ni-modified MgTa2O6 ceramics

Ni²⁺ modified MgTa₂O₆ ceramics with a trirutile phase and space group P4₂/mnm were obtained. The correlations between crystallographic characteristics and microwave dielectric performance of MgTa₂O₆ ceramics were systematically studied based on the chemistry bond theory (PVL theory) for the first time. The results indicate that the introduction of Ni²⁺ causes a change in polarizability and the Mg–O bond ionicity, which contributes to the variation of dielectric constant. Moreover, the lattice energy, and packing fraction, full width at half maximum of the Raman peak of Ta–O bond, as the quantitative characterization of crystallographic parameters, regulate the dielectric loss of MgTa₂O₆ ceramics in GHz frequency band. In addition, the study of sintering behavior shows that the densification and micromorphology are the crucial factors affecting the microwave dielectric performance. Typically, Ni²⁺ doping on the A-site of MgTa₂O₆ can effectively promote the Q × f values to 173,000 GHz (at 7.43 GHz), which ensures its applicability in 5G communication technology.     

Investigation of crystal characteristics,Raman spectra,and microwave dielectric properties of Mg1-xZnxTa2O6 ceramics

Mg_(1-x)Zn_xTa₂O₆ (x = 0.00?0.08) dielectric ceramics were synthesized via the traditional solid-state reaction method. We used XRD and Rietveld refinement to demonstrate that a pure Mg_(1-x)Zn_xTa₂O₆ phase with trirutile structure was formed. Zn²⁺ substitution helped to decrease the Raman full width at half width of the A_1g mode at 703 cm^?1, which resulted in an increase in the order and rigidity of the TaO₆ octahedron, this in turn contributed to improving the Q×f values. Additionally, the introduction of Zn²⁺ significantly promoted grain growth and increased the dense, and the molecular polarizability, these factors lead to a higher permittivity. Moreover, enhanced Ta-O bond energy resulted in a more stable TaO₆ octahedron in the Mg_(1?x)Zn_xTa₂O₆ system, which contributed to enhanced τ_f values via substitution of Zn²⁺ doped on the A-site. Correspondingly, the microwave dielectric properties were significantly improved for 0.04-doped samples, obtaining: ε_r = 27, Q × f = 185,000 GHz (at 7.47 GHz), τ_f =32 ppm/°C.     

Toughness enhancement and equivalent initial fracture toughness of cementitious composite reinforced with aligned steel fibres

Based on theoretical analysis and numerical simulation, the impact of steel fibres on the stress intensity factor (SIF) at the crack tip for cementitious composite was studied. The enhanced toughness of steel fibre reinforced cementitious composite (SFRC) in resisting cracks was explained by the decrement of SIF caused by steel fibre inclusions at the crack tip of the composite. The equivalent initial fracture toughness was used to characterize the crack initiation of SFRC. A simplified method for determining the of SFRC was proposed based on a linear regression method. Fracture tests were conducted on three‐point bending notched beams with different steel fibre volume fractions and specimen sizes to study the crack initiation behaviour of aligned steel fibre reinforced cementitious composite (ASFRC). of ASFRC was calculated, and the size effect of was analysed. The results showed that slightly increased with the steel fibre volume fraction and gradually became stable. For the tested specimens, whose heights varied between 40 and 100 mm, the specimen size had little impact on the .     

PIXE study on recovery of making-technology of Chinese Longquan celadon made in the Southern Song Dynasty (1127–1279 CE)

Proton induced X-ray emission (PIXE) technique and factor analysis were used to study the recovery of making-technology of Chinese Longquan celadon made in the late Southern Song Dynasty (1127–1279 CE). Based on factor analysis, for the raw material for body and the recipe for glaze, there is a close but slightly different relationship between these Longquan celadons unearthed from the core area of Dayao and the non-core area, despite all the Longquan celadons belong to the high-calcium-glaze system. The chemical compositions of most of the tentative body and glaze samples are very close to those of Longquan celadons unearthed from the core area of Dayao and the non-core area. This study can provide a guidance for recovery of making-technology of Longquan celandon.     

A novel bio‐based phthalonitrile resin derived from catechin: synthesis and comparison of curing behavior with petroleum‐based counterpart

The development of bio‐based thermosetting resins with good thermal stability can potentially afford sustainable polymers as replacements for petroleum‐based polymers. We report a practical route to a novel catechin‐based phthalonitrile resin precursor (CA‐Ph), which contains free phenolic hydroxyl groups that result in ‘self‐curing’ at elevated temperatures to afford a thermostable polymer. Comparison of the performance of this CA‐Ph resin with that of a conventional petroleum‐based bisphenol A phthalonitrile resin (BPA‐Ph; containing 5 wt% of the curing agent 4,4′‐diaminodiphenylsulfone) revealed that CA‐Ph exhibits a lower melting point and curing temperature. Cured CA‐Ph resin retains 95% of its weight at 520 °C under a nitrogen atmosphere, which compares favorably with results obtained for BPA‐Ph resin that retains 95% of its weight at a lower temperature of 484 °C. Kinetic results indicated that the curing reactions of both CA‐Ph and BPA‐Ph systems follow an autocatalytic mechanism. These results suggest that catechin is a useful bio‐based feedstock for the preparation of self‐curing and thermally stable phthalonitrile resins for advanced technological applications. © 2017 Society of Chemical Industry     