Phase transformation and interface segregation behavior in Si3N4 ceramics sintered with La2O3–Lu2O3 mixed additive

Microstructure and mechanical property of silicon nitride (Si₃N₄) ceramic are strongly dependent on the selection of sintering additives. When rare‐earth (RE) oxide is used as the sintering additive, segregation of RE ions at interface between Si₃N₄ grain and intergranular glassy film (IGF) is believed to play a critical role. Although the ionic radius of RE ion is known to be an empirical parameter to modify the mechanical property, the correlation between the segregated ions and their ionic radii is still under controversy. In order to address this issue, (i) rate of α‐β phase transformation and (ii) segregation behavior at the interface were studied for Si₃N₄ ceramics sintered using mixture of La₂O₃ and Lu₂O₃ as additives in this study. Specimens of Lu content 30% and higher exhibited lower activation energies for the α‐β phase transformation as compared with those of Lu content 20% and lower. In terms of the segregation behavior, La was preferably segregated at one site and Lu at the other site along β‐Si₃N₄/IGF interface in the specimens of Lu content 30% and higher. It is understood from these results that Lu segregation site should be more closely related with grain growth.     

Thermotropic and Barotropic Phase Behavior of Phosphatidylcholine Bilayers

Bilayers formed by phospholipids are frequently used as model biological membranes in various life science studies. A characteristic feature of phospholipid bilayers is to undergo a structural change called a phase transition in response to environmental changes of their surroundings. In this review, we focus our attention on phase transitions of some major phospholipids contained in biological membranes, phosphatidylcholines (PCs), depending on temperature and pressure. Bilayers of dipalmitoylphosphatidylcholine (DPPC), which is the most representative lipid in model membrane studies, will first be explained. Then, the bilayer phase behavior of various kinds of PCs with different molecular structures is revealed from the temperature–pressure phase diagrams, and the difference in phase stability among these PC bilayers is discussed in connection with the molecular structure of the PC molecules. Furthermore, the solvent effect on the phase behavior is also described briefly.     

miR-29 Represses the Activities of DNA Methyltransferases and DNA Demethylases

Members of the microRNA-29 (miR-29) family directly target the DNA methyltransferases, DNMT3A and DNMT3B. Disturbances in the expression levels of miR-29 have been linked to tumorigenesis and tumor aggressiveness. Members of the miR-29 family are currently thought to repress DNA methylation and suppress tumorigenesis by protecting against de novo methylation. Here, we report that members of the miR-29 family repress the activities of DNA methyltransferases and DNA demethylases, which have opposing roles in control of DNA methylation status. Members of the miR-29 family directly inhibited DNA methyltransferases and two major factors involved in DNA demethylation, namely tet methylcytosine dioxygenase 1 (TET1) and thymine DNA glycosylase (TDG). Overexpression of miR-29 upregulated the global DNA methylation level in some cancer cells and downregulated DNA methylation in other cancer cells, suggesting that miR-29 suppresses tumorigenesis by protecting against changes in the existing DNA methylation status rather than by preventing de novo methylation of DNA.     

Growth and microstructure of Ba β-alumina films by laser chemical vapor deposition

Ba β-alumina films were prepared by laser chemical vapor deposition. Mostly single-phase Ba β-alumina films were obtained at 1125–1200 K and for an Al/Ba molar ratio of 12.4–16.6. BaAl₂O₄ and α-Al₂O₃ were codeposited with Ba β-alumina under Ba- and Al-rich conditions, respectively. The Ba β-alumina films consisted of hexagonal grains, and the (1 1 0)-oriented Ba β-alumina films had a fin-like columnar structure. The highest deposition rate reached 120 μm h^?1 at around 1200 K. A thin layer of Ba-rich superstructure was formed on the surface of the (1 1 0)-oriented columnar grains.     

Transparent Lu3NbO7 bodies prepared by reactive spark plasma sintering and their optical and mechanical properties

Transparent lutetium niobate (Lu₃NbO₇) bodies were prepared by reactive spark plasma sintering using Lu₂O₃ and Nb₂O₅ powders. Fully dense Lu₃NbO₇ bodies with density greater than 99.5% of the theoretical were obtained at 1300–1650 °C. The grains steadily grew from 0.1 to 0.6 μm with increasing sintering temperature from 1200 to 1450 °C and significant grain growth from 2.2 to 9.2 μm occurred at 1550–1650 °C. The Lu₃NbO₇ body sintered at 1450 °C showed the highest transmittance of 63% at 550 nm after heat treatment at 850 °C in air for 6 h. Fully dense, submicron-size transparent Lu₃NbO₇ exhibited Vickers hardness of ～13.0 GPa and indentation fracture toughness of 1.0 MPa m^1/2.     

