Theoretical and practical implications of creep curve shape analyses for 7010 and 7075

Over tensile stress ranges giving creep lives up to 2000 hours at 373 to 463 K, the creep and creep fracture properties of 7010 are compared with results recorded for 7075 and other precipitation-hardened aluminum alloys. Using the ϕ methodology to quantify the systematic variations in creep curve shape with changing test conditions, the behavior patterns displayed by the different alloys are shown to depend on the extent to which precipitate coarsening causes a progressive loss of creep strength with increasing test duration and temperature. The ϕ relationships also introduce new approaches for rationalization and interpretation of creep data sets, based on the activation energy for lattice diffusion in the alloy matrices and the yield stress or UTS at the creep temperatures.     

Volumetric out-of-furnace heat treatment of 3600-M3 decomposers

Specifications require that all the welds in 12-m-diam. decomposers with a capacity of 3600 m³ be subjected to high-temperature tempering before going into service in order to alleviate the stresses from the welding operation. Specialists at the organizations VNIIPTkhimnefteapparatury and VNIImontazhspetsstroi have proposed out-of-furnace volumetric (complete) of the assembled decomposer with the use of special heaters. The use of this heating method has shortened assembly operations while providing the welds with a highquality heat treatment and reducing the stresses overall (including welding stresses, stresses from assembly of the decomposer, etc.) The technology ensures uniform heating of the housing of the decomposer and provides for close control over the process. The experience gained in heat-treating decomposers can also be used in the construction of other containers that come into contact with corrosive media. __________ Translated from Metallurg, No. 3, pp. 61–64, March, 2006.     

Atomistic simulations of grain boundary migration in copper

While the motion of twist boundaries can be readily studied by atomistic simulations with molecular dynamics (MD) under the action of an elastic driving force, the approach fails for tilt boundaries. This is due to the interaction of the elastic stress with the grain boundary (GB) structure, which causes plastic strain by GB sliding. A novel concept, the orientation correlated driving force, is introduced to circumvent this problem. It is shown that this concept can be successfully applied to the study of the migration of tilt boundaries. The migration behavior of several twist and tilt GBs was investigated. The transition from low-to high-angle boundaries can be captured, and a structural transition of tilt boundaries was found at high temperatures, which also affected the migration behavior. The results compare well with experimental results of the motion high-angle boundaries, but for low-angle boundaries, the agreement is poor. This article is based on a presentation made in the “Hillert Symposium on Thermodynamics & Kinetics of Migrating Interfaces in Steels and Other Complex Alloys,” December 2–3, 2004, organized by The Royal Institute of Technology in Stockholm, Sweden.     

Reliable eye-diagram analysis of data links via device macromodels

This paper addresses the impact of device macromodels on the accuracy of signal integrity and performance predictions for critical digital interconnecting systems. It exploits nonlinear parametric models for both single-ended and differential devices, including the effects of power supply fluctuations and receiver bit detection. The analysis demonstrates that the use of well-designed macromodels dramatically speeds up the simulation as well it preserves timing accuracy even for long bit sequences.     

On-line estimation of kinetic parameters in anaerobic digestion using observer-based estimators and multiwavelength fluorometry.

Observer-based estimators (OBE) were used for estimation of state variables and kinetic parameters in an anaerobic digestion (AD) process. A simplified first-order model with time-varying kinetic parameters was used to design an OBE for kinetic parameter estimation. This approach was validated on a laboratory-scale anaerobic reactor equipped with a multiwavelength fluorometer for on-line measurements of COD and VFA concentrations in the reactor effluent. The proposed estimators provide continuous adjustment of kinetic parameters and can be used for predictions of state variables between samples acquisition and during sensor failure.     

