Synthesis of CeO2-ZrO2 solid solution by glycothermal method and its oxygen release capacity

The glycothermal (GT) reaction of Ce acetate and Zr alkoxide directly yielded CeO₂-ZrO₂ solid solutions in a region of low Ce content ≤40 mol%. Of the CeO₂-ZrO₂ solid solutions obtained by the GT method and subsequent calcination at 500 or 800 °C, the sample with 20 mol% Ce content had the largest BET surface area. This sample exhibited the highest Ce-based oxygen release capacity in the whole Ce/Zr composition range. The oxygen release capacities of CeO₂-ZrO₂ solid solutions synthesized by the GT method were much larger than those of the samples prepared by a coprecipitation (CP) method. The Reitveld analysis and the repetitive reduction-oxidation experiment indicated that the CeO₂-ZrO₂ solid solution synthesized by the GT method has a homogeneous structure as compared with that prepared by the CP method.     

Structure and Properties of Endosperm Starch and Water Soluble Polysaccharides from Sugary Mutant of Rice (Oryza sativa L.)

Structure and properties of starch and water soluble polysaccharides (WSP) from sugary (su) endosperm of rice were examined. The su starch contained more amylose and had a somewhat higher ratio of the short chains to the long chains of amylopectin than normal starch. The WSP consisted of short α-1, 4-chains and their average degree of polymerization was 8.6 glucose units. Susceptibility of the su starch to crude Rh. glucoamylase was higher than that of the normal. The initial and final temperatures and heat of gelatinization of the su starch granules were much lower than those of the normal ones.     

Fabrication of fluorine-terminated diamond-like carbon thin film using a hyperthermal atomic fluorine beam

Surface modification of diamond-like carbon (DLC) film was performed using a hyperthermal atomic fluorine beam on the purpose of production of hydrophobic surface by maintaining the high hardness of DLC film. By the irradiation of atomic fluorine beam of a 1.0 × 10²⁰ atoms/cm², the contact angle of a water drop against the DLC surface increased from 73° to 111°. The formation of CF₃, CF₂ and CF bonding on the modified DLC surface was confirmed from the measurements of X-ray photoelectron spectra and near-edge X-ray absorption fine structure spectra. Irradiation of hyperthermal atomic fluorine beam was concluded to produce insulator fluorine-terminated DLC film, which has high F content on the surface, by the taking of the use of neutral atomic beam as a fluorine source.     

Epoxidation catalysts derived from introduction of titanium centers onto the surface of mesoporous aluminophosphate: Comparisons with analogous catalysts based on mesoporous silica

Titanium/AlPO materials were prepared by grafting a titanium alkoxide (titanium isopropoxide) onto a mesoporous aluminophosphate. The structures of the surface-bound titanium species were investigated by UV–vis, FTIR, MAS NMR, and XANES/EXAFS spectroscopies. The titanium anchoring occurs by reaction between the alkoxide precursor and surface Al–OH and P–OH groups of the AlPO support. The titanium species exist in isolated tetrahedral coordination environments, and as oligomerized species. The catalysts prepared are selective and active for the liquid-phase epoxidation of cyclohexene in the presence of TBHP. The observed activities and selectivities were comparable with those obtained for similarly prepared titanium/SBA-15 samples of similar Ti content (but higher BET surface area).     

Synthesis and Sintering of Cerium(II) Monosulfide

Cerium monosulfide (CeS) powder was synthesized by the reduction of Ce₂S₃ powder with metallic Ce, which was obtained from ceria (CeO₂) powder using carbon disulfide (CS₂) gas. To obtain the maximum amount of CeS from a mixture of Ce₂S₃ and Ce, an excess amount of metallic Ce, a stoichiometric composition, was necessary in the synthesis at 1273 K for 10.8 ks. The preliminary sintering experiments also were performed using a synthetic CeS powder containing a small amount of Ce, Ce₂O₂S, and β-Ce₂S₃ as impurities. It was found that the oxygen content in the sintered compact decreases gradually as the sintering temperature increases, because of the removal of the impurities due to the evaporation of the volatile CeO. Single-phase CeS was formed by sintering at 2173 K. To evaluate the activation energy for densification of single-phase CeS, a CeS powder was prepared by milling an initial sintered compact and was used as an ingredient for hot-press experiments. Densification data during hot-press sintering were analyzed using a kinetic equation, showing that boundary diffusion is a rate-limiting process. The results suggest that this boundary diffusion model can explain well the densification data, with an apparent activation energy of 479 kJ·mol^-1.