Cathodic processes in the leaching and electrochemistry of covellite in mixed sulfate–chloride media

The cathodic processes that occur on a covellite (CuS) surface in mixed sulfate–chloride solutions in the absence and presence of copper(II) ions have been studied using potentiostatic transients and cyclic voltammetry at rotating disk electrodes in the potential range 0.3–0.7 V (versus SHE). This range is relevant to the oxidative leaching of this copper mineral in sulfate and chloride lixiviants. Variations in the concentrations of sulfate and chloride ions had a small effect on the cathodic reduction of covellite in the potential range of 0.5–0.3 V, although the presence of chloride ion resulted in a significant increase in the anodic current on the reverse sweep. On the other hand, addition of copper(II) ions resulted in enhanced cathodic currents and subsequent anodic currents in both sulfate and chloride solutions due to reduction of covellite to an undefined reduced copper sulfide species. Reduction of copper(II) to copper(I) ions becomes the preferred cathodic reaction as the concentration of chloride ions increases, becoming mass transport controlled at a rotating disc electrode at potentials below about 0.4 V. Potentiostatic measurements at potentials negative to the mixed potential in acidic chloride solutions have shown that reduction of copper(II) ions is reversible and have been used to estimate the rate of oxidative dissolution of the mineral which value agrees reasonably well with previously reported leaching rates under similar conditions. Reduction of dissolved oxygen has been found to be very much slower that that of copper(II) ions under ambient conditions.     

Preparation of monodisperse poly(vinyl alcohol) microspheres by heterogeneous surface saponification and iodine complex formation

Monodisperse poly(vinyl acetate) (PVAc) microspheres with high molecular weight obtained by suspension polymerization of vinyl acetate were saponified in alkaline aqueous solution to keep their spherical structure. The saponification was restricted on the surface of the PVAc microspheres and obtained particles had skin/core structure. Various poly(vinyl alcohol) (PVA) microspheres with different diameters and degrees of saponification (DSs) were obtained. The conversion of PVAc to PVA during the heterogeneous surface saponification time were examined by nuclear magnetic resonance spectroscopy and after 72 h hydrogel type PVA microspheres completely saponified were obtained. The crystal melting temperatures of the microspheres obtained by the saponification were measured a constant value of 238°C irrespective of varying DS, and the peaks became enlarged as reaction time. Iodine complexes were formed in saponified microspheres with DS of 41% and 99% by immersing them in I₂/KI aqueous solution and decomposed by the reduction of I₂ in the complexes to 2I^? using sodium sulfite to confirm whether the skin formed through the saponification was composed of PVA with high VA content. Obviously, characteristic blue color developments owing to I₅^?‐PVA complexes were observed in both saponified regions and a red in the PVAc core. Consequently, it was concluded that the PVA skins formed by heterogeneous surface saponification had high DSs. Such complexes endowed polymeric microspheres a good radiopacity which would be useful in clinical treatment of vascular diseases and were examined by X‐ray irradiation image. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Polyaniline-multiwalled carbon nanotube composites: Characterization by WAXS and TGA

Polyaniline/carboxylated multi-walled carbon nanotube (PAni/c-MWNT) nanocomposites have been synthesized by micellar aided emulsion polymerization with various c-MWNTs compositions, viz., 0.5, 1, 5, and 10 wt %. The microcrystalline parameters such as the nanocrystal size (〈N〉), lattice strain (g), interplanar distance (d_hkl), width of the crystallite size distribution, surface weighted crystal size (D_s), and volume of the ordered regions were calculated from the X-ray data by using two mathematical models, namely the Exponential distribution and Reinhold distribution methods. The effects of heat ageing on the microcrystalline parameters of the PAni/c-MWNT nanocomposites were also studied and the results are correlated. The thermal stability and electrical resistivity of the PAni/c-MWNT nanocomposites were examined with thermogravimetric analysis (TGA) and a conventional two-probe method. The TGA data indicate that the thermal stability of the nanocomposites improved after the incorporation of c-MWNTs. The influence of temperature on the resistivity of the nanocomposites was also measured. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci 2008     

Accelerated wear testing with a microfabricated surface to evaluate the lubrication ability of biomolecules on polyethylene

Wear of ultrahigh‐molecular‐weight polyethylene (UHMWPE) and wear‐particle‐induced osteolysis and bone resorption are the major factors causing the failure of total joint replacements. It is feasible to improve the lubrication and reduce the wear of artificial joints. We need further understanding of the lubrication mechanism of the synovial fluid. The objective of this study is to evaluate the lubricating ability of three major components in the synovial fluid: albumin, globulin, and phospholipids. An accelerated wear testing procedure in which UHMWPE is rubbed against a microfabricated surface with controlled asperities has been developed to evaluate the lubrication behavior. An analysis of the wear particle dimensions and wear amount of the tests has provided insights for comparing their lubrication performance. It is concluded that the presence of biomolecules at the articulating interface may reduce friction. A higher concentration of a biological lubricant leads to a decrease in the wear particle width. In addition, in combination with the wear results and mechanical analysis, the roles of individual biomolecules contributing to friction and wear at the articulating interface are discussed. These results can help us to identify the role of the biomolecules in the boundary lubrication of artificial joints, and further development of lubricating additives for artificial joints may be feasible. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Structure and processability of iodinated poly(vinyl alcohol). IV. Drawability of the films iodinated at solution before casting

