SiCP增强泡沫铝基复合材料制备工艺及润湿性研究

对采用熔体发泡法直接制备碳化硅颗粒增强泡沫铝基复合材料进行了探索，讨论了制备过程中SiCp与铝液间的润湿性、发泡工艺参数与温度控制等对制备工艺的影喻。表明该工艺简单，易于操作，不需任何增粘措施，处理后的SiCp浸润性好且分布均匀，孔洞分布均匀。     

钇对Ti-43Al-9V合金组织性能的影响

采用OM，XRD，SEM和TEM等测试方法，分析了稀土元素(Y)对Ti—43Al—9V合金显微组织以及力学形能的影响。实验结果表明，Ti—43Al—9V—0．3Y合金由γ相、α2相、B2相和YAl2相组成；添加稀土可以细化Ti—43Al—9V合金的晶粒尺寸，并促进细小的α2／γ层片形成以及细化粗大的α2／γ／B2层片。对TiAl合金力学性能测试表明，适量添加稀土Y(0．3％，原子分数)可明显改善合金的室温强度和塑性，但过量添加将会造成材料性能降低；断口分析表明过量添加稀土导致沿晶断裂比例增加将损害TiAl合金的性能。     

BFe30-1-1白铜管早期腐蚀失效原因分析

某电厂凝汽器BFe30-1-1白铜管投运后几年内出现较为严重的局部腐蚀和点腐蚀，为此，对材质、水质等诸多因素进行了分析研究，通过宏观、微观检查和电化学试验，认为是微生物及生物粘泥的附着引起了铜管的早期腐蚀失效。     

LJ船用微机测流系统的应用

LJ船用微机测流系统是能自动完成测深、测速、流量计算等一系列工作的水测验仪器。经过哈尔滨水站检验，证明该系统可以在大中河流测站使用。     

Molten Salt Synthesis of Ba（ Mgl／3Nb2／3 ）O3 Powder

The single-phrase Ba(Mgl/3Nb2/3)O3(BMN) powder was saccessfully prepared by the KCImolten salt synthesis(MSS) method. The temperature for single-phase BMN powders by MSS was about 400℃ lower than that by the solid-phase method. The average particle size (APS) was about 0.91,u.m at 900℃ and increased with increasing synhesis temperature. Based on the APS, the activation energy for particle growth in theMSS, whose value was 64. 1kJmol^-1.was attained. The sinterability of the powder prepared by MSS method wasbetter than that pretared by solid-phase method.     

利用小波变换提取电力系统故障时刻的研究

在简要介绍小波理论的基础上，将小波变换应用于电力系统故障时刻的提取，并给出了220kV系统单相接地故障的MATLAB仿真实例，同时根据有效信号和随机噪声的小波变换呈现出不同的特征，探讨了小波分析用于微机继电保护时，尺度参数对小波变换的影响。     

d类截面受压钢构件稳定承载力的分析比较

对由厚钢板组成的钢受压构件d类截面稳定系数的正确取值进行了分析、比较,指出了钢结构设计规范GB50017-2003中受压构件d类截面稳定系数曲线确定过程中的错误;并通过按不同规范对比设计的算例,探讨了d类截面受压钢构件在不同规范之间稳定承载力的差异.     

电磁场法向分量边界条件非独立性的微分法证明

电磁场的法向分量边界条件不独立 ,但先前关于这一命题的微分法证明有局限性 .文中指出了这一局限性 ,给出了对任何光滑界面普遍适用的微分证明法 .     

Internal oxidation of dilute Cu–Al alloy powers with oxidant of Cu2O

The mechanisms responsible for the nucleation, growth and coarsening of Al₂O₃ particles in dilute Cu–Al alloys during internal oxidation have been investigated, and the alumina morphologies produced have been studied by electron microscopy using two-stage preshadowed carbon replica method. The alumina particle size has been observed to increase with increasing temperature of oxidation, with increasing time of oxidation, and with decreasing oxygen resource coefficient over the experimental range. These results indicate that the alumina particle size is determined by a competition between the rate of nucleation as the internal oxidation front passes and the subsequent growth and coarsening rates of the particles.     

Hot-pressed AlN-Cu metal matrix composites and their thermal properties

AlN-Cu metal matrix composites containing AlN volume fractions between 0.1 and 0.5 were fabricated firstly by liquid phase sintering of AlN using Y₂O₃ as a sintering aid and then by hot pressing the powder mixtures of sintered AlN and Cu at 1050°C with a pressure of 40 MPa under flowing nitrogen. With Y₂O₃ additions of 1.5 to 10 wt%, the densification of AlN could be achieved by liquid phase sintering at 1900°C for 3 h and subsequently slow cooling. The sintered AlN showed a maximum thermal conductivity of 166 W/m/K at a Y₂O₃ level of 6 wt%. Dense AlN-Cu composites with AlN contents up to 40 vol% were achieved by hot pressing. The thermal conductivity and the coefficient of the thermal expansion (CTE) of the composites decreased with increasing AlN volume fractions, giving typical values of 235 W/m/K and 12.6 × 10^–6/K at an AlN content of 40 vol%.