A novel fabrication route to make macroporous silicon carbide (SiC) has been proposed in this study. The route is composed of the following two steps: the fabrication of porous α‐SiC/novolac‐type phenolic composite using hexamethylenetetramine (HMT) as a curing/blowing agent for the novolac monomer and a conventional reaction‐bonded (RB) sintering of the composite. The α‐SiC/novolac‐type phenolic composite was carbonized at 800°C for 2 h in N2 gas and then reacted with the molten silicon at 1450°C for 30 min under vacuum, resulting in the macroporous RB‐SiC with an open porosity of 48% and relatively large pore size of ~110 μm. The compressive strength of the macroporous RB‐SiC was 113 MPa, which is relatively high compared to those reported for macroporous SiC of equivalent porosities and pore sizes. 相似文献
The tetragonality and carbon distribution in tempered Fe-0.6C-1Mn martensite were investigated by X-ray diffraction and atom probe tomography to elucidate strain relaxation in the tetragonal lattice during tempering and its relationship with the solubility of excess carbon in martensite. Even though tetragonality (c/a) decreased with an increase in the tempering temperature, it persisted at low levels up to 400 °C. Si addition suppressed the decrease in tetragonality at 400 °C by inhibiting recovery in the dislocated matrix. Such persistence implies that dislocation migration is crucial for the complete release of tetragonal lattice strain at such a temperature, in addition to the decrease in the amount of solute carbon in martensite. A low level of tetragonality was observed for martensite containing carbon in the solid solution below the critical value of ~ 0.2 mass pct, at which a bcc structure was predicted. The amount of solute carbon after tempering was linearly correlated with tetragonality in the solute carbon content range of 0.07 to 0.6 mass pct, and the correlation coefficient was similar to those for as-quenched auto-tempered martensite and bainitic ferrite; these results indicate that the amount of excess carbon is simply determined by the amount of tetragonal lattice distortions remaining after carbide precipitation and recovery.
In the present paper, some solid lubricants were tested in backward extrusion friction tests with flat-headed punches using aluminium at room temperature. The results showed that anti-seizure ability was improved when wax was added to the solid lubricant samples. In addition, a water-based graphite lubricant and an ultrahigh molecular weight polyethylene (UHMW-PE) lubricant were tested using aluminium workpieces heated to 500°C. The lubricity of the UHMW-PE lubricant was found to be superior to that of the graphite lubricant. 相似文献
In order to improve LWR source term under severe accident conditions, the first version of a fission product chemistry database named ‘ECUME’ was developed. The ECUME is intended to include several datasets of major chemical reactions and their effective kinetic constants for representative severe accident sequences. It is expected that the ECUME can serve as a fundamental basis from which fission product chemical models can be elaborated for use in the severe accident analysis codes. The implemented chemical reactions in the first version were those for representative gas species in Cs-I-B-Mo-O-H system from 300 to 3000 K. The chemical reaction kinetic constants were evaluated from either literature data or calculated values using ab-initio calculations. The sample chemical reaction calculation using the presently constructed dataset showed meaningful kinetics effects at 1000 K. Comparison of the chemical equilibrium compositions by using the dataset with those by chemical equilibrium calculations has shown rather good consistency for the representative Cs-I-B-Mo-O-H species. From these results, it was concluded that the present dataset should be useful to evaluate fission product chemistry in Cs-I-B-Mo-O-H system under LWR severe accident conditions, where kinetics effects should be considered. 相似文献