The drawability of iodinated at solution before casting (IBC) polyvinyl alcohol films prepared by casting aqueous solutions of 10 wt % PVA containing 15.2, 39.8, 83.2, 117.0, and 140.1% was examined with a tensile tester at 20–60°C. The tensile behavior of IBC films showed that the yield and breaking loads were much lower, and the breaking elongation was even higher than those of the unoriented iodinated after casting (IAC) films as well as the untreated PVA films. The maximum draw ratios of the films with the weight gain of 15.2, 39.8, 83.2, 117, and 140.1% were 4.5, 5.5, 8.5, 8.0, and 7.5, respectively, which were achieved at 20°C in all. The crystallinity of all films increased by the maximum draw, regardless of crystallinity before drawing. The crystalline structure was recovered to the original PVA crystalline lattice by deiodination. Amorphous orientation and initial moduli increased with the maximum draw ratio, while the orientation of crystals was constant. The orientation and moduli increased up to the weight gain of 83.2%, whose highest draw ratio and initial modulus were 8.5 and of 7.1 GPa, respectively, and then decreased. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2008     

Isothermal crystallization behavior of hybrid biocomposite consisting of regenerated cellulose fiber,clay, and poly(lactic acid)

Quantitative analysis of isothermal crystallization kinetics of PLA/clay nanocomposite and PLA/clay/regenerated cellulose fiber (RCF) hybrid composite has been conducted. The crystallization rate constant (k) according to Avrami equation was higher in PLA/clay nanocomposite than in PLA/clay/RCF hybrid composite at the same crystallization temperature. The equilibrium melting temperature obtained by Hoffman–Weeks equation was almost same in both composites, whereas stability parameter was greater in hybrid composite than in nanocomposite. Activation energy of hybrid composite for crystallization was larger than that of nanocomposite. The value of nucleation parameter (K_g) and surface free energy (s_e) of hybrid composite were larger than nanocomposite, indicating that hybrid composite has a less folding regularity than nanocomposite. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

EPR kinetics in irradiated syndiotactic polystyrene at elevated temperatures

Free radicals are formed upon irradiation of polymers. The annealing of γ-ray irradiated syndiotactic polystyrene (sPS) with doses 10, 23 and 36 kGy was studied with electron paramagnetic resonance (EPR) spectroscopy. The EPR spectra are possibly attributed to three types of radicals, (a) the benzyl radical Ra, (b) resonance structure of the phenyl radical Rb, and (c) carbon-superoxide-centered radical Rc with three-, four-, and single-line features, respectively. Radical Ra can be easily formed by the removal of the proton from the tertiary carbon; radical Rb is created from delocalization of the spin of the radical Ra onto the benzene ring; and radical Rc may be generated from the interaction of a carbon-centered radical with dioxygen from the air which forms a carbon-superoxide center. By comparing EPR spectra of the radicals with a DPPH standard, the spin numbers of the radicals can be calculated. The spin number of all radicals decreases exponentially with time in the temperature range of 60-90 °C regardless of dose of the irradiation. The annealing of Ra, Rb, and Rc follows first-order kinetics. The activation energies of the annihilation are determined to be 15.8-19.0, 16.0-19.5, and 23.2-26.6 kJ/mol for radicals Ra, Rb, and Rc, respectively. The kinetic study presented herein can serve as a criterion for γ-ray irradiation process in various applications, such as sterilization of polymer materials and devices.     

Survey of nitrate and nitrite contents of vegetables grown in Korea.

A scientific basis for the evaluation of the risk to public health arising from excessive dietary intake of nitrate in Korea is provided. The nitrate () and nitrite () contents of various vegetables (Chinese cabbage, radish, lettuce, spinach, soybean sprouts, onion, pumpkin, green onion, cucumber, potato, carrot, garlic, green pepper, cabbage and Allium tuberosum Roth known as Crown daisy) are reported. Six hundred samples of 15 vegetables cultivated during different seasons were analysed for nitrate and nitrite by ion chromatography and ultraviolet spectrophotometry, respectively. No significant variance in nitrate levels was found for most vegetables cultivated during the summer and winter harvests. The mean nitrates level was higher in A. tuberosum Roth (5150 mg kg(-1)) and spinach (4259 mg kg(-1)), intermediate in radish (1878 mg kg(-1)) and Chinese cabbage (1740 mg kg(-1)), and lower in onion (23 mg kg(-1)), soybean sprouts (56 mg kg(-1)) and green pepper (76 mg kg(-1)) compared with those in other vegetables. The average nitrite contents in various vegetables were about 0.6 mg kg(-1), and the values were not significantly different among most vegetables. It was observed that nitrate contents in vegetables varied depending on the type of vegetables and were similar to those in vegetables grown in other countries. From the results of our studies and other information from foreign sources, it can be concluded that it is not necessary to establish limits of nitrates contents of vegetables cultivated in Korea due to the co-presence of beneficial elements such as ascorbic acid and alpha-tocopherol which are known to inhibit the formation of nitrosamine.