Characterization of hot-pressed films from superfine wool powder

In this study, superfine wool powder was plasticized with glycerol and hot-pressed into a film. Scanning electron microscopy photos showed that the superfine wool powder could be molded into a smooth film and that the wool powder was distributed evenly in the cross section of the film. Fourier transform infrared analysis revealed no substantial changes in the chemical structure of the wool powder after hot pressing, but the absorbing peaks of glycerol were found in the spectrum. X-ray diffraction analysis showed that the overall crystallinity increased after the wool powder was hot-pressed into film. Thermogravimetry (TG) analysis indicated that the thermal stability of the hot-pressed film decreased. A transition point appeared in the TG curve of the wool hot-pressed film as glycerol was added. The differential thermal analysis curve of the film showed sharp absorbing peaks similar to that of wool powder. With increasing glycerol content, the film showed increasing ductility and softness. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

关于《高分子化学》课程教学的几点思考

高分子化学是高分子材料专业的专业基础课。文章从几个方面对高分子化学课程教学进行初步探索,包括选择教学重点、兴趣点,合理有效利用多媒体与双语教学方式、开展师生互动教学,完善配套的实验与生产实践等,在教学的同时努力提高学生的专业素质。     

超临界CO2萃取烟草中烟碱

为研究超临界CO2萃取烟草中烟碱的工艺条件,利用实验室超临界萃取装置对烟草中烟碱进行了提取,考察了萃取压力、萃取温度、夹带剂乙醇的浓度、萃取时间等因素对烟碱提取率的影响,并就各个工艺参数对萃取率的影响机理和原因进行了分析与讨论。结果表明:在本研究范围内,最佳萃取工艺条件为:萃取压力30 MPa,萃取温度50℃,夹带剂乙醇浓度75%～80%,夹带剂流量为0.5 mL.min-1时,萃取时间为2～2.5 h。     

高半纤维素浆粕制备Lyocell纤维的研究

采用半纤维素质量分数21%的高半纤维素浆粕在N-甲基吗琳-N-氧化物(NMMO)水溶液中制备Lyocell纤维,并与半纤维素质量分数为10%的高α-纤维素浆粕的可纺性进行了对比。结果表明:高半纤维素浆粕在溶剂NMMO·H_2O中更易溶解,其过滤性能和可纺性能好,可在较高浆粕浓度下纺丝,制备成Lyo- cell纤维的产率高,且能提高Lyocell纤维的力学性能。高半纤维素浆液的稳定性能略低,在溶剂回收中需要消耗较多的双氧水进行氧化回收溶剂NMMO。     

控制气相PE流化床高度对装置运行周期的影响

分析了聚合过程中控制流化床床高对聚合物粒径,催化剂聚合产率和装置运行周期的影响.增加流化床床高,有利于聚合物粉料对反应器上部扩大段的冲刷,有效减少了粉料堵塞循环回路和反应器结块的发生几率,提高了聚合反应器运行周期.     

bPE-g-MAH对PC/bPE共混物力学性能与断面形态结构的影响

利用熔融接枝法制备了双峰聚乙烯接枝马来酸酐(bPE-g-MAH),将其用作聚碳酸酯/双峰聚乙烯(PC/bPE)共混物的增容剂。通过力学性能测试和扫描电镜分析,研究了bPE-g-MAH对共混物相容性和力学性能的影响。结果表明:bPE-g-MAH的加入使得PC和bPE两相的界面黏合作用增强,使PC/bPE共混物的冲击强度显著提高。     

热处理工艺对中碳合金钢冲击磨料磨损耐磨性的影响

研究淬火加热温度和回火温度对中碳合金钢６０ＳｉＭｎＣｒＭｏＶＲＥ冲击磨料磨损耐磨性的影响。试验结果表明,耐磨性随淬火加热温度升高而提高,９５０℃淬火后可获得最高的耐磨性,超过９５０℃淬火,耐磨性随淬火温度升高而降低。淬火回火后的耐磨性在３５０℃以下随回火温度升高略有降低,３５０℃以上回火耐磨性迅速提高,４００℃回火后耐磨性达到最大值,以后,随回火温度升高,耐磨性连续降低     

SiC颗粒增强铝基复合材料薄板的力学性能

研究了粉末冶金法制备的ＳｉＣ颗粒增强铝基复合材料薄板的常温及高温力学性能,结果表明,铝基复合材料薄板在常温下具有较高的强度,薄板性能基本呈各向同性,其断裂机制主要为颗粒从基体脱粘,同时有少量颗粒破碎。随着温度的升高,复合材料板材强度逐渐下降,延伸率增大。在２００℃时仍能保持较高的强度和较好的综合性能,其抗拉强度达３７０ＭＰａ,屈服强度达２４３ＭＰａ,延伸率达１１．３％。     

铝合金半固态加工技术应用

对于垂直式电磁搅拌器 ,提高搅拌效率的最有效措施是减少漏磁通。对于通常的Al Si类合金的半固态加工坯料 ,在足够的搅拌强度下 ,熔体冷却速度控制在 0 .5～ 3.0℃ /s可得到较好的组织。在二次加热时共晶体中的针簇状Si相通过扩散溶解到α相中 ,Si相本身变成细小颗粒 ,初生α相在共晶熔化后才开始球化。对于AlSi9Cu3合金 ,其共晶相在二次加热熔化后重新凝固时 ,Si相呈细小颗粒析出 ;对于A357合金 ,仍然生成针簇状组织。与常规压铸相比 ,半固态压铸内浇道厚度要增加 2～ 3mm ,压射比压要高 5～ 2 0MPa,才能保证充型完好。     

壳体凸台挤压模

详细说明壳体凸台挤压模的模具结构及工作过程 ,并介绍了凸台成形中产生的缺陷和防范措施