Beneficial effects of wettability altering surfactants in oil-wet fractured reservoirs

In fractured reservoirs, an effective matrix-fracture mass transfer is required for oil recovery. Surfactants have long been considered for oil recovery enhancement, mainly in terms of their ability to reduce oil–water interfacial tension. These surfactants are effective when the fractured formations are water-wet, where capillary imbibition of surfactants from the fracture into the matrix contributes to oil recovery. However, another beneficial aspect of surfactants, namely their ability to alter wettability, remains to be explored and exploited. Surfactants capable of altering wettability can be especially beneficial in oil-wet fractured formations, where the surfactant in the fracture diffuses into the matrix and alters the wettability, enabling imbibition of even more surfactant into the matrix. This sequential process of initial diffusion followed by imbibition continues well into the matrix yielding significant enhancements in oil recovery.In order to test this hypothesis of sequential diffusion–imbibition phenomenon, Dual-Drop Dual-Crystal (DDDC) contact angle experiments have been conducted using fractured Yates dolomite reservoir fluids, two types of surfactants (nonionic and anionic) and dolomite rock substrates. A new experimental procedure was developed in which crude oil equilibrated with reservoir brine has been exposed to surfactant to simulate the matrix-fracture interactions in fractured reservoirs. This procedure enables the measurements of dynamic contact angles and oil–water interfacial tensions, in addition to providing the visual observations of the dynamic behavior of crude oil trapped in the rock matrix as it encounters the diffusing surfactant from the fractures. Both the measurements and visual observations indicate wettability alterations of the matrix surface from oil-wet to less oil-wet or intermediate wet by the surfactants. Thus this study is of practical importance to oil-wet fractured formations where surfactant-induced wettability alterations can result in significant oil recovery enhancements. In addition, this study has also identified the need to include contact angle term in the dimensionless Bond number formulations for better quantitative interpretation of rock–fluids interactions.     

Influence of the second phase on the room-temperature tensile and creep deformation mechanisms of α-β titanium alloys: Part I. Tensile deformation

The effects of α and β phase interactions on the room-temperature tensile and creep deformation behavior of α + β titanium alloys with Widmanst?tten microstructures were studied using Ti-6.0 wt pct Mn and Ti-8.1 wt pct V as the model two-phase alloy systems. This article, Part I, deals with tensile deformation. It was found that when the α phase is present as thin (<10-μm) plates in the α + β alloys, significant twinning occurs. No significant twinning was observed in single-phase alloys with the same chemistry and similar grain size. Additionally, the β phase of Ti-8.1 V deforms by stress-induced hexagonal martensite (α′), while only twinning occurs in the single-phase β alloy with the same chemistry. Twinning in the α phase in association with stress-induced martensite (SIM) in the β phase was observed for the first time in a two-phase titanium alloy. This behavior is explained in terms of a number of factors including elastic interaction stresses between the α and β phases, coherency between the α phase and hexagonal martensite, and β phase stability.     

Identification of the adverse effect of nitrate on the phosphate release rate and improvement of EBPR process models.

The adverse effect of nitrate on the phosphate release rate in the anaerobic phase was observed and was hardly explainable with conventional EBPR process models. Four possible mechanisms were proposed including substrate competition, reduced fermentation, parallel reaction and sequential reaction. Batch experiments were designed and conducted to identify the dominant mechanism. Results showed that the sequential reaction was the only possible mechanism where only denitrification occurred if any nitrate existed in the anaerobic phase. Then the phosphate release following after the nitrate was completely removed. Nitrate inhibition effect was added into the PHA storage rate to incorporate the sequential reaction in the conventional ASM3 plus EAWAG bio-P module (ASM3 + P). Nitrate inhibition coefficient, K(I,NO,PAO) was found to be as low as 0.05 mg/L. This correlated well with experimental observation where no also meant that the anaerobic compartment of a continuous flow reactor could be seriously affected by the residual nitrate contained in the sludge recycle flow. This phenomenon caused overestimation of the phosphate uptake rate and consequently underestimation of PO4(3-) -P concentration. This problem was resolved by incorporation of a nitrate inhibition term in the ASM3 + P for more accurate simulation of the EBPR process.     

Vacuum degassing of chromium-nickel-molybdenum steel at the Magnitogorsk Metallurgical Combine

The Magnitogorsk Metallurgical Combine has conducted a study of the effect of technological factors on the hydrogen content of chromium-nickel-molybdenum steel after vacuum degassing. It was established that the most important factor is the hydrogen content of the steel before the degassing operation. The study also determined the effects of the circulation coefficient, the duration of the degassing operation, and the vacuum used in the treatment. __________ Translated from Metallurg, No. 7, pp. 68–69, July, 2006.