Production technology for low-carbon,low-sulfur boron steel

A technology for slag formation in the ladle–furnace unit is considered; the slag is based on the CaO–SiO₂–MgO–Al₂O₃–B₂O₃ system. This technology permits both microalloying of the steel with boron (reduced from the oxide phase) and desulfurization of the steel. The resulting boron content in the steel is 0.001–0.008%; the sulfur content in low-alloy steel and pipe steel is low (0.004–0.010%); and the consumption of manganese ferroalloys is reduced to 0.5 kg/t for 08кп steel and 1.4 kg/t for 09Г2C steel. In addition, the proposed technology increases the strength of the rolled steel, without loss in its plasticity; and reduces the environmental impact thanks to the replacement of fluorspar by colemanite.     

Ga-doped IZO films obtained by magnetron sputtering as transparent conductors for visible and solar applications

C-axis textured thin films of gallium-doped indium zinc oxide (GIZO) with a 2% ratio of Ga/Zn, were obtained via RF-magnetron sputtering with high transparency and electrical conductivity. A Box-Behnken response surface design was used to evaluate the effects of the deposition parameters (In₂O₃ target power, deposition time, and substrate temperature) on the chemical composition, optical, electrical, and structural properties of the GIZO films. The optical constants and the electrical properties were obtained using optical models. The GIZO stoichiometry, and therefore the In/Zn atomic ratio, affected the crystallinity, crystalline parameters, band gap, and charge carrier mobility of the GIZO films. The charge carrier density was related to the change in the crystalline parameters of the hexagonal structure and the In/Zn atomic ratio. The best electrical conductivity values (1.75?×?10³ Ω^?1 cm^?1) were obtained for GIZO films with In/Zn ratio ≥?1. Several figures of merit (FOM) defined for the visible and solar regions were comparatively used to select the optimal In/Zn atomic ratio that provided the best balance between the conductivity and the transparency. The optimal In/Zn ratio was in a range of 0.85–0.90 for the GIZO films.     

A Dual Inhibitor of DYRK1A and GSK3β for β-Cell Proliferation: Aminopyrazine Derivative GNF4877

Loss of β-cell mass and function can lead to insufficient insulin levels and ultimately to hyperglycemia and diabetes mellitus. The mainstream treatment approach involves regulation of insulin levels; however, approaches intended to increase β-cell mass are less developed. Promoting β-cell proliferation with low-molecular-weight inhibitors of dual-specificity tyrosine-regulated kinase 1A (DYRK1A) offers the potential to treat diabetes with oral therapies by restoring β-cell mass, insulin content and glycemic control. GNF4877, a potent dual inhibitor of DYRK1A and glycogen synthase kinase 3β (GSK3β) was previously reported to induce primary human β-cell proliferation in vitro and in vivo. Herein, we describe the lead optimization that lead to the identification of GNF4877 from an aminopyrazine hit identified in a phenotypic high-throughput screening campaign measuring β-cell proliferation.     

Modeling the Motion of a Saw Ginning Machine

The dynamic characteristics of a saw gin as a subsystem with lumped and distributed parameters are considered in the paper. On the basis of investigation of the machine assembly, graphs are drawn that allow establishing the maximum values of the angle of relative rotation and the angle of rotation of the saw cylinder shaft under torsion.     

La0.6Sr0.4Co0.2Fe0.8O3-δ nanofiber cathode for intermediate-temperature solid oxide fuel cells by water-based sol-gel electrospinning: Synthesis and electrochemical behaviour

Water-based sol-gel electrospinning is employed to manufacture perovskite oxide La_0.6Sr_0.4Co_0.2Fe_0.8O_3-δ (LSCF) nanofiber cathodes for intermediate-temperature solid oxide fuel cells. LSCF fibrous scaffolds are synthesized through electrospinning of a sol-gel solution employing water as the only solvent. Morphological characterizations demonstrate that the LSCF fibers have highly crystalline structure with uniform elemental distribution. After heat treatment, the average fiber diameter is 250 nm and the porosity of the nanofiber tissue is 37.5 %. The heat treated LSCF nanofibers are applied directly onto a Ce_0.9Gd_0.1O_1.95 (CGO) electrolyte disk to form a symmetrical cell. Electrochemical characterization is carried out through electrochemical impedance spectroscopy (EIS) in the temperature range 550?°C–950?°C, and reproducibility of the electrochemical performance for a series of cells is demonstrated. At 650?°C, the average measured polarization resistance R_p is 1.0 Ω cm². Measured performance decay is 1 % during the first 33?h of operation at 750?°C, followed by an additional 0.7 % over the subsequent 70?h.