Crystallographic characteristics and microwave dielectric properties of Ni-modified MgTa2O6 ceramics

Ni²⁺ modified MgTa₂O₆ ceramics with a trirutile phase and space group P4₂/mnm were obtained. The correlations between crystallographic characteristics and microwave dielectric performance of MgTa₂O₆ ceramics were systematically studied based on the chemistry bond theory (PVL theory) for the first time. The results indicate that the introduction of Ni²⁺ causes a change in polarizability and the Mg–O bond ionicity, which contributes to the variation of dielectric constant. Moreover, the lattice energy, and packing fraction, full width at half maximum of the Raman peak of Ta–O bond, as the quantitative characterization of crystallographic parameters, regulate the dielectric loss of MgTa₂O₆ ceramics in GHz frequency band. In addition, the study of sintering behavior shows that the densification and micromorphology are the crucial factors affecting the microwave dielectric performance. Typically, Ni²⁺ doping on the A-site of MgTa₂O₆ can effectively promote the Q × f values to 173,000 GHz (at 7.43 GHz), which ensures its applicability in 5G communication technology.     

聚氨酯分散剂在液体靛蓝制备中的应用

采用异佛尔酮二异氰酸酯(IPDI)、聚乙二醇200、400、600、800(PEG200、PEG400、PEG600、PEG800)、2,2-二羟甲基丙酸(DMPA)、1-苯基-1,2-乙二醇、中和剂三乙胺(TEA)、甲乙酮肟等为原料,制备了一种阴离子聚氨酯分散剂.通过FTIR、GPC、TG表征了分散剂的结构与性能.利用自制的分散剂采用研磨法制备了液体靛蓝分散液,以液体靛蓝分散液粒径、离心稳定性、储存稳定性为指标,探讨了分散剂链长、用量对分散液性能的影响.结果表明,研磨1 h后,以PEG400为软段合成的聚氨酯分散剂用量为染料质量的60％时制备的液体靛蓝粒径为277.1 nm,1000 r/min离心稳定性达到93.98％,3000 r/min离心稳定性为51.13％,常温放置7 d后粒径变化在20 nm以内,染色后织物的颜色深度(K/S)为10左右,约是粉状靛蓝染色K/S的2倍,染色织物的颜色性能并未改变,SEM显示分散体颗粒大小分布均匀,与分散剂甲基萘磺酸钠的甲醛缩合物(MF)和木质素85A相比,其分散体系稳定性差别不大.     

Investigation of crystal characteristics,Raman spectra,and microwave dielectric properties of Mg1-xZnxTa2O6 ceramics

Mg_(1-x)Zn_xTa₂O₆ (x = 0.00?0.08) dielectric ceramics were synthesized via the traditional solid-state reaction method. We used XRD and Rietveld refinement to demonstrate that a pure Mg_(1-x)Zn_xTa₂O₆ phase with trirutile structure was formed. Zn²⁺ substitution helped to decrease the Raman full width at half width of the A_1g mode at 703 cm^?1, which resulted in an increase in the order and rigidity of the TaO₆ octahedron, this in turn contributed to improving the Q×f values. Additionally, the introduction of Zn²⁺ significantly promoted grain growth and increased the dense, and the molecular polarizability, these factors lead to a higher permittivity. Moreover, enhanced Ta-O bond energy resulted in a more stable TaO₆ octahedron in the Mg_(1?x)Zn_xTa₂O₆ system, which contributed to enhanced τ_f values via substitution of Zn²⁺ doped on the A-site. Correspondingly, the microwave dielectric properties were significantly improved for 0.04-doped samples, obtaining: ε_r = 27, Q × f = 185,000 GHz (at 7.47 GHz), τ_f =32 ppm/°C.     

Study of haze emission efficiency based on new co-opetition data envelopment analysis

As haze intensifies in China, controlling haze emission has become the country's top priority for environmental protection. Because haze moves across different regions, it is necessary to develop a data envelopment analysis (DEA) model underpinned by both competition and cooperation to evaluate the haze emission efficiency in different provinces. This study innovatively adopts the spatial econometrics to construct the co-opetition matrices of Chinese provinces, then builds the co-opetition DEA model to evaluate the haze emission efficiency of them, and finally uses the haze data of 2015 as an example to assess the applicability of the model. The results of the study include the following: First, compared with the traditional CCR (A. Charnes & W. W. Cooper & E. Rhodes) model, this study constructs the co-opetition DEA cross-efficiency model that integrates haze's feature of cross-border moving; thus, it is more in line with the reality of haze emission and movement. Second, compared with the efficiency value gained from the CCR model, the haze emission efficiency values for Tianjin and Guangdong, two decision-making units, register greater variance when using the DEA model. The reason might lie in that they have a different spatial transportation relationship with their surrounding provinces. Third, the haze emission efficiency of provinces, according to the evaluation based on the co-opetition DEA method, varies greatly: Those with high efficiency are mostly inland provinces with slow economic growth and adverse climatic conditions, whereas many of the provinces with low efficiency are located in the relatively prosperous East China. The specific co-opetition DEA model constructed in this study enriches the research on the DEA model, which can be applied to the emission efficiency evaluation of similar pollutants around the world and can contribute empirical support to the haze reducing efforts of the government with its empirical results.     

