真空蒸发沉积VOPc薄膜及磁场对薄膜结构与性能的影响

用真空蒸发制备了酞菁氧钒 (VOPc)薄膜 ,并在磁场中进行了热处理。用X光电子能谱、X射线衍射、紫外 可见吸收光谱、原子力显微镜等手段对制备的薄膜进行了表征。结果表明沉积的酞菁氧钒薄膜为α 型 ,成分接近酞菁氧钒的分子式。制备的薄膜在磁场中进行了热处理 ,发现磁场使酞菁氧钒薄膜性质发生改变 :UV VIS吸收谱Q带发生红移 ;XRD谱图衍射峰强度明显增强 ,峰位略有变化 ;原子力显微镜 (AFM)分析发现晶粒大小无明显变化。以上结果说明磁场的存在使得VOPc分子在热处理过程中发生了定向的排列     

一种基于FBG和LPG的温控报警模型

文章依据FBG温度传感的原理以及LPG滤波技术,提出了一种新的光纤光栅温度报警模型.用MATLAB对系统所采用的方法进行了模拟,结果表明该系统能满足温度报警的要求.     

长庆油田陕北区原油破乳剂的筛选和复配

实验考察了8种市售水溶性破乳荆对长庆油田陕北区有代表性的宝塔区、安塞和子长原油(均为低硫中间基-石蜡基原油)的脱水效果(加量100mg／L，脱水温度55℃，时间3h)。目前长庆采油一厂使用的YT-100和延炼集团使用的GT-940对这3种原油的脱水效果均较好，但对子长原油的脱水率不高，分别为69．7％和58．9％。在由所选性能较好的破乳刺组成的4种二元复配物中，GT-940 HQ96-1对3种原油的脱水效果均高于单剂，最佳配比分别为4：1，4：1，3：2；其余3种复配物则对原油有选择性，其中GT-940 YT-100相近(97．5％)；YT-100 HQ96-1仅能改善子长原油的脱水效果，配比为4：1时脱水率最高(76．4％)；SP-169 HQ96-1仅能改善宝塔区原油的脱水效果．配比3：2和2：3时脱水率最高(92．9％)。表5参6。     

激光角膜矫正术中所用激光波长的选择

用分光光度计测定了12例兔角膜和1例人角膜的吸收光谱,结果表明波长小于300nm的准分子激光和波长在1.88μm～2.64μm,2.36μm～40μm的激光,均可对角膜进行切割并可望用于激光角膜矫正术。     

关东大地震火灾及城市防灾对策

关东大地震火灾 ,可谓 2 0世纪世界上最大的地震火灾 ,造成的人员伤亡和财产损失确实称得上前所未有。最近 ,有关方面正在吸取阪神大地震的教训 ,实施各种防灾对策。笔者以为 ,只有把确实存在着严重程度远远超过阪神大地震的灾害这件事 ,牢牢铭刻在头脑中 ,理顺对付罕见的大灾害的基本思路 ,才能从总体上全面地研究灾害对策。而且 ,关东大地震火灾的有些问题至今尚未研究清楚 ,笔者切望彻底搞清这些问题 ,以促进火灾工程学的发展。有鉴于此 ,有必要对关东大地震火灾这一历史性大灾害作一番回顾。1.关东大地震的调查情况关东大地震发生在 192…     

Rapid synthesis of La0.7Sr0.3MnO3+λ catalysts by microwave irradiation process

Microwave irradiation processing (MIP) was considered as a potential method to synthesize perovskite-type oxides rapidly, cleanly and energy-efficiently. In this paper, La_0.7Sr_0.3MnO_3+λ, a kind of promising catalyst for automobile exhaust purification, was successfully prepared by MIP in not more than 5 min. The sol–gel method was also used for comparison. All the samples were evaluated by catalytic activity tests in the simulated exhaust and characterized by XRD, BET, TEM and XRF analyses. The results showed that the integrated perovskite-type phase and uniform particle size were obtained in the microwave-treated samples. And those ones exhibited a better oxidation activity under slightly oxygen-rich condition than that by sol–gel method, which may be related to more A-site cation vacancies and larger bulk oxygen content generated in MIP. Possible formation mechanism of perovskites in MIP was also discussed.     

基于类库思想的Powerbuilder录入界面实现

在ERP及其他数据库开发项目中．方便而操作风格一致的录入界面是被用户所广泛要求的。笔者在工程项目中总结了部分用户需要的功能．并在PowerBuilder中以基类的形式实现．在加快工程进度和方便用户方面取得了不错的效果。     

70推土机主离合器分离杆螺栓失效分析

主离合器分离杆螺栓是一个重要安全件，使用中经常发生断裂。经过失效分析确定断裂原因是由其配件引起。提高配件的冷加工质量及改进结构，可解决分离杆螺栓的断裂问题。