We report two cases of metastatic non-functioning pancreatic endocrine tumour with very elevated plasma levels of alpha-fetoprotein. In these two cases, serial plasma levels of alpha-fetoprotein, initially normal, correlated well with hepatic tumour progression and were associated with fatal outcome. These results suggest that elevated plasma concentration of alpha-fetoprotein may be caused by metastatic pancreatic endocrine tumour and than alpha-fetoprotein serial measurement may be useful in prognostic evaluation.     

Diffusion bonding of an aluminium-lithium alloy (AA8090) using aluminium-copper alloy interlayers

Diffusion bonds have been produced between sheets of an Al-Li-Cu-Mg-Zr alloy using aluminium-4% copper vapour deposited metallic interlayers. Microstructural changes occurred both in the parent alloy and in the bond interface after diffusion bonding cycles and post-bonding heat treatments were analysed. Different metallographic techniques (light microscopy, scanning and transmission electron microscopy) have been used. Diffusion bonding trials were carried out using the same alloy (AA8090), both in non-superplastic (T6) and superplastic conditions. Differences in their behaviours in relation to diffusion bonding were observed.     

The geometric nature of plasticity laws

This paper concerns the plasticity constitutive laws in small strain. In the thermodynamic approach developed here, the key concept is that of internal variables. The differential nature of plasticity law has been pointed out for a long time. If we unite the invariance condition of these laws in a state variable transformation, this involves, ultimately, that the natural mathematic frame of plasticity theory is Differential Geometry. The system state is defined as a point of a differentiable manifold. The state variable are the local coordinates of this point in a chart. The internal stresses are the components of a covariant vector of the cotangent bundle to internal state manifold and the elastic domain is a convex part of cotangent vector space. The plastic yield criteria such as von Mises condition define a Riemannian structure over the manifold. The metric element is identified with the internal dissipation element. Constitutive laws link the covariant derivatives of the thermodynamic stress with the state variable. Hardening modulus splits up in two parts, kinematic hardening and metric hardening. This last is defined by Christoffel connection coefficients. Applied to von Mises isotropic yield condition, the metric hardening is identified with isotropic hardening. The Baltov-Sawczuk model is also analysed. The use of appropriate polar coordinates simplifies significantly the computations. Generalization to a significant category of non-differentiable yield criteria, such as Tresca condition, is considered by introducting a metric tensor family. The adaptation of Drucker's postulate to the proposed model requires the introduction of parallel transport of the internal stress covector. Generally, this transport is different over distinctive paths joining two points. This fact expresses internal state manifold curvature. The Riemann-Christoffel tensor is computed for von Mises, Baltov-Sawczuk and Tresca models.     

On-body propagation velocity estimation using ultra-wideband frequency-domain spatial correlation analyses

On-body communications around the human torso are considered, using ultra-wideband transmissions. The velocity of the diffracted wave propagating around the body is extracted from frequency- domain spatial correlation analyses.     

A method to study the history of a double oxide film defect in liquid aluminum alloys

Entrained double oxide films have been held responsible for reductions in mechanical properties in aluminum casting alloys. However, their behavior in the liquid metal, once formed, has not been studied directly. It has been proposed that the atmosphere entrapped in the double oxide film defect will continue to react with the liquid metal surrounding it, perhaps leading to its elimination as a significant defect. A silicon-nitride rod with a hole in one end was plunged into liquid aluminum to hold a known volume of air in contact with the liquid metal at a constant temperature. The change in the air volume with time was recorded by real-time X-ray radiography to determine the reaction rates of the trapped atmosphere with the liquid aluminum, creating a model for the behavior of an entrained double oxide film defect. The results from this experiment showed that first oxygen, and then nitrogen, was consumed by the aluminum alloy, to form aluminum oxide and aluminum nitride, respectively. The effect of adding different elements to the liquid aluminum and the effect of different hydrogen contents were also studied. This article is based on a presentation made in the John Campbell Symposium on Shape Casting, held during the TMS Annual Meeting, February 13–17, 2005, in San Francisco, CA.     

Characterization of an ASIC for CPG sensors with grid-only depth of interaction sensing

A new version of the front-end application specific integrated circuit (ASIC) for co-planar-grid (CPG) sensors is presented. Compared to the first version, the ASIC is optimized for signal/noise performance, modified in peaking time, and it implements timing signals to measure the depth of interaction using the grids signals only. Experimental results using state-of the-art CPG sensors and different approaches for reducing the error due to electron trapping are reported. A new technique that makes use of the sum and difference of the grids signals is also presented.     

Detection of failure sites by focused ion beam and nano-probing in the interconnect of three-dimensional stacked circuit structures

Focused ion beam (FIB) and nano-probing were applied for failure analysis of three-dimensional stacked circuits with copper through-silicon-vias between the stacked chips. The failure analysis was done after high temperature storage and thermal cycling tests. Passive voltage contrast in FIB allowed to pinpoint the open sites. FIB cross-sections showed the presence of opens at the bottom of the copper vias. The failure cause was suspected to be an interlayer particle, which was confirmed by optical profilometry. Nano-probing was used on another sample to pinpoint the failure location through the measurement of the local resistance within the daisy chains. The failure was traced out to be related with surface contamination.     

Shape-Controlled Synthesis and Upconversion Luminescence of Y2O3:Yb, Er Microstructures

The Y2O3: Yb3 , Er3 microstructures were fabricated by a hydrothermal method without surfactants.The microstructures structure was characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM,KYKY 1000B).The up-conversion luminescence spectra were studied under 978 nm laser diode excitation.In Yb3 and Er3 codoped Y2 O3 microcrystals, the relative intensity of green emission became stronger as the morphology of sample changed from wires to films.