Effects of poly(acrylic acid) and poly(ethylene oxide) adsorption on the stability of alumina suspension

The effect of adsorbed polymer on the stability of alumina suspension was investigated. Poly(ethylene oxide) (PEO), poly(acrylic acid) (PAA) and similar kinds of polymer salts were used as a dispersant. The amount of polymer adsorbed on alumina surface and the suspension stability was measured. The pH, molecular weight, and concentration were considered as experimental parameters. PEO shows low affinity on the alumina surface while PAA has high affinity. In the case of PAA adsorption, the surface charge change by polymer adsorption influences suspension stability strongly, but not in the case of PEO adsorption. In simultaneous adsorption of PEO and PAA, the PAA concentration was fixed and PEO concentration was varied. The stability of suspension increased with increasing PEO concentration, and this is partly due to the steric stabilization by adsorption of PAA-PEO complex or adsorption of PEO through pre-adsorbed PAA and the depletion effect of non-adsorbed polymer. Suspension adsorbing sodium salts of PAA and poly(methacrylic acid) (PMA) each showed similar stability. But, when the PEO and these kinds of salts were added together to the suspension, the one with PAA sodium salt could keep a higher stability even with lower molecular weights of PEO compared with suspension with PMA sodium salt.     

Living cationic polymerization of isobutyl vinyl ether (II): Photoinduced living cationic polymerization in a mixed solvent of toluene and diethyl ether

A new method of preparation of living cationic polymer of isobutyl vinyl ether via photoinduced polymerization in the presence of diphenyliodonium iodide (DPII, initiator) and zinc iodide in a mixed solvent of toluene/diethyl ether, which was irradiated at ?78°C for short period, was completed within 15 min. The reaction was allowed for further reaction in the dark until monomer was fully consumed. It was found that increase in the conversion of monomer to polymer during the irradiation is very limited. Confirmation of the linear dependence of number‐average molar mass of resulting polymer on % conversion together with the fact that polymerization proceeds until monomer consumption, and controllability of number‐average molar mass of resulting polymer, depending on the molar ratio of monomer and initiator, strongly suggests the living nature of this polymerization, unless reaction temperature becomes higher than 0°C, i.e., the absence of chain breaking process. The narrow molar mass distribution, whose polydispersity index values are less than 1.2, reveals that the rate of initiation where irradiation is usually completed within 15 min is much faster than that of propagation in cationic nature in this system. Effect of some major factors, such as solvent polarity and temperature, on the living nature of the polymerization was also investigated. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 101: 3581–3586, 2006     

Electrical properties of (Bi3.5La0.5)Ti3O12 thin-films prepared by liquid source misted chemical deposition

The ((Bi_3.5La_0.5)Ti₃O₁₂(BLT) thin-films used in this study were fabricated on a Pt(111)/SiO₂/Si(100) substrate by a Liquid Source Misted Chemical Deposition (LSMCD) technique. X-ray diffraction patterns showed that the BLT films were crystallized and no other phases were observed when annealed above 650 ‡C. Grain size and remnant polarizations increased with increase in the annealing temperature, while leakage current densities decreased. The remnant polarizations (Pr) increased from 2.0 to 4.8 and 19.0 μC/cm2 with increase in the annealing temperature from 650 to 700 and 750 ‡C, respectively. The BLT films annealed at 700 ‡C in O₂ showed a good fatigue resistance of reduced polarization by 10% after 10⁹ switching cycles when 9 V of bipolar voltage was applied at a frequency of 40 kHz.     

Changes in pore properties of phenol formaldehyde-based carbon with carbonization and oxidation conditions

Porous carbon beads were prepared by carbonizing at 700 and 1000 °C under N₂ (NN-series) or CO₂ atmospheres (CO-series) and a subsequent oxidization with boiling nitric acid solution (13%, v/v) for 3 h (ANN- and ACO-series). BET surface area of both CO- and NN-series samples tends to increase with increasing carbonization temperature, but CO-series samples show higher BET surface areas (700 °C: 610 m²/g, 1000 °C: 780 m²/g) compared with those of NN-series samples (700 °C: 380 m²/g, 1000 °C: 580 m²/g). After acid oxidation, BET surface areas of NN-series samples increased from 580 to 650 m²/g, whereas those of CO-series samples decreased from 780 to 600 m²/g. On subsequent acid oxidation, acidic surface functional groups increased in both CO- and NN-series samples, but the CO-series samples tend to have much more acidic surface functional groups. Adsorption of halogenated methanes, such as tetra-, tri- and dichloromethanes, onto the samples of CO-, NN-, ACO- and ANN-series was thought to be driven initially by the basicity, but the acidic functional groups that could attract adsorbates via dipole-dipole interaction might hinder the adsorption of subsequently incoming adsorbates.     

Magnetic mechanical capsule robot for multiple locomotion mechanisms

This paper proposes a magnetic mechanical capsule robot which crawls in a fluid-filled tube. The developed capsule robot employs two locomotion mechanisms simultaneously. It has spiral ribs at both ends, which are rotated by a small on-board motor. Such rotating spiral structures generate a driving force of the capsule robot. We invented a magnetic mechanical mechanism to transfer the rotational motion of the frontal part into the linear motion of the middle part. Using this original mechanism, the linearly moving part at the middle of the capsule robot generates a supportive driving force. The improved mobility is evaluated in experiments. The developed capsule robot employing multiple locomotion mechanisms moves 44% faster than the spiral motion-based capsule robot. The developed magnetic mechanical mechanism and the mobile robotic platform could be used for pipe inspection robots or medical robots.     

Leakage current in a Si-based nanopore structure and its influence on noise characteristics

We have measured leakage current in a silicon substrate-based nanopore membrane device immersed in an aqueous environment which typically shows the current level of few nA. This current level is compared with the measured current density (400 nA/cm² at 1 V) from the pristine Si wafer (p-type, 10¹⁶/cm³ boron doping) indicating that the exposed Si surface in a nanopore membrane device acts as an electrochemical reaction site. The leakage current is drastically reduced from >10 nA to <100 pA at 1 V by the deposition of a dielectric layer to the Si-based nanopore membrane device. We also noted that the root-mean-square noise of the ionic current is also reduced from 38 to 28 pA in correlation with the reduction of leakage current, indicating that electrochemical reaction provides one of the major sources of noise.     

Effectiveness test of alginate‐derived polymeric surfactants

A series of alginate‐derived polymeric surfactants (APSs) with a linear alkyl group (C8, C12, C16) was synthesized by oxidation followed by reductive amination of 2,3‐dialdehydic alginate. The products were characterized by measuring IR spectra, NMR spectra, surface tension and critical micelle concentration (cmc). They were also tested for the solubilization of azobenzene and adsorption of heavy metal. In the case of 40% CHO‐C8 APSs, the lowest interfacial tension value (31.5 m Nm^?1) was obtained at the cmc value of 1.35 g dm^?3. The dissolving capacity of 40% CHO‐C8 APS towards azobenzene was 27 times greater than that of alginate. The overall cobalt (Co²⁺) removal efficiency by adsorption using APSs was high compared with that of sodium alginate at pH 3, 5 and 7. Equilibrium aspects of cobalt adsorption onto 10% CHO‐APSs were studied, and the results show that APSs had high equilibrium capacities for cobalt uptake, 115.5 mgg^?1. © 2002 Society of Chemical Industry     

Polyurethane‐infiltrated carbon foams: A coupling of thermal and mechanical properties

The thermal and mechanical properties of polyurethane‐infiltrated carbon foam of various densities were investigated. By combining the high thermal conductivity of the carbon foam with the mechanical toughness of the pure polyurethane, a mechanically tough composite (relative to the unfilled foam) that could be used at higher temperatures than the polyurethane's degradation was formed. Both the tensile strength and the modulus increased by an order of magnitude for the composites compared to unfilled foam, while the compressive and shear strengths and moduli of the composites approached values exhibited by pure polyurethane. At both 300 and 400°C, the rectangular blocks of pure polyurethane lost their mechanical integrity due to decomposition in air. Thermogravimetric analysis confirms substantial initial weight loss above 290°C. Filled carbon foam blocks, however, maintain their mechanical integrity at both 300 and 400°C indefinitely, although the bulk of the rectangular block mass is polyurethane. Three different carbon foam densities are examined. As expected, the higher density foams show greater heat transfer. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 87: 2348–2355, 2003     

The influence of titanium on the electrochemical properties of the AB5-type metal hydrides

AB₅-type intermetallic compounds were prepared by arc-melting in argon atmosphere. The composition of a stoichiometric compound LaNi_3.6Al_0.4Co_0.7Mn_0.3 with a hexagonal CaCu₅ structure was varied by stoichiometric and nonstoichiometric addition of Ti. With the increase of the Ti y0.05 content in LaNi_3.6Al_0.4Co_0.7Mn_0.3Ti_y, the hydrogen storage capacity is enhanced, whereas when y=0.1–0.3, it is decreased. The discharge capacity and cyclability are increased considerably by addition of titanium in the range of 0.02–0.1 with a maximum value at about 0.1%. The highest maximum capacity is achieved for a nonstoichiometric addition of 0.05% Ti. The kinetic properties are also additionally improved by the formation of a titanium-rich second phase. This can explain the improvement of the capacity for alloys with low Ti content. The decrease in capacity for high Ti content was also correlated with the amount of the Ti-rich phase. Therefore, the improvement of kinetics are due to the catalytic effect, grain boundary diffusion effect or more pronounced alloy pulverization upon cycling. This study has been aimed to improve the electrode properties of a series of multicomponent LaNi_3.6Al_0.4Co_0.7Mn_0.3Ti_y (y=0.0, 0.02, 0.05, 0.1, 0.2, 0.3) alloys which have mutual complementary properties. All the prepared alloys have been subjected to analyses by EDS, SEM and XRD. In order to determine the hydrogen storage capacity, the pressure composition isotherms (P–C–T curves) have been used. The metal hydride electrodes were characterized by galvanostatic cycling test.