Residual stresses and transformation toughening in MoSi2 composites reinforced with partially stabilized zirconia

The results of study of the effects of yttria stabilization (0–6 mol.%) on the room-temperature fracture behavior and toughening mechanisms in zirconia-reinforced MoSi₂ are presented in this paper. Transformation toughening is shown to occur only in composites reinforced with zirconia particles stabilized with 2 mol.% yttria. However, the fracture toughness levels are comparable in the other composites with yttria levels between 0 and 6 mol.%. Toughening in the other composites is attributed to the combined effects of residual stress, microcrack shielding/anti-shielding and/or crack deflection. A rigorous micromechanics-based model is presented for the estimation of residual stress levels in brittle materials reinforced with phases that can transform during cooling or under stress. The model is applied successfully to the rationalization of the observed fracture and toughening phenomena.     

对洪水分级的浅见

洪水的等级划分应考虑流量、水位、防洪能力及灾害等因素,综合这些因素把洪水分成5个等级。1、2级洪水,洪水流量小,水位低,基本无灾;3级洪水,洪水流量较大或水位较高,有一定灾害;4级洪水,为大洪水或高水位,有较大灾害;5级洪水,为特大洪水或高水位,灾情严重。     

Electrical properties and positron annihilation study of (Ba<Subscript>1−<Emphasis Type="Italic">x</Emphasis></Subscript>Ho<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript>)TiO<Subscript>3</Subscript> ceramics

DC resistivity, dielectric constant, dielectric loss and positron annihilation spectra of (Ba_1−x Ho _x )TiO₃ ceramics have been measured as a function of holmium concentration x. It has been found that the DC resistivity of (Ba_1−x Ho _x )TiO₃ is strongly dependent on the Ho content: it decreases three orders of magnitude and reaches a minimum at x = 0.4%. Doping with 0.6% holmium increases the permittivity of BaTiO₃ by approximately three times (from ∼1,300 to ∼4,000), with only a slight increase in the corresponding dielectric loss. The local electron density and defect concentration estimated using positron annihilation technique conforms well to the features found in the dielectric and resistivity measurements. The results have been discussed in terms of a mixed compensation model.     

60m高度处单片露天超高混凝土悬臂墙的设计与施工

通过采用竖向预应力技术 ,解决了 60m高度处单片 8m高悬臂钢筋混凝土墙根部裂缝宽度超过规范限值的问题 ;采用将预应力钢绞线顶端锚固于墙高中段等结构和施工措施 ,控制墙体长细比不超过 3 0 ,减少了由于长细比过大对墙体承载力的不利影响     

Preliminary<Emphasis Type="Italic">in vitro</Emphasis> and<Emphasis Type="Italic">in vivo</Emphasis> characterizations of a sol-gel derived bioactive glass-ceramic system

This study investigates quantitatively and qualitatively the sol-gel derived bioactive glass-ceramic system (BGS)—apatite-wollastonite (AW) type granules in the size range of 0.5–1 mm, as an effective graft material for bone augmentation and restoration. Scanning electron micrographs (SEM) of the sintered granules revealed the rough material surface with micropores in the range 10–30 μm. X-ray diffraction (XRD) pattern of the granules revealed the presence of crystalline phases of the hydroxyapatite and wollastonite, and the functional groups of the silicate and phosphates were identified by Fourier transform infrared spectroscopy (FT-IR). Thein vitro cell culture studies with L929 mouse fibroblast cell line showed very few cells adhered on the BGS disc after 24 h. This could be due to the highly reactive surface of the disc concomitant with the crystallization but not due to the cytotoxicity of the material, since the cellular viability (MTT assay) with the material was 80‰ Cytotoxicity and cytocompatibility studies proved that the material was non-toxic and biocompatible. After 12 weeks of implantation of the BGS granules in the tibia bone of New Zealand white rabbits, the granules were found to be well osteointegrated, as observed in the radiographs. Angiogram with barium sulphate and Indian ink after 12 weeks showed the presence of microcapillaries in the vicinity of the implant site implicating high vascularity. Gross observation of the implant site did not show any inflammation or necrosis. SEM of the implanted site after 24 weeks revealed good osteointegration of the material with the newly formed bone and host bone. New bone was also observed within the material, which was degrading. Histological evaluation of the bone healing with the BGS granules in the tibial defect at all time intervals was without inflammation or fibrous tissue encapsulation. After 2 weeks the new bone was observed as a trabeculae network around the granules, and by 6 weeks the defect was completely closed with immature woven bone. By 12 weeks mature woven bone was observed, and new immature woven bone was seen within the cracks of the granules. After 24 weeks the defect was completely healed with lamellar bone and the size of the granules decreased. Histomorphometrically the area percentage of new bone formed was 67.77% after 12 weeks and 63.37% after 24 weeks. Less bone formation after 24 weeks was due to an increased implant surface area contributed by the material degradation and active bone remodeling. The osteostimulative and osteoconductive potential of the BGS granules was established by tetracycline labelling of the mineralizing areas by 2 and 6 weeks. This sol-gel derived BGS granules proved to be bioactive and resorbable which in turn encouraged active bone formation.