PTC型BaTiO3陶瓷的孪晶和孪晶界

用透射电镜和高分辨电镜观察研究了PTC型BaTiO_3陶瓷的孪晶和孪晶界结构,并提出了可能的{111}孪晶及孪晶界的原子结构模型。结果表明,{111}孪晶形成氧八面体共面的共格倾斜孪晶界,在孪晶界处可能存在一定量的A空位且原子密度要低于孪晶体内。同时还发现两种其它特征的孪晶现象。     

CaO-SiO2系玻璃的析晶动力学研究

利用溶胶-凝胶法制得CaO-SiO2系基础玻璃,通过差热分析曲线分析质量比为CaO-SiO2玻璃的析晶能力。经分析,其析晶活化能E=457.1kJ·mol-1,而晶化生长指数是随升温速率的不同而不同,速率越大,晶化生长指数越小。     

Nanocrystalline CeO2 in SBA-15: Performance of Pt/CeO2/SBA-15 Catalyst for Water-gas-shift Reaction

CeO₂ particles confined within the pores of an SBA-15 mesoporous silica host were prepared by incipient wetness impregnation (IMP) and deposition precipitation (DP) methods. The materials were characterized by XRD, N₂-adsorption and temperature programmed reduction (TPR) to evaluate the structure, texture, and redox properties. The preparation procedure had significant impact on the assembling mode of CeO₂ inside the SBA-15 mesopores. A high dispersion of CeO₂ particles was achieved via DP, whereas the dispersion of CeO₂ prepared by IMP was found to be inhomogeneous and CeO₂ partially blocked the pores. The CO conversion in the water-gas-shift reaction was enhanced over 1 wt% Pt supported on CeO₂-modified SBA-15 obtained by DP.     

塑料啤酒瓶开发现状

介绍了塑料啤酒瓶的优点,详细介绍了各种以PET为基础的改性啤酒瓶材料,并列举了大量的开发实例。     

Thermal analysis of styrene–alkyl methacrylate polymers. I. Glass transition temperatures

The glass transition temperatures (T_g's) of several polystyrenes and styrene–alkyl methacrylate copolymers and terpolymers were measured using thermomechanical analysis (TMA) and differential scanning calorimetry (DSC). The polymers studied had number-average molecular weights from 3000 to 250,000 g/mole. The results indicate that the composition dependence of the T_g's for the copolymers and terpolymers can be satisfactorily described by a general Fox equation. In general, the measured T_g's of the copolymer and terpolymer samples depend more on the steric effects of the constituent pendent groups than on their molecular weights. The chain flexibility rather than the size of the pendent group is the determining factor in the glass transition properties of the styrene polymers.     

物联网环境下企业内部控制环境研究

物联网作为未来的发展趋势之一,将在各个方面决定未来世界和人类社会的发展方向。而自智慧地球、感知中国等战略提出以来,世界各国也纷纷开展物联网领域的规划布局,将物联网建设上升到国家战略。物联网在全世界范围内掀起了继计算机和互联网之后的第三次信息革命浪潮。在这空前火爆的物联网宏观背景下,微观企业也不可避免的受到物联网影响。在这一背景下,通过分析物联网环境对企业内部控制环境的影响。本文认为,物联网环境下企业内部控制环境将更加信息化、虚拟化、智能化。     

ZrO2对CaO-SiO2系玻璃析晶的影响

通过DSC曲线研究了不同含量的ZrO2对CaO-SiO2系玻璃析晶的影响,根据JMA方程计算动力学参数(如析晶活化能E、频率因子ν、晶化指数n)。从计算结果可以看出,随着ZrO2含量的增加,析晶活化能E减少,而频率因子ν和晶化指数n增加。当ZrO2含量为7%时,E值最小:235.58kJ/mol;n值最大:4.70。说明ZrO2在CaO-SiO2玻璃体系是有效的晶核剂。     

Preparation and characterization of polyelectrolyte copolymers containing methyl methacrylate and 2-hydroxyethyl methacrylate. I. Polymers based on methacrylic acid

Acidic polyelectrolyte copolymers containing 2-hydroxyethyl methacrylate (HEMA), methyl methacrylate (MMA), and methacrylic acid (MAA) were prepared by free radical polymerization to high conversion in solution. Copolymer yields were obtained by gravimetry (all in the 30–50% range), relative molecular weights estimated by intrinsic viscosity measurements (all in the 50–70 cc/g range), tacticity by ¹³C nuclear magnetic resonance (NMR) spectroscopy (all polymers predominantly syndiotactic with some atactic content), and composition by acid/base titrations in conjunction with ¹H-NMR spectroscopy (all close to the monomer charge ratios). Acid strengths or apparent pKa's were examined as a function of extent of ionization. Measurements performed in water indicated that the compact/extended coil transformation in predominantly syndiotactic polymethacrylic acid occurs also in copolymers of similar tacticity containing moderate to high concentrations of MAA. The apparent pKa of such polymers containing only small amounts of MAA did not vary with extent of ionization, indicating a low degree of interaction between the acid groups. In copolymer pairs containing similar amounts of MAA but differing HEMA and MMA contents, the polymer containing more HEMA appeared the stronger acid, presumably due to a better solvation of that polymer which would increase the net spatial charge–charge separation and decrease cooperative effects that lead to suppressed ionization.     

Factors influencing magnetic polymer microspheres prepared by dispersion polymerization

Magnetic iron oxide (Fe₃O₄) was prepared by a coprecipitation method. Core–shell composite magnetic polymer microspheres with carboxyl groups were synthesized by the dispersion polymerization of styrene and acrylic acid in the presence of magnetic oxide, and dibenzoyl peroxide was used as an initiator. The synthesized magnetic polymer microspheres were characterized with X‐ray diffraction, transmission electron microscopy, scanning electron microscopy, Fourier transform infrared spectroscopy, and so forth. The results indicated that the product was single‐phase Fe₃O₄, and its average size was about 10 nm. The configuration of the microspheres, which contained carboxyl groups, was spherical, and the average size was about 2 μm. The results of vibrating sample magnetometry tests showed that the magnetic powders produced by different surfactants had different saturation magnetizations. When poly(ethylene glycol) with a weight‐average molecular weight of 4000 was used as a surfactant, the saturation magnetization of the samples reached 69.2 emu/g. The factors that affected the shape, magnetism, size, and distribution of the microspheres were also studied. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007     

An SVD-based adaptive robust speech steganography using MDCT coefficient

Multimedia Tools and Applications - Speech is one of the essential ways of communication. The study of speech steganography provides great value in information security. To improve imperceptibility...