Preparation and electrochromism of pyrochlore-type tungsten oxide film

Pyrochlore-type WO_3 powder was synthesized via hydrothermal method using aqueous sodium tungstate solution and oxalic acid as raw materials. The as-prepared powder was made into a soliquoid,from which films were made by dip coating process with indium-tin oxide(ITO).The obtained films were characterized by thermogravimetric and differential thermal analysis(TG-DTA), X-ray diffraction(XRD),scanning electron microscopy(SEM),transmission electron microscopy(TEM), cyclic voltammetry(CV), chronoamperometry(CA) and ultravioletvisible(UV-Vis) absorption. Results show that the crystal of the pyrochlore-type WO_3 powder is perfect. When the calcination temperature rises from room temperature to500 ℃,the pyrochlore-type structure first becomes deformed, then it is destroyed and turns into amorphous phase,finally it will completely convert to WO_3 with a monoclinic structure. Electrochemical and optical tests demonstrate that the film calcined at 300 ℃ exhibits the best electrochromic performance and has a coloration efficiency of up to 68.5 cm~2 C~(-1) at 884 nm.     

Design and optimization of ceramic membrane structure: From the perspective of flux matching between support and membrane

The support flux was first investigated as a separate influencing factor for its effect on performances of ceramic filtration membranes. Three pre-membranes were prepared by tape-casting and then transfer-coated to supports to form dual-layer ceramic membranes after sintering. Experiments demonstrated that membrane layers with almost the same properties were obtained despite the huge difference in support flux. When the support flux increases from 3.120 to 97.53 m³m^?2h^?1, the flux of these three membrane series have increased by 75%, 186% and 228%, respectively. Experimental rules can provide structural design and evaluation from the perspective of permeability. The limit membrane flux of a certain system was derived according to the resistance distribution law of internal membrane structure and the Darcy's theorem. On this basis, a method for designing support flux was proposed. Furthermore, we present a criterion to quickly and easily evaluate the match between the support and the top layer, which is the ratio of membrane resistance to total resistance. Finally, the filtration resistance of penetration caused by suction of membrane particles into the support was measured for the first time, taking the advantage of the transfer-coating method that inherently free of penetration. Our works are expected to deepen the understanding of the ceramic membrane structure and provided guidance for its rational design and optimization.     

文献计量视角下健康人力资本研究动态分析

通过文献计量方法从样本选取、研究动态分析、主题分布三方面对健康人力资本发展现状及热点问题进行总结.研究结果表明,自2004年开始该领域所属学科种类和期刊源日益丰富,并形成合著度较高的核心作者群体,健康人力资本研究成为人力资本领域的研究热点,健康人力资本与经济增长或收入的关系、健康人力资本指标体系的构建和居民健康人力资本收入效应的测算等问题都成为当前和未来的研究重点.     

臭氧技术在废水处理中的应用

由于臭氧的强的氧化性能,使其成为一种强氧化剂和消毒剂;臭氧技术已经广泛用于废水处理行业,臭氧具有较好的的消毒杀菌、脱色、除臭味等作用,文章通过介绍臭氧的一些基本性质,臭氧消毒杀菌、氧化、脱色及除臭味的机理,臭氧的制取方式,现代臭氧技术的研究方向等,为废水处理中臭氧技术的应用提供参考。     

3-三氟甲基-5,6,7,8-四氢-1,2,4-三唑[4,3-α]吡嗪盐酸盐的合成

乙二胺与氯乙酸乙酯经取代、环合反应制得2-哌嗪酮,2-哌嗪酮与Boc酸酐进行氨基保护反应后,再与五硫化二磷进行硫代反应制得4-(N-叔丁氧羰基)-2-哌嗪硫酮,其与三氟乙酰肼经取代、环合、脱叔丁氧羰基成盐,得标题化合物,总收率为45.7%(以氯乙酸乙酯计)。为磷酸西他列汀中间体的工业化生产提供了一条较理想的工艺路线。