Temperature Dependence of KIC for High-Pressure Hot-Pressed Si3N4 Without Additives

Temperature dependence of K_IC values for Si₃N₄ bodies sintered at high pressures without additives was studied from room temperature to 1400°C. Little change in K_K was found in this range.     

Redox properties of CeO2 and Pt-Rh/CeO2 studied by TAP method

Redox properties of CeO₂ and Pt-Rh/CeO₂ were studied by temporal analysis of products (TAP) method using alternative pulses of CO and O₂. A portion of pulsed CO was oxidized to CO₂ and a portion of CO was adsorbed on the surface. Pulsing ¹⁸O₂ onto the catalyst which has surface species derived from CO, evolved CO₂ contained no ¹⁸O suggesting that the surface species will be carbonate ions.     

Lysozyme requires fluctuation of the active site for the manifestation of activity

Mutations around His15 which lie far away from the active site,stimulated glycol chitin activity of lysozyme at physiologicaltemperature. Del-Argl4Hisl5 lysozyme, a mutant lysozyme whoseArgl4 and Hisl5 were deleted together, and has the highest activityamong these mutant lysozymes, had a similar binding abilityto a trimer of N-acetyl-glucosamine, a substrate analogue, relativeto native lysozyme. This suggests that the increased activitywas due to an increased k_cat in the catalysis reaction. TheH-D exchange rate of the N-1 proton in the Trp63 which is locatedin the active site cleft, was enhanced in the Del-Argl4Hisl5lysozyme, while 2-D proton NMR analysis revealed no conformationalchange around Trp63. We conclude that some sort of fluctuationat the active site might be required for the manifestation ofactivity. This theory is supported by the finding that the Del-Argl4Hisl5lysozyme showed a shift in temperature dependency of activityto lower temperatures compared with that of native lysozyme.     

Influence of reaction temperature on direct esterifications in a continuous recycling process between terephthalic acid and ethylene glycol

Simulations were carried out with a continuous recycle esterification model for the terephthalic acid–ethylene glycol (TPA–EG) system proposed previously. The influence of reaction temperatures, recycle ratios, and residence times on the oligomer characteristics was examined and the following results were obtained: (1) The main reactions proceed more under higher reaction temperatures, but the side reactions on diethylene glycol (DEG) proceed further than do the main reactions. (2) The higher residence time ratio of the first reactor to the total results in the proceeding of esterifications, which becomes remarkable as the temperature becomes high. (3) As the recycle ratio becomes high, the esterfications proceed, but in the very high degree of esterification, the tendency is reversed. (4) The characteristics of oligomer are almost the same at the same degree of esterification, independent of the reaction conditions. © 1994 John Wiley & Sons, Inc.     

Resistance to sulfur poisoning of hot gas cleaning catalysts for the removal of tar from the pyrolysis of cedar wood

In the partial oxidation of tar derived from the pyrolysis of cedar wood, the effect of H₂S addition was investigated over non-catalyst, steam reforming Ni catalyst, and Rh/CeO₂/SiO₂ using a fluidized bed reactor. In the non-catalytic gasification, the product distribution was not influenced by the presence of H₂S. Steam reforming Ni catalyst was effective for the tar removal without H₂S addition, however, the addition of H₂S deactivated drastically. In contrast, Rh/CeO₂/SiO₂ exhibited higher and more stable activity than the Ni catalyst even under the presence of high concentration of H₂S (280 ppm). On the Ni catalyst, the adsorption of sulfur was observed by XPS and Ni species was oxidized during the partial oxidation of tar. In the case of Rh/CeO₂/SiO₂, the adsorption of sulfur was below the detection limit of XPS. This can be related to the self-cleaning of catalyst surface during the circulation in the fluidized bed reactor for the partial oxidation of tar derived from cedar pyrolysis.     

Low-temperature selective reduction of NO with propene over alkaline-exchanged mordenites

Partially protonated alkaline mordenites showed higher activity per acid amount below 573 K than acidic zeolites for the selective reduction of NO with C₃H₆ in the presence of O₂, which can be related to a high concentration of NO₃ ^- species in the zeolite channels. This revised version was published online in July 2006 with corrections to the Cover Date.     

Microstructure and Thermal Shock Resistance of Molten Glass-Coated Carbon Materials Fabricated by Interfacial Control

Carbon substrates were coated completely with a molten silicate glass, where the wettability of carbon to glass was improved by infiltration and pyrolysis of perhydropolysilazane. Microstructures of the carbon–glass interface were dependent on P n ₂ during coating. Coating at lower P n ₂ induced the formation of cristobalite at the carbon–glass interface. When the coating was performed at higher P n ₂, the glass and carbon were strongly adhered, without the formation of cristobalite. Coating at higher P n ₂ improved the thermal shock resistance of the glass layer, because crack initiation was not induced by the phase transformation of cristobalite during the cooling process. In the case of coating at higher P n ₂, an oxynitride glass layer was formed at the glass subsurface by dissolution of N₂. A porous glass subsurface layer with uniform spherical micro-pores could be produced by soaking near the glass transition temperature in a steam environment. The porous layer with fine and homogeneous microstructure acts as a thermal shock absorbing layer, so that glass-coated carbon with a porous glass layer has excellent thermal shock resistance in addition to steam oxidation resistance.     

Copper ⇌ Alkali Ion Exchange of Alkali Aluminosillcate Glasses in Copper-Containing Molten Salt: I, Monovalent Copper Salt, CuCl

Cu⁺⇌ R⁺ (R = Li, Na, and K) ion exchange experiments were conducted for 20R₂O·10Al₂O₃·70SiO₂ glasses in molten CuCl at 550°C in air and nitrogen atmospheres. The depth profiles of the copper incorporated into glasses were determined with an electron microprobe X-ray analyzer. The total amount of diffusing copper, M _t, strongly depended on the type of alkali ion in the glass and the ion-exchange atmosphere; i.e., M _t increased with increasing cationic size in the order Li < Na < K and M _t was greater in air than in nitrogen. The Cu ⇌ R⁺ ion exchange kinetics are discussed in detail.     

One-Step Synthesis of Luminescent Nanoparticles of Complex Oxide, Strontium Aluminate

An organic aqueous solution of metal acetylacetonate precursors was subjected to spray pyrolysis in order to fabricate SrAl₂O₄:Eu (SAO) nanoparticles. Non-agglomerated luminescent SAO nanoparticles, having a spherical shape with a size of 10–30 nm, were achieved in a single step, while only submicrometer-sized SAO particles were obtained from the conventional ultrasonic pyrolysis of the metal nitrates. Without any post-annealing process, the as-prepared SAO nanoparticles were observed to exhibit a strong photoluminescence, which is comparable with that of the submicrometer-sized SAO particles. A mechanism for the formation of the nanoparticles is also discussed.     

Hydrothermal Formation of Hydroxyapatite Layers on the Surface of Type-A Zeolite

Type-A zeolite evenly covered with hydroxyapatite thin layers was prepared using hydrothermal treatment at 120°C for 8 h under autogenous pressure. The hydroxyapatite needlelike nanocrystals, 100–200 nm in diameter and 30 nm in thickness, were grown under the reaction between discharged Ca²⁺ ions from type-A zeolite and PO₄³⁻ ions in (NH₄)₃PO₄ solution. The preferential orientations of the c -axis of hydroxyapatite crystals perpendicular to a zeolite surface were observed using transmission electron microscopy. The crystal structure of type-A zeolite was not destroyed under the reaction, but the surface morphology was changed only with complete covering of scaly hydroxyapatite particles.