Flame structure and NO emission characteristics in counterflow diffusion flame of blended fuel of H₂/CO₂/Ar have been numerically simulated with detailed chemistry. The combination of H₂, CO₂ and Ar as fuel is selected to clearly display the contribution of hydrocarbon products to flame structure and NO emission characteristics due to the breakdown of CO₂. A radiative heat loss term is involved to correctly describe the flame dynamics especially at low strain rates. The detailed chemistry adopts the reaction mechanism of GRI 2.11, which consists of 49 species and 279 elementary reactions. All mechanisms including thermal, NO₂, N₂O and Fenimore are taken into account to separately evaluate the effects of CO₂ addition on NO emission characteristics. The increase of added CO₂ quantity causes flame temperature to fall since at high strain rates a diluent effect is prevailing and at low strain rates the breakdown of CO₂ produces relatively populous hydrocarbon products and thus the existence of hydrocarbon products inhibits chain branching. It is also found that the contribution of NO production by N₂O and NO₂ mechanisms are negligible and that thermal mechanism is concentrated on only the reaction zone. As strain rate and CO₂ quantity increase, NO production is remarkably augmented. Copyright © 2002 John Wiley & Sons, Ltd.     

Effect of microporosity on tensile properties of as-cast AZ91D magnesium alloy

In the present study, the effect of microporosity on the tensile properties of as-cast AZ91D magnesium alloy was investigated through experimental observation and numerical prediction. The test specimens were fabricated by die-casting and gravity-casting. For gravity-casting, the inoculation and use of various metallic moulds were applied to obtain a wide range of microporosity. The deficiency of the interdendritic feeding of the liquid phase acted as a dominant mechanism on the formation of the micropores in the Mg?Al-alloys, rather than the evolution of hydrogen gas. Although tensile strength and elongation has a nonlinear and very intensive dependence upon microporosity, the yield strength appeared to have a linear relationship with microporosity. However, it was possible to quantitatively estimate the linear contribution of microporosity on the individual tensile property for a range of microporosity, which was below about 1%. The numerical prediction suggests that the effect of microporosity on fractured strength and elongation decreased as the strain hardening exponent increased. Furthermore, the shape and distribution of micropores may play a more dominant role than local plastic deformation on the tensile behavior of AZ91D alloy.     

超声波处理和染料结晶性能对粒度分布的影响

超声波是一种频率超越人类听觉范围的声波 ,主要分为动力超声波 ( 1 8ｋＨｚ～ 1ＭＨｚ)和用于诊断的超声波 ( 1ＭＨｚ以上 )。多年以来 ,超声波作为一种辅助工具广泛应用于许多领域 ,从而引起了化学家的极大兴趣。研究表明 ,在纺织品染色过程中 ,超声波能提高反应速率可能归因于超声波的能量 ,有关超声波的应用潜力已有许多文献报道。超声波能提高染色效率主要归因于液体介质中的空化现象 ,这一点已被一致认可。所谓空化现象是指微气泡增长、崩溃、爆炸。Ｍａｓｏｎ指出 ,经超声波辐射的固体粒度显著减小。Ｔｏｍｌｉｓｏｍ和其他工作者也…     

Smart TDI readout circuit for long-wavelength IR detector

A smart time delay and integration (TDI) readout circuit is suggested which performs background suppression, cell-to-cell non-uniformity compensation, and dead pixel correction. Using the smart TDI readout circuit, the integration capacitor area occupying almost the whole area of a unit-cell can be reduced to one-fifth and transimpedance gain can increase by five times. From measurement results, it is found that the skimming current error for a few hundred nA background current is < 1.25 nA corresponding to LSB/2 of ADC and the non-uniformity introduced by cell-to-cell background current variation is reduced to 1.02 nA     

Effects of solidification structure on fatigue crack initiation and fatigue strength in Al−Si−Mg cast alloys

Rotating-bending uniaxial fatigue tests and micro-fatigue crack initiation tests were carried out using a permanent mold cast (PMC) and semi-solid die cast (SDC) with Al−7%Si−0.35%Mg composition in order to examine the relationship between solidification structures and fatigue behaviors. The crack length was measured using a replication method. Fatigue strength was improved in SDC, which was almost consistent with the predicted fatigue strength using the size of Si particle cluster. Resistance to fatigue crack initiation and fatigue strength were improved in SDC owing to the finer Si cluster and to higher ultimate tensile strength. Fatigue crack in PMC was preferentially initiated at pores. For SDC, the fatigue crack was initiated at the Si particle/matrix interface, and then sucessively grew along eutectic cell boundaries.     

Novel T-rail electrodes for substrate removed low-voltage high-speed GaAs/AlGaAs electrooptic modulators

A novel traveling-wave electrode utilizing capacitively loaded T-rail elements was developed for low-voltage high-speed substrate-removed GaAs/AlGaAs electrooptic modulators. Electrodes with varying dimensions were fabricated and characterized. Electrode phase velocity, characteristic impedance, loss coefficient, and capacitive loading were extracted from the measured s-parameters up to 40 GHz. Electrode was also simulated using a finite-element solver. The measured and calculated electrode capacitance values were found to be in excellent agreement, showing that the electrode can be precisely designed. Approaches were outlined to provide a group velocity-matched very high-speed modulator electrode suitable for a low drive-voltage substrate-removed GaAs/AlGaAs electro-optic modulator     

A 0.9 V 92 dB Double-Sampled Switched-RC Delta-Sigma Audio ADC

A 0.9 V third-order double-sampled delta-sigma audio ADC is presented. A new method using a combination of a switched-RC technique and a floating switched-capacitor double-sampling configuration enabled low-voltage operation without clock boosting or bootstrapping. A three-level quantizer with simple dynamic element matching was used to improve linearity. The prototype IC implemented in a 0.13 CMOS process achieves 92 dB DR, 91 dB SNR and 89 dB SNDR in a 24 kHz audio signal bandwidth, while consuming 1.5 mW from a 0.9 V supply. The prototype operates from 0.65 V to 1.5 V supply with minimal performance degradation.     

Facile modifications of polyimide via chloromethylation: II. Synthesis and characterization of thermocurable transparent polyimide having methylene acrylate side groups

From chloromethylated polyimide, a useful starting material for modification of aromatic polyimides, a thermocurable transparent polyimide having acrylate side groups was prepared. In the presence of 1,8‐diazabicyclo[5,4,0]undec‐7‐ene, chloromethylated polyimide was esterified with acrylic acid to synthesize poly(imide methylene acrylate). The polymer was soluble in organic solvent, which makes it possible to prepare a planar film by spin coating. The polymer film became insoluble after thermal treatment at 230 °C for 30 min. Optical transparency of the film at 400 nm (for 1 µm thickness) was higher than 98 % and not affected by further heating at 230 °C for 250 min. Adhesion properties measured by the ASTM D3359‐B method ranged from 4B to 5B. Preliminary results of planarization testing showed a high degree of planarization (DOP) value (>0.53). These properties demonstrate that poly(imide methylene acrylate) could be utilized as a thermocurable transparent material in fabricating display devices such as TFT‐LCD. Copyright © 2004 Society of Chemical Industry     

Holographic polymer‐dispersed liquid crystal fabrication under electric field

The transmission mode of holographic polymer‐dispersed liquid crystals (HPDLCs) was developed an under electric field. It is reported that orientation of LC molecules under an electric field induces orientation of oligomer molecules giving rise to low off‐state diffraction and small grating shrinkage. Copyright © 2005 Society of Chemical Industry