高炉炉渣流动性的实验研究

以宝钢高炉渣中的四大组元(CaO,SiO2,Al2O3,MgO)为基础,实验研究MgO,Al2O3含量及碱度对炉渣的熔化性温度和流动性的影响.结果表明,炉渣中Al2O3含量控制在16%,配制适量的MgO(9%～10%),在1 500℃以上的高温区域,炉渣仍能保持正常的流动性,适合炉缸温度充沛的高炉使用;MgO含量由6%增加到10%时,较明显地降低了炉渣粘度,粘度的递减值约为0.07～0.15 Pa.s.     

西北江三角洲来水来沙的非线性分形特征

根据西、北江干流高要、石角及西北江三角洲网河区顶点马口、三水四个水文站的流量和含沙量资料 ,应用非线性分形原理的R S方法 ,计算西北江干流及西北江网河区顶点四个水文站的流量、含沙量的赫斯特数H和分形维数D ;探讨西、北江干流来水来沙的分形特征及西北江三角洲的分水分沙规律。结果表明 ,流量的分维数略大于含沙量的分维数 ,三水站流量及含沙量的分维数与其上游的石角站流量、含沙量的分维数相差较大 ,与思贤的分水分沙造成西北江的水沙交换有关     

Effect of specimen size and loading conditions on spalling of concrete

Different qualities of concrete have been fire tested using different geometries of the specimens as well as different load levels and load configurations. The main objective with the study was to examine a test methodology consisting of a full‐scale test and different small scale‐tests for determining the probability of spalling and the amount of spalling of fire exposed concrete structures. A reference specimen was defined as a one‐sided fire exposed slab with the dimensions 1800 × 1200 mm² giving an exposed area of 1500 × 1200 mm². A number of concrete qualities with different probabilities for spalling, were tested using the reference specimen. These tests showed that the reference specimens worked well giving the expected test results. Small specimens were manufactured in different shapes with the same concrete as the one used in the reference tests. These small specimens were tested either at the same time as the reference specimens in the large furnace or afterwards on a small‐scale furnace where the fire exposed surface was 450 × 360 mm². The test results clearly show the increased probability and the increased amount of spalling by using external compressive loading. The results also show that by using pre‐stress through bars or wires the load can be lost due to heating of the bars/wires which results in a decreased amount of spalling. The boundary of the specimen also affects the amount of spalling. The spalling around the edges was in all tests less than the spalling on the central parts of the exposed area. It could also be noted that the spalling did not pass completely through any of the specimens. The reason for this is probably that the water/vapour could migrate out from the unexposed surface of the specimen. Copyright © 2006 John Wiley & Sons, Ltd.     

激光结晶a-Si:H SOI离子注入和快速退火

本文对激光结晶a-Si∶H SOI结构砷注入和快速退火行为作了研究.a-Si∶H激光结晶有Lp-LCR,OD,FCR-2,FCR-1四个结晶区.用剖面电镜观察了结晶区的结构.扩展电阻测量表明Lp-LCR区中有两种扩散机制,即杂质在晶粒体内扩散和沿缺陷扩散.OD区中有三种扩散形式,除有上述两种以外,还有沿缺陷的扩散.首次比较了沿晶界和缺陷的扩散速度.     

Biaxiale Ermüdung reibrührgeschweißter Strukturelemente

Biaxial fatigue of friction stir welded stiffened panels Within the framework of the European WelAir project, cruciform specimens made from stiffening FSW overlap joints were fatigued in the DLR biaxial test rig. To resemble the loading situation of pressurized fuselage structures, proportional loading without any phase shift, but with different load ratios λ between the loading components in both directions was applied.Natural crack initiation and subsequent crack growth were governed by the stiffness gradient caused by introducing the stringer. Cracks initiated and propagated at run‐in and run‐out locations in a direction perpendicular to the weld seam. The shortest fatigue life was observed for uniaxial loading in welding direction (λ = 0). An additional stress component perpendicular to the joint line (λ > 0) resulted in a higher number of cycles to failure. Similar to single stringer panels, increasing the load ratio also increased the number of cycles to failure for FSW clip‐stringer structural members, but additionally gives a different location of the fatal crack.     

ESR Refining Potential for Titanium Alloys using a CaF2‐based Active Slag

Since the end of the Cold War and due to the needs to produce titanium more cost‐efficient and thus more attractive for its civilian use, the electroslag remelting (ESR) process has become an increasingly important topic of international research programmes, because titanium and titanium aluminides can be chemically refined by ESR in some degree. Using ESR, titanium turnings from machining steps and scrap from foundries can be remelted, refined and provided as secondary titanium for the market at relatively favourable prices. This article investigates the removability of the main impurities out of titanium and titanium‐aluminium alloys by electroslag remelting using the active slag system CaF₂‐Ca‐(CaO). Thermochemical and kinetic aspects of the ESR process are considered.