A Practical Model for the Interactions Between Hydrating Portland Cements and Poly-β-Naphthalene Sulfonate Condensate Superplasticizers

The performance of poly-β-naphthalene sulfonate condensate superplasticizer (BNS) as a dispersant for cement in concrete is affected severely by slight differences in the characteristics of the cement. In order to be able to predict these effects, a model for estimating the fluidity of cement paste containing BNS is proposed. This model is based on an assumption that the fluidity of cement paste is proportional to the BNS adsorption amount per surface area of hydrated cement (Ad/Hy). BNS is known to show two types of sorption on hydrated cement: one is the bulk absorption into initial hydrates and the other one is the superficial adsorption onto hydrates. Only the superficially adsorbed BNS is expected to work as a dispersant. By assuming a competitive Langmuir-type adsorption on hydrates between BNS and SO₄²⁻, a simple method to estimate Ad/Hy is developed, with the concentrations of BNS and SO₄²⁻ as the only two independent parameters. The resulting estimates of Ad/Hy show a good correlation with paste flow and its change with elapsed time for a broad range of cements. The SO₄²⁻ concentration in the aqueous phase of the cement paste just after the beginning of the mixing is known to affect the performance of BNS as a dispersant. By using the proposed model to discriminate between the superficial adsorption and bulk absorption of BNS, this phenomenon is explained quantitatively.     

Electrochemical formation of AlN in molten LiCl-KCl-Li3N systems

Electrochemical formation of aluminum nitride was investigated in molten LiCl-KCl-Li₃N systems at 723 K. When Al was anodically polarized at 1.0 V (versus Li⁺/Li), oxidation of nitride ions proceeded to form adsorbed nitrogen atoms, which reacted with the surface to form AlN film. The obtained nitrided film had a thickness of sub-micron order. The obtained nitrided layer consisted of two regions; the outer layer involving AlN and aluminum oxynitride and the inner layer involving metallic Al and AlN. When Al electrode was anodically polarized at 2.0 V, anodic dissolution of Al electrode occurred to give aluminum ions, which reacted with nitride ions in the melt to produce AlN particles (1-5 μm of diameter) of wurtzite structure.     

Synthesis and application of fluorescein- and biotin-labeled molecular probes for the chemokine receptor CXCR4

The design, synthesis, and bioevaluation of fluorescence- and biotin-labeled CXCR4 antagonists are described. The modification of D-Lys8 at an epsilon-amino group in the peptide antagonist Ac-TZ14011 derived from polyphemusin II had no significant influence on the potent binding of the peptide to the CXCR4 receptor. The application of the labeled peptides in flow cytometry and confocal microscopy studies demonstrated the selectivity of their binding to the CXCR4 receptor, but not to CXCR7, which was recently reported to be another receptor for stromal cell-derived factor 1 (SDF-1)/CXCL12.     

HCl emission during co-pyrolysis of demolition wood with a small amount of PVC film and the effect of wood constituents on HCl emission reduction

In this study, HCl emission during the co-pyrolysis of demolition wood and a small amount of polyvinyl chloride (PVC) film (the Cl content of which ranged from 0.5% to 6% by weight) in an N₂ atmosphere at elevated temperatures of up to 600 °C was measured using a laboratory-scale cylindrical batch reactor. In the pyrolysis experiments, HCl emission was reduced by the presence of wood. The effect of the primary constituents of wood (cellulose, hemicellulose, and lignin) on HCl emission was investigated by not only measuring HCl emission and Cl distribution to various phases during the co-pyrolysis of each constituent with PVC film but also by conducting thermogravimetric analysis of the constituents. This investigation first revealed that hemicellulose significantly reduced HCl emission by fixing most of the Cl molecules in a sample into pyrolyzed residue.     

Fracture Strength and Microstructure of β-SiAlON with Hafnia Addition

The influence of HfO₂ addition on the fracture strength and microstructure of ß-SiAlON ceramics sintered from Si₃N₄ and Al₂O₃ powders was investigated. The strength was increased by the addition of HfO₂, from ∼500 MPa to 700 MPa, and was almost constant from ambient temperature to 1300°C. Monoclinic HfO₂ grains that were distributed in the SiAlON grain boundaries had a flat shape (∼20 nm thick) and were surrounded by an amorphous phase. The aluminum concentration in ß-SiAlON in the samples with an Al₂O₃ starting composition of 15 wt% was decreased by the addition of HfO₂. The amount of secondary phases was very small at grain boundaries between the SiAlON grains; amorphous phases were observed infrequently at the triple points but were very small (∼20 nm). The effects of HfO₂ addition on the mechanism of the microstructure development and fracture strength are discussed.