A novel spin-finishing method for antistatic modification of polyester fiber. Surface reaction onto amine-containing copoly(amide-ethers) blended with polyester fiber

Copoly(amide-ethers) containing two types of tertiary amine units were made as antistatic modifiers for poly(ethylene terephthalate) (PET) fibers. The filaments of the copolymers were melt-spun and reacted with three alkylating agents in order to quaternize the tertiary amine into a sulfo-betaine, a carbobetaine, and an ammonium ion. The apparent electric resistivity of the filaments was greatly reduced by this reaction, being in the range of 10⁶ to 10⁸ Ω/cm. However, because these quaternized copolymers incurred decomposition during blend spinning with PET, a blend PET fiber containing one type of copoly(amide-ether) was melt-spun and subjected to quaternization of the amino groups as well as to surface crosslinking with various alkylating and epoxy agents. The quaternized blend fibers obtained showed improved antistatic properties compared with the original blend fiber. Particularly, the fibers crosslinked with epoxy compounds were found to have the best antistatic properties that had ever been attained with this type of modification. The antistatic properties were retained even after dyeing, because both hydrophilic and ionic groups had been effectively immobilized on the surface. Since this quaternization and crosslinking could be conducted on-line with spinning and drawing within a short reaction time, this modification technique is called “spin-finishing method”, which should be superior to the conventional methods in terms of cost performance and productivity.     

A facile antistatic modification of polyester fiber based on ion-exchange reaction of sulfonate-modified polyester and various cationic surfactants

A new technique for imparting antistatic properties to poly(ethylene terephthalate) (PET) fiber has been developed. In this technique, blend polyester fibers containing poly(ethylene terephthalate/5-sulfoisophthalate) (SIP-PET) were prepared by blend spinning and then treated with various cationic surfactants in the process of dyeing. The surfactants could effectively be immobilized on the fiber as the counter cations of the sulfonate groups of the 5-sulfoisophthalate (SIP) units and aid the release of static electrons formed in the fiber. Thus, the half-life time (t_1/2) of leakage of static charge and the surface resistivity (Rs) of the blend PET fibers became much lower after treating. The best result was obtained with a methylated quaternary ammonium salt of a stearylamine-ethylene oxide (EO) adduct or hydrochloride of a laurylamine-EO adduct as the surfactant of which the number of EO units was around ten. Even after five washing cycles the t_1/2 value of the fibers treated with these surfactants was kept lower than 30 s with the Rs value maintained in the order of 10¹³ Ω cm^-2. Therefore, the present technique could be useful for practical production of polyester fibers with “semi-permanent” antistatic properties which can be recovered by re-treatment even if they were lost.     

Kinetics of oxygen reduction reaction at tin-adatoms-modified gold electrodes in acidic media

In the present report, oxygen reduction reaction (ORR) at polycrystalline gold (Au (poly)) electrode in situ modified by the underpotential deposition (upd) of Sn-adatoms is addressed. The ORR was investigated at the Sn-adatoms-modified Au (poly) electrode by the hydrodynamic voltammetric technique with a view to evaluating the various related kinetic parameters. The results demonstrated that the underpotential deposited Sn-adatoms on the Au (poly) electrode substantially promoted the activity of the electrode towards an exclusive one-step four-electron ORR forming H₂O as the final product.     

Copolymerization of ethanesultam with 2-methyl-2-oxazoline

Summary This paper describes the so-called No Catalyst Copolymerization between dioxo-1,1-thiazetidine-1,2(Ethanesultam; ESm) and 2-methyl-2-oxazoline. The copolymerization took place without any added initiator to produce copolymers of MeOZO and ESm. The structure of the copolymer was determined by the IR and NMR spectra, elemental analysis, as well as by the result of an alkaline hydrolysis of the copolymer. The reaction scheme of the copolymerization via zwitterion mechanism (Eq 3–5) was proposed.     

Precision die-casting of optical MU/SC conversion sleeve

The performance of MU/SC conversion sleeve produced by bulk metallic glass (Zr₅₅Al₁₀Ni₅Cu₃₀) was examined. A precision die-casting method was applied to improve size accuracy. The size accuracy of the conversion sleeve produced by the precision die-casting method was ±1 μm, and optical insertion loss (Li) was less than 0.3 dB for a standard value. The wear resistance of metallic glass is improved by surface oxidation treatment in air at 673 K. The MU/SC conversion sleeve produced from bulk metallic glass has superior characteristics for optical parts.     

Decreased Podocyte Vesicle Transcytosis and Albuminuria in APC C-Terminal Deficiency Mice with Puromycin-Induced Nephrotic Syndrome

In minimal change nephrotic syndrome, podocyte vesicle transport is enhanced. Adenomatous polyposis coli (APC) anchors microtubules to cell membranes and plays an important role in vesicle transport. To clarify the role of APC in vesicle transport in podocytes, nephrotic syndrome was induced by puromycin amino nucleoside (PAN) injection in mice expressing APC1638T lacking the C-terminal of microtubule-binding site (APC1638T mouse); this was examined in renal tissue changes. The kidney size and glomerular area of APC1638T mice were reduced (p = 0.014); however, the number of podocytes was same between wild-type (WT) mice and APC1638T mice. The ultrastructure of podocyte foot process was normal by electron microscopy. When nephrotic syndrome was induced, the kidneys of WT+PAN mice became swollen with many hyaline casts, whereas these changes were inhibited in the kidneys of APC1638T+PAN mice. Electron microscopy showed foot process effacement in both groups; however, APC1638T+PAN mice had fewer vesicles in the basal area of podocytes than WT+PAN mice. Cytoplasmic dynein-1, a motor protein for vesicle transport, and α-tubulin were significantly reduced in APC1638T+PAN mice associated with suppressed urinary albumin excretion compared to WT+PAN mice. In conclusion, APC1638T mice showed reduced albuminuria associated with suppressed podocyte vesicle transport when minimal change nephrotic syndrome was induced.     

Removal of phosphate ions with a chemically modified chitosan/metal‐ion complex

The adsorption of metal ions (Mo⁶⁺, Cu²⁺, Fe²⁺, and Fe³⁺) was examined on chemically modified chitosans with a higher fatty acid glycidyl (CGCs), and the adsorption of Cu²⁺ was examined on ethylenediamine tetraacetic acid dianhydride modified CGCs (EDTA‐CGCs) synthesized by the reaction of the CGCs with ethylenediamine tetraacetic acid dianhydride. The adsorption of phosphate ions onto the resulting substrate/metal‐ion complex was measured. Mo⁶⁺ depicted remarkable adsorption toward the CGCs, although all the Mo⁶⁺ was desorbed under the adsorption conditions of the phosphate ions. The other metal ions were adsorbed to some extent on CGCs by chelating to the amino group in the substrate, except for CGC‐1, which had the highest degree of substitution (83.9%). Considerable amounts of Fe²⁺ were adsorbed onto CGCs; however, only a limited number of phosphate ions was adsorbed onto the substrate/metal‐ion complex. As a result, the following adsorbent/metal‐ion complexes gave higher adsorption ability toward phosphate ions: CGC‐4/Cu²⁺, CGC‐4/Fe³⁺, and EDTA‐CGC‐3/Fe³⁺. Where, CGC‐3 is a chemically modified chitosan with the degree of substitution of 26.5 percentage, and CGC‐4 is one with the degree of substitution of 16.0 percentage. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Mechanical properties and thermal aging behavior of styrene‐butadiene rubbers vulcanized using liquid diene polymers as the plasticizer

The mechanical properties of styrene‐butadiene rubber (SBR) vulcanizates prepared using various plasticizers including liquid polybutadiene and styrene‐butadiene copolymers were investigated. The effect of the liquid polymers as the plasticizers on the mechanical properties of the polymers, such as the hardness, tensile storage modulus, tanδ, and the modulus at 100% elongation values, were determined before and after the thermal aging. As a result, it was revealed that the use of these liquid polymers gave less amount of change in the measurement values for the mechanical properties during the aging. The crosslinking density and the amount of free polymers were also determined on the basis of the swelling and extraction data, respectively, using several organic solvents. These results support the fact that the added liquid polymers are fixed to the SBR networks. We revealed the superiority of the liquid styrene‐butadiene copolymers as the plasticizer, which provides sufficient mechanical properties after vulcanization and the excellent maintenance of the properties during the thermal aging